Two-component polymer ceramic tile adhesive and preparation method thereof

A ceramic tile adhesive and polymer technology, which is applied in the field of building materials, can solve the problems of tile shedding and weak tensile adhesiveness of the adhesive, and achieve increased bonding strength, improved interface density, and mechanical occlusal big effect

Inactive Publication Date: 2020-01-17
广东楼管家新材料科技有限公司
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies in the prior art, the object of the present invention is to provide a two-component polymer tile adhesive and its preparation method to solve the problems caused by thermal expansion and cooling of the existing adhesive after bonding tiles. If the shrinkage is too large, the stretching adhesion of the adhesive itself is not strong, which will easily lead to the problem that the tiles will fall off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The two-component polymer tile adhesive provided in this embodiment is made of two groups of mixture components, and the group A mixture is made of the following components in parts by weight: 300 parts of cement, 45 parts of crushed stone , 15 parts of redispersible latex powder, 7 parts of hydroxypropyl methylcellulose, 6 parts of calcium formate, 15 parts of epoxy resin, 45 parts of water, 50 parts of emulsion and 15 parts of cellulose.

[0033] The Group B mixture is made up of the following components in parts by weight:

[0034] 300 parts of cement, 45 parts of crushed stone, 15 parts of dispersible latex powder, 4 parts of acrylate copolymer, 20 parts of styrene rubber powder, 15 parts of epoxy resin, 45 parts of water, 50 parts of emulsion, and 15 parts of cellulose.

[0035] Wherein, the number of the crushed stone is 30-100 mesh.

[0036] The preparation method of the aforementioned two-component polymer tile adhesive, which comprises the following steps:

...

Embodiment 2

[0043] The two-component polymer tile adhesive and preparation method thereof provided in this embodiment are basically the same as those in Embodiment 1, except that:

[0044] The A-group mixture is made up of the following components in parts by weight:

[0045] 250 parts of cement, 35 parts of crushed stone, 5 parts of dispersible latex powder, 3 parts of hydroxypropyl methylcellulose, 4 parts of calcium formate, 10 parts of epoxy resin, 40 parts of water, 40 parts of emulsion, 5 parts of cellulose;

[0046] The Group B mixture is made up of the following components in parts by weight:

[0047] 250 parts of cement, 35 parts of crushed stone, 5 parts of dispersible latex powder, 1 part of acrylate copolymer, 15 parts of styrene rubber powder, 10 parts of epoxy resin; 40 parts of water, 40 parts of emulsion, and 5 parts of cellulose.

Embodiment 3

[0049] The two-component polymer tile adhesive and its preparation method provided in this embodiment are basically the same as those in Embodiments 1 and 2, except that:

[0050] The A-group mixture is made up of the following components in parts by weight:

[0051] 450 parts of cement, 55 parts of crushed stone, 30 parts of dispersible latex powder, 10 parts of hydroxypropyl methylcellulose, 10 parts of calcium formate, 20 parts of epoxy resin, 50 parts of water, 60 parts of emulsion, and 20 parts of cellulose;

[0052] The Group B mixture is made up of the following components in parts by weight:

[0053] 450 parts of cement, 55 parts of crushed stone, 30 parts of redispersible latex powder, 6 parts of acrylate copolymer, 30 parts of styrene rubber powder, 20 parts of epoxy resin; 50 parts of water, 60 parts of emulsion, and 20 parts of cellulose.

[0054] To sum up, by setting parts of epoxy resin, the thermal expansion and cold contraction of the adhesive is relatively w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a two-component polymer ceramic tile adhesive which is prepared from two groups of mixtures, wherein an A group of mixture comprises hydroxypropyl methylcellulose, calcium formate and epoxy resin; a B group of mixture comprises an acrylate copolymer, benzene rubber powder and epoxy resin; the A group of mixture is prepared from the following components in parts by weight: 250 to 450 parts of cement, 35 to 55 parts of gravel, 5 to 30 parts of redispersible latex powder, 3 to 10 parts of hydroxypropyl methylcellulose, 4 to 10 parts of calcium formate, 10 to 20 parts of epoxy resin, 40 to 50 parts of water, 40 to 60 parts of an emulsion and 5 to 20 parts of cellulose. The invention also discloses a preparation method of the two-component polymer ceramic tile adhesive.According to the preparation method, epoxy resin is adopted to weaken the thermal expansion and cold contraction of the adhesive, so that the tensile cohesiveness of the adhesive is increased, and ceramic tiles are prevented from falling off; gravel is adopted, so that the mechanical occlusion effect between gravels is greater, the bonding strength is increased; and meanwhile, silica fume is doped, the interface compactness is improved, and the interface bonding strength is remarkably improved.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a two-component polymer tile adhesive and a preparation method thereof. Background technique [0002] Tile adhesive, also known as tile adhesive or tile adhesive, is mainly used to paste decorative materials such as tiles, face tiles, floor tiles, etc. Tile adhesive is a substance that plays a bonding role between tiles and walls, floors, etc. It is required to have certain bonding strength, shear strength, efflorescence resistance, aging resistance and other properties. [0003] However, after the existing adhesives are bonded to the tiles, the adhesive itself has poor tensile adhesion due to excessive thermal expansion and cold contraction, which easily causes the tiles to fall off. SUMMARY OF THE INVENTION [0004] In view of the deficiencies in the prior art, the purpose of the present invention is to provide a two-component polymer tile adhesive and a preparati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B24/28
CPCC04B28/00C04B2111/00637C04B14/02C04B2103/0057C04B24/383C04B24/04C04B24/281C04B24/2641C04B24/2676
Inventor 沈腾飞周福星胡新
Owner 广东楼管家新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap