A kind of al-cu system casting alloy suitable for forging processing and preparation method thereof

An alloy, al-si technology, applied in the field of casting aluminum alloys, can solve problems such as deterioration of mechanical properties

Active Publication Date: 2021-09-14
LANZHOU FLIGHT CONTROL
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the thermal processing of aluminum alloys, the casting structure is transformed into a processed structure, accompanied by dynamic recovery and dynamic recrystallization phenomena. Dynamic recovery includes dislocation formation, migration and annihilation phenomena, which occur in all metal thermal processing processes, as High-level dislocation energy metals, dislocations in aluminum alloys are easy to move, so the traditional discontinuous dynamic recrystallization phenomenon of nucleation and grain growth is difficult to occur. Generally, the dynamic recrystallization mechanism in the thermal processing of aluminum alloys is continuous. Dynamic recrystallization, the formation of small-angle grain boundaries in the cast original grains, and then the transformation from small-angle grain boundaries to high-angle grain boundaries, resulting in deterioration of mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of al-cu system casting alloy suitable for forging processing and preparation method thereof
  • A kind of al-cu system casting alloy suitable for forging processing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The following introduces some schemes among the multiple possible implementation cases of the present invention, aiming to provide a basic understanding of the present invention, but not intended to identify the key or decisive elements of the present invention or to limit the scope of protection. Therefore, the following specific embodiments are only exemplary descriptions of the technical case of the present invention, and should not be regarded as the entirety of the present invention or as a limitation or restriction on the technical solution of the present invention.

[0024] The percentages by weight of the components in the Al-Cu cast aluminum alloy with excellent forging properties in this example are: Cu: 4.8%, Mn: 0.7%, Si: 0.5%, Mg: 0.5%, Ti: 0.35%, and the remaining impurities <0.3%, the balance is Al.

[0025] The preparation process is as follows: the raw materials are dissolved and refined to obtain an alloy solution; the aluminum alloy solution is poured...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The present invention proposes an Al-Cu series casting alloy suitable for forging processing and a preparation method thereof. Aiming at the problem that the Al-Cu series casting alloy with high copper content is difficult to forge, the pouring process is shortened by adding various strengthening elements and inhibiting elements Medium solidification temperature range and increase the grain boundary dragging effect, reduce the generation of dendrites, etc., to achieve the effect of enhancing the forging performance of the material. The percentages of each component and weight in Al-Cu series casting alloy are: Cu: 4%~6%, Mn: 0.5%~1.0%, Si: 0.4%~0.8%, Mg: 0.3%~0.6%, Ti: 0.15% to 0.4%, the remaining impurities <0.5%, and the balance is aluminum. By increasing the content ratio of Mn element and Si element in Al-Cu-based casting alloys, the Si phase is refined and dispersed and the second phase particles (Al 2 Cu, ALCuFeMn compound equal) a large number of dispersed precipitation, the pinning effect is strengthened, which significantly improves the forging performance of Al-Cu series casting alloys. The mechanical properties after forging are tensile strength ≥ 500MPa, yield strength ≥ 350MPa, and elongation ≥ 15%.

Description

technical field [0001] The invention relates to a casting aluminum alloy, in particular to an Al-Cu series casting alloy suitable for forging processing and a preparation method thereof, which has excellent forging properties. Background technique [0002] Al-Cu cast aluminum alloy is a typical high-strength and high-toughness alloy with excellent comprehensive mechanical properties. It has high strength, good ductility and plasticity, and excellent high-temperature performance and machinability. It is currently mainly used as a military and Civilian structural materials have great application prospects in aviation, aerospace, and automotive wheel industries. [0003] However, since the Al-Cu cast aluminum alloy has a wide crystallization temperature range, and there is Al with poor plasticity in the eutectic structure during solidification 2 Cu phase, easy to crack. At the same time, due to the different solidification speeds of structural parts during the production proc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/16C22C1/03C22F1/057
CPCC22C1/026C22C1/03C22C21/14C22C21/16C22F1/002C22F1/057
Inventor 王军阳冯延泽杨世林
Owner LANZHOU FLIGHT CONTROL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products