Modified attapulgite powder for coagulation algae removal
A soil powder and modification technology, which is applied in the fields of flocculation/sedimentation water/sewage treatment, water/sewage treatment, sterilization/microdynamic water/sewage treatment, etc. Water pollution and other problems, to shorten the coagulation and sedimentation time, increase the specific surface area, and enhance the adsorption performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] A modified attapulgite powder for coagulation and algae removal comprises the following raw materials in parts by weight: 100 parts by weight of attapulgite, 1 part by weight of tea saponin, and the attapulgite is 200-300 mesh.
[0024] Its preparation method is:
[0025] S1. Calcining 500 g of attapulgite at a temperature of 200° C. for 2 hours and cooling to room temperature;
[0026] S2. Add 5kg of acetone into the autoclave, disperse the attapulgite into the acetone, set the pressure of the autoclave to 3.5MPa, the reaction temperature to 160°C, react for 6h, and cool to 75°C;
[0027] S3. Put 5 g of commercially available tea saponin powder into the above reaction solution, disperse and cool to obtain a precipitated mixture of tea saponin and attapulgite, and dry it to make modified attapulgite powder.
Embodiment 2
[0029] A modified attapulgite powder for coagulation and algae removal comprises the following raw materials in parts by weight: 100 parts by weight of attapulgite, 2 parts by weight of tea saponin, and the attapulgite is 200-300 mesh.
[0030] Its preparation method is:
[0031] S1. Calcining 500 g of attapulgite at a temperature of 200° C. for 2 hours and cooling to room temperature;
[0032] S2. Add 5kg of acetone into the autoclave, disperse the attapulgite into the acetone, set the pressure of the autoclave to 4MPa, the reaction temperature to 120°C, react for 6h, and cool to 75°C;
[0033] S3. Put 10 g of commercially available tea saponin powder into the above reaction solution, disperse and cool to obtain a precipitated mixture of tea saponin and attapulgite, and dry it to make modified attapulgite powder.
Embodiment 3
[0035] A modified attapulgite powder for coagulation and algae removal comprises the following raw materials in parts by weight: 100 parts by weight of attapulgite, 3 parts by weight of tea saponin, and the attapulgite is 200-300 mesh.
[0036] Its preparation method is:
[0037] S1. Calcining 500 g of attapulgite at a temperature of 200° C. for 2 hours and cooling to room temperature;
[0038] S2. Add 5kg of acetone into the autoclave, disperse the above-mentioned attapulgite into the acetone, set the pressure of the autoclave to 4MPa, the reaction temperature to 160°C, react for 6h, and cool to 75°C;
[0039] S3. Put 15 g of commercially available tea saponin powder into the above reaction solution, disperse and cool to obtain a precipitated mixture of tea saponin and attapulgite, and dry it to prepare a modified attapulgite powder.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com