Bicycle saddle and forming process thereof

A molding process and bicycle technology, applied in bicycle saddles, bicycle accessories, transportation and packaging, etc., can solve the problems of insufficient rider comfort, uneven stress on the seat cushion, and reduced elasticity of the seat cushion, and achieve wear resistance and Good durability, increased softness, and improved tensile strength

Active Publication Date: 2020-04-28
WENLING DONGFANGHONG CYCLE PARTS
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] When the ETPU material is applied to the bicycle seat cushion, the elasticity of the seat cushion will decrease and the hardness will increase due to the long-term contact and friction between the buttocks and the seat cushion during riding. Insufficient comfort when riding

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bicycle saddle and forming process thereof
  • Bicycle saddle and forming process thereof
  • Bicycle saddle and forming process thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1-3

[0043] In the preparation example 1-3, the starch of canna taro was selected from the product number of 2019 sold by Guangxi Tianlin Rongan Agricultural Development Co., Ltd., and the gelatin was selected from the gelatin and polyvinyl alcohol of the product number of T6325 sold by Henan Guanqi Biotechnology Co., Ltd. The polyvinyl alcohol with the brand name PVA2699 sold by Shanghai Yingjia Industrial Development Co., Ltd. and the silicon dioxide are selected from the silicon dioxide and diatom mud with the product number T-1 sold by Tongqi Chemical (Shanghai) Co., Ltd., and the diatom mud is selected from Dongguan Diatom mud sold by Jinpai Industry and Trade Co., Ltd. is JP0010.

preparation example 1

[0044] Preparation example 1: Mix 0.8kg canna starch, 0.8kg gelatin and 0.3kg boric acid, add 1.2kg polyvinyl alcohol, and continuously feed formaldehyde gas, seal and stir for 2 hours, take it out, add 0.6kg silicon dioxide and 0.3kg Diatom mud is mixed and stirred evenly to prepare modified polyvinyl alcohol, the degree of polymerization of polyvinyl alcohol is 2550, and the degree of alcoholysis is 99%.

preparation example 2

[0045] Preparation example 2: Mix 1.3kg canna starch, 1.2kg gelatin and 0.5kg boric acid, add 2.3kg polyvinyl alcohol, and continuously feed formaldehyde gas, seal and stir for 3 hours, take it out, add 0.9kg silicon dioxide and 0.4kg silicon dioxide The algae mud is mixed evenly to prepare modified polyvinyl alcohol, the degree of polymerization of the polyvinyl alcohol is 2600, and the degree of alcoholysis is 99%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bicycle saddle and a forming process thereof. The forming process of the bicycle saddle comprises the following steps that S1, preparation of mold: an upper mold and a lowermold of the bicycle saddle are prepared; S2, plastifying and extruding: the raw materials of the bicycle saddle are injected into a mixing mill, mixed into a molten material, and extruding and granulating are carried out to obtain particles; S3, mold closing: the particles in the step S1 are fused and then injected into a cushion cavity formed by the upper mold and the lower mold, steam is injected into the cushion cavity after injection is completed, and the mold closing time is 6-10 min; and S4, cooling and demolding: after the bicycle saddle is cured, cooling and mold opening are conducted,and the bicycle saddle is taken out. The bicycle saddle has the advantages of being lasting in elasticity, good in abrasion resistance and durability, comfortable in hardness, environmentally friendly, antibacterial and capable of preventing stuffiness.

Description

technical field [0001] The invention relates to the technical field of bicycle accessories, more specifically, it relates to a bicycle seat cushion and its forming process. Background technique [0002] The seat cushion of a bicycle is the part that has the most contact with the human body during riding, and it is also the part that mainly bears the weight of the human body. The design of the bicycle seat cushion directly affects the comfort of people during riding. [0003] Most of the existing bicycle seat cushions are usually made of an inner layer made of elastic material and wrapped with an outer skin and sewed. The elastic material is foam plastic or sponge material, and the outer skin is leather or plastic material. The inner layer and the outer skin generally need to be repaired. Separate production, and finally manually assembled and stitched, the production process is more cumbersome, the production cost is higher, and because the outer skin is thin, the outer skin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L29/04C08L67/02C08L3/02C08L89/00C08L23/12C08K13/06C08K3/36C08K7/26C08K3/34C08K9/04C08K3/22C08K7/20C08K3/28C08K5/14C08K7/18C08J9/08B29C45/73B29C33/04B29B9/06B62J1/26
CPCB29B9/06B29C45/7337B62J1/26C08J9/0023C08J9/0061C08J9/0066C08J9/009C08J9/0095C08J9/08C08J9/103C08J9/30C08J2203/02C08J2203/04C08J2375/04C08J2403/02C08J2423/12C08J2429/04C08J2467/02C08J2489/00C08K3/28C08K3/34C08K3/36C08K5/14C08K7/18C08K7/20C08K7/26C08K9/04C08K13/06C08K2003/2241C08K2201/011
Inventor 朱巧敏
Owner WENLING DONGFANGHONG CYCLE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com