Polypropylene glass fiber composite material

A glass fiber and composite material technology, applied in the field of polypropylene glass fiber composite materials, can solve the problems of easy warping, weak interaction force, falling off, etc., to improve bending resistance and impact resistance, improve mechanical properties and Heat resistance, effect of improving interfacial interaction

Inactive Publication Date: 2020-03-24
CHANGSHU DONGYU INSULATED COMPOUND MATERIALS
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the weak interaction between the glass fiber and the polymer matrix, it is easy to fall off from the polymer matrix to form a cavity, which not only significantly lowers the fiber reinforcement effect and mechanical properties of the material, but also affects the overall quality of the injection molded part. The support effect is also very limited, and its products are easy to warp and deform

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of polypropylene glass fiber composite material, described polypropylene glass fiber composite material is compounded by polypropylene masterbatch, glass fiber, polypropylene fiber, coupling agent and maleic anhydride grafted polypropylene, and its mass percent is respectively : 40% polypropylene masterbatch, 36% glass fiber, 12% polypropylene fiber, 2% coupling agent and 10% maleic anhydride grafted polypropylene, wherein the polypropylene masterbatch includes T30S and EPS30R, and the T30S The mass ratio of EPS30R to the polypropylene masterbatch is 1:1, and the polypropylene glass fiber composite material is formed by twin-screw co-extrusion.

[0017] The glass fiber is chopped glass fiber, and the fiber length of the chopped glass fiber is 2.5-3 mm, preferably 3 mm.

[0018] The coupling agent is a silane coupling agent, preferably a vinyltriethoxysilane coupling agent.

[0019] The graft ratio of the maleic anhydride grafted polypropylene is 1.5%-1.6%, prefe...

Embodiment 2

[0021] A kind of polypropylene glass fiber composite material, described polypropylene glass fiber composite material is compounded by polypropylene masterbatch, glass fiber, polypropylene fiber, coupling agent and maleic anhydride grafted polypropylene, and its mass percent is respectively : 42% polypropylene masterbatch, 38% glass fiber, 10% polypropylene fiber, 4% coupling agent and 6% maleic anhydride grafted polypropylene, wherein the polypropylene masterbatch includes T30S and EPS30R, and the T30S The mass ratio of EPS30R to the polypropylene masterbatch is 1:1, and the polypropylene glass fiber composite material is formed by twin-screw co-extrusion.

[0022] The glass fiber is chopped glass fiber, and the fiber length of the chopped glass fiber is 2.5-3 mm, preferably 3 mm.

[0023] The coupling agent is a silane coupling agent, preferably a vinyltriethoxysilane coupling agent.

[0024] The graft ratio of the maleic anhydride grafted polypropylene is 1.5%-1.6%, prefer...

Embodiment 3

[0026] A kind of polypropylene glass fiber composite material, described polypropylene glass fiber composite material is compounded by polypropylene masterbatch, glass fiber, polypropylene fiber, coupling agent and maleic anhydride grafted polypropylene, and its mass percent is respectively : 41% polypropylene masterbatch, 37% glass fiber, 11% polypropylene fiber, 3% coupling agent and 8% maleic anhydride grafted polypropylene, wherein the polypropylene masterbatch includes T30S and EPS30R, and the T30S The mass ratio of EPS30R to the polypropylene masterbatch is 1:1, and the polypropylene glass fiber composite material is formed by twin-screw co-extrusion.

[0027] The glass fiber is chopped glass fiber, and the fiber length of the chopped glass fiber is 2.5-3 mm, preferably 3 mm.

[0028] The coupling agent is a silane coupling agent, preferably a vinyltriethoxysilane coupling agent.

[0029] The graft ratio of the maleic anhydride grafted polypropylene is 1.5%-1.6%, prefer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polypropylene glass fiber composite material. The polypropylene glass fiber composite material is formed by compounding the following components by mass percentage: 40%-42% of polypropylene master batch, 36%-38% of glass fiber, 10%-12% of polypropylene fiber, 2%-4% of a coupling agent and 6%-10% of maleic anhydride grafted polypropylene, wherein the polypropylene master batch comprises T30S and EPS30R, the mass ratio of the T30S to the EPS30R in the polypropylene master batch is 1:1, and the polypropylene glass fiber composite material is formed by co-extrusion of double screws. By the above way, the mechanical properties and heat resistance of the polypropylene glass fiber composite material can be improved, the modulus of the polypropylene glass fiber compositematerial is not lower than that of a wood template, the product does not deform or bend easily, and the production cost can be lowered.

Description

technical field [0001] The invention relates to the field of glass fiber composite materials, in particular to a polypropylene glass fiber composite material. Background technique [0002] However, with the development of science and technology society, polypropylene is widely used in all aspects of daily life. At present, due to the low strength and modulus of polypropylene, it can no longer meet the application in some engineering fields. Improving the tensile strength and modulus of polypropylene is an effective way to broaden the application of polypropylene, and it is also an important field of high-performance polypropylene. [0003] Glass fiber is a one-dimensional inorganic filler with high strength and modulus. When it is added to the polymer matrix, it can effectively bear stress and load as a skeleton, which can significantly improve the mechanical properties of the polymer matrix and Heat resistance. [0004] At present, there have been a large number of resear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L51/06C08K7/14C08J5/08
CPCC08J5/08C08J2323/12C08J2423/12C08J2451/06C08K7/14C08K2201/004
Inventor 吴祖明杨波陈超许春艳王健
Owner CHANGSHU DONGYU INSULATED COMPOUND MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products