A vibration-isolation rubber bearing

A vibration isolation rubber and bearing technology, which can be used in earthquake protection, bridges, bridge parts, etc., can solve problems such as mechanical properties decline, permanent deformation reduction, molecular chain breakage, etc.

Active Publication Date: 2021-08-10
LUOYANG SUNRUI SPECIAL EQUIP
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The higher the damping of the rubber material, the greater the energy consumption and the greater the heat generation, which will cause the molecular chain to break and accelerate the aging of the rubber, and the durability is poor; reducing the damping and improving the elasticity of the rubber material can improve the reset performance of the bearing and reduce permanent deformation, but Will not be able to guarantee energy consumption and shock isolation effect
[0005] (2) Insufficient temperature adaptability of a single rubber material
However, as a result of such modification, the overall properties of the rubber material, especially the mechanical properties, will often be reduced.
This is because when two or more types of rubber are blended and modified, the vulcanization time, vulcanization speed and vulcanization degree cannot be well matched when different materials are co-vulcanized, so there are few practical applications.
[0006] (3) The same kind of rubber has insufficient adaptability when meeting the vertical load-bearing and horizontal shear properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A vibration-isolation rubber bearing
  • A vibration-isolation rubber bearing
  • A vibration-isolation rubber bearing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A shock-isolation rubber bearing of the present invention, such as figure 1 As shown, it is mainly composed of upper and lower support steel plate 1, upper and lower sealing steel plate 2, stiffening steel plate 3, protective adhesive layer 4, first adhesive layer 1R, second adhesive layer 2R, third adhesive Layer 3R composition. The three rubber layers are all nitrile rubber, but the formula is different. The first rubber layer 1R is nitrile rubber with low acrylonitrile content, which has good low temperature performance, flexibility and elasticity; the second rubber layer 2R is high acrylonitrile content Nitrile rubber has good damping performance and high strength; the third rubber layer 3R is nitrile rubber with medium acrylonitrile content, which has good damping performance and moderate performance. The first type of adhesive layer 1R, the second type of adhesive layer 2R and the third type of adhesive layer 3R are vertically arranged sequentially, and the thick...

Embodiment 2

[0035] A shock-isolation rubber bearing of the present invention, such as figure 2As shown, it is mainly composed of upper and lower support steel plate 1, upper and lower sealing steel plate 2, stiffening steel plate 3, protective adhesive layer 4, first adhesive layer 1R, second adhesive layer 2R, third adhesive Layer 3R composition. The first rubber layer 1R is nitrile rubber with medium acrylonitrile content, which has good damping performance; the second rubber layer 2R is nitrile rubber with low acrylonitrile content, which has good low temperature performance, flexibility and elasticity; the third rubber layer Layer 3R is natural rubber with good elasticity and strength. The first type of adhesive layer 1R, the second type of adhesive layer 2R and the third type of adhesive layer 3R are symmetrically arranged, and the thickness of the first type of adhesive layer 3R accounts for 40% of the total thickness of the support adhesive layer. The three adhesive layers have ...

Embodiment 3

[0037] A shock-isolation rubber bearing of the present invention, such as image 3 As shown, it is mainly composed of upper and lower support connecting steel plates 1, upper and lower sealing steel plates 2, stiffening steel plates 3, protective adhesive layer 4, shear key 5, lead core 6, first adhesive layer 1R, second The seed layer is composed of 2R. The two types of glue are the same, but the formula is different. The first type of adhesive layer 1R is natural rubber, reinforced with low-structure carbon black, with high elasticity and good recovery; the second type of adhesive layer 2R is natural rubber, reinforced with high-structure carbon black, with high strength and certain Energy consumption capacity. The first type of adhesive layer 1R and the second type of adhesive layer 2R form a group, the second type of adhesive layer 2R in each group is on the top, the first type of adhesive layer 1R is on the bottom, and multiple groups of adhesive layers are arranged alt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A shock-isolation rubber bearing, which is composed of a rubber rubber layer, a stiffened steel plate, a protective rubber layer, a sealing layer steel plate and a support connecting steel plate, and the cylindrical space surrounded by the protective rubber layer is provided with alternating rubber rubber layers and stiffened steel plates. Filled laminated rubber body, the upper and lower ends of the laminated rubber body are respectively provided with sealing steel plates that seal the two ends of the protective rubber layer, and the multi-layer rubber rubber layer is combined by a specific arrangement. The specific arrangement The method is one of sequential arrangement, alternate arrangement or symmetrical arrangement; through the use of different rubber materials, each adhesive layer can achieve vibration reduction characteristics, high damping characteristics, shear characteristics, high load-bearing characteristics, etc. function, and the use of each adhesive layer can realize the performance coordination of the overall support, which can not only have both elasticity and damping performance, but also ensure the coordination of vertical load-bearing performance and horizontal shear performance. At the same time, it has multiple damping peaks to ensure the support The seat has good environmental adaptability and durability.

Description

technical field [0001] The invention relates to a rubber bearing, in particular to a shock-isolation rubber bearing. Background technique [0002] Isolation rubber bearings are rubber bearings used for seismic isolation of houses, bridges or other structures in earthquake areas, including natural rubber bearings (LNR), lead rubber bearings (LRB) and high damping rubber bearings (HDR) , the main structure is integrally vulcanized by laminated rubber and stiffened steel plates. The upper and lower structures are connected by sealing steel plates and connecting steel plates, which can effectively reduce the effect of structural seismic force. It has been applied in many engineering projects in recent years. [0003] The vibration-isolation rubber bearing needs to have good vertical bearing capacity, horizontal shear performance, self-resetting performance and damping energy dissipation characteristics, as well as good environmental adaptability and durability. In order to achi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E01D19/04E04B1/36E04B1/98E04H9/02
CPCE01D19/041E04B1/36E04B1/98E04H9/022
Inventor 姜文英仝延锋胡海青张永兆冯莺史保进刘绍辉栾绪波
Owner LUOYANG SUNRUI SPECIAL EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products