Polymer ceramic material for pouring mold and manufacturing method thereof

A technology of polymer ceramics and pouring molds, which is applied in the direction of coating, etc., can solve the problems of increasing the cost of materials for manufacturers, complicated processes, and high processing costs, and achieve the advantages of reducing material prices and overall weight, high surface finish, and conducive to precise casting. Effect

Pending Publication Date: 2020-04-28
自贡诚鑫阀门有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Insufficient: easy to deform, the mold may be deformed after each casting, and long-term use will increase the material cost of the manufacturer
Disadvantages: The processing cost is 8-10 times higher than that of wooden molds, and the weight of the model is heavy, which is not conducive to on-site construction, and it is difficult to repair after deformation
Disadvantages: The processing cost is 5-8 times higher than that of wood moulds. Because it is necessary to manufacture the wax film of the metal mold base first, the wax film is covered with sand to form the mold base. The process is relatively complicated, and only small finished products can be manufactured. For large castings Not applicable
Disadvantages: Because the foam model needs to be manufactured first, and the foam model is then covered with sand to form the mold base, the process is relatively complicated, the pressure capacity is low, and the pressure parts cannot be manufactured, the thermal stability is poor, and it is not easy to use. The deformation will increase in the environment where the temperature exceeds 60 degrees.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1, the present invention is a polymer ceramic material for pouring molds, comprising the following components by weight percentage: plastic material 60-70%, ceramic powder 10-15%, glass fiber 5-10%, metal fiber 1 -3%, plasticizer 1-2%.

[0026] The plastic material is polymer PP powder, ABS powder or PVC powder.

[0027] The metal fiber is 304 or 316 metal material with a diameter of 0.03mm.

[0028] Plasticizers are usually benzoates or epoxies.

[0029] Plastic material powders such as polymer PP powder, ABS powder or PVC powder are used; ceramic powder and glass powder are used to improve wear resistance and increase strength supplement; glass fiber and metal fiber are used as curing to increase its support strength and reduce deformation Performance; plasticizers are used to increase stability.

Embodiment 2

[0030] Embodiment 2 includes the following components by weight percentage: 65% of plastic material, 13% of ceramic powder, 8% of glass fiber, 2% of metal fiber, and 1% of plasticizer. The combination of the intermediate values ​​of each component can effectively improve the product strength, increase the melting temperature, and increase the tensile, bending, compressive and impact-resistant capabilities.

Embodiment 3

[0031] Embodiment 3 includes the following components by weight percentage: PP powder 70%, ceramic powder 15%, glass fiber 10%, metal fiber 3%, plasticizer 2%. Polypropylene (PP powder) is a semi-crystalline thermoplastic with high impact resistance. After selecting the PP plastic material and various material components, the overall strength of the material can reach 70-80HSD, and the density can reach 1.6(g / mlat25℃), the melting point can be increased to 200℃, the abrasion resistance can be increased by 40%, and the deformation resistance can be increased by 35%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Densityaaaaaaaaaa
Melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polymer ceramic material for a pouring mold and a manufacturing method thereof. The polymer ceramic material comprises the following components in percentage by weight: 60-70% of a plastic material, 10-15% of ceramic powder, 5-10% of glass fiber, 1-3% of metal fiber and 1-2% of a plasticizer. A mold prepared from the polymer ceramic material is low in price, convenient toprocess, beneficial to molding, high in surface smoothness, long in service life, not prone to deformation, beneficial to accurate casting and capable of manufacturing large pressed parts. Compared with a metal material, the weight and the specific gravity are low, the material price and the overall weight are greatly reduced, water absorption is avoided, deformation of the mold is reduced, the surface is subjected to crystal plating treatment, the smoothness is greatly superior to that of the metal material, an oxidation reaction is avoided after the surface is made of a non-metal material,and the service life of the surface smoothness is prolonged.

Description

technical field [0001] The invention relates to the technical field of mold materials, in particular to a polymer ceramic material for casting molds and a manufacturing method thereof. Background technique [0002] Existing types of casting molds include: wooden molds, metal molds, paraffin molds and foam molds. The following is an analysis of the characteristics of several molds: [0003] Advantages of wooden molds: cheap, easy to process, good for modeling, and capable of manufacturing large pressure parts. Disadvantages: easy to deform, may cause mold deformation after each casting, and long-term use will increase the material cost of the manufacturer. The surface finish is low, the surface roughness of the casting product is relatively large, and the molding effect is poor. Strong water absorption will cause rot and mold scrapping. It cannot be achieved that precise casting has a short service life. Poor thermal stability, not easy to use in an environment where the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L55/02C08L27/06C08K13/04C08K3/00C08K7/14C08K7/06C08J7/04
CPCC08K13/04C08K3/00C08K7/14C08K7/06C08K2201/003C08J2323/12C08J2355/02C08J2327/06C08L23/12C08L55/02C08L27/06
Inventor 张柔依张剑赵友鹏费茜
Owner 自贡诚鑫阀门有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products