Ultraviolet light-cured water-based flexographic printing ink and preparation method thereof

A light-curing and ultraviolet technology, applied in ink, household utensils, applications, etc., can solve the problems of low drying rate, low adhesion fastness, low sensitivity, etc., and achieve the effect of high drying rate, low price, and sensitive photosensitivity

Inactive Publication Date: 2020-05-15
XIAN UNIV OF TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to provide a kind of ultraviolet photocurable water-based flexo printing ink, solve the water-based flexo printing ink existing in the prior art with low sensitivity, high viscosity, low mobility, low adhesion fastness, poor stability, and low drying rate , the problem of high cost
[0008] Another object of the present invention is to provide the preparation method of the above-mentioned ultraviolet photocurable water-based flexo printing ink, which solves the problem of low sensitivity, high viscosity, low mobility, low adhesion fastness and poor stability of water-based flexo printing inks in the prior art. , low drying rate and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A preparation method of ultraviolet photocurable water-based flexo printing ink, specifically implemented according to the following steps:

[0050] Step 1, take the following raw materials respectively by mass percentage:

[0051] PVA17-99 5%, ammonium dichromate 7%, pigment 15%, sodium nitrate 1%, industrial ethanol 4%, boric acid 1%, TS-103 defoamer 1%, urea 3%, the rest is deionized water, The sum of the mass percentages of the above components is 100%; wherein, the pigment is composed of benzidine yellow G and transparent yellow GG with a mass ratio of 3:2;

[0052] Step 2, prepare PVA17-99 mixed solution

[0053] Slowly add PVA17-99 to 1 / 4 volume of deionized water at 20°C, and at the same time use a mixer to stir evenly at 300r / h until PVA17-99 is fully swollen and dispersed, then raise the temperature to 90°C and stir evenly until PVA17-99 is completely Dissolve and keep warm for 2h to obtain PVA17-99 solution;

[0054] Add ammonium dichromate to 1 / 4 volume o...

Embodiment 2

[0059] A preparation method of ultraviolet photocurable water-based flexo printing ink, specifically implemented according to the following steps:

[0060] Step 1, take the following raw materials respectively by mass percentage:

[0061] PVA17-99 7%, ammonium dichromate 5%, sodium nitrate 1%, industrial ethanol 4%, permanent orange G15%, TS-103 defoamer 2%, urea 4%, boric acid 2%, the rest is deionized Water, the sum of the mass percentages of the above raw materials is 100%;

[0062] Step 2, prepare PVA17-99 mixed solution

[0063] Slowly add PVA17-99 to 1 / 4 volume of deionized water at 20°C, and at the same time use a mixer to stir evenly at 280r / h until PVA17-99 is fully swollen and dispersed, then raise the temperature to 95°C and stir evenly until PVA17-99 is completely Dissolve and keep warm for 2h to obtain PVA17-99 solution;

[0064] Add ammonium dichromate to 1 / 4 volume of deionized water, stir evenly to obtain ammonium dichromate solution, set aside;

[0065] Ad...

Embodiment 3

[0069] A preparation method of ultraviolet photocurable water-based flexo printing ink, specifically implemented according to the following steps:

[0070] Step 1, take the following raw materials respectively by mass percentage:

[0071] PVA17-99 7%, ammonium dichromate 5%, benzidine yellow GR15%, industrial ethanol 4%, TS-103 defoamer 2%, urea 4%, boric acid 2%, sodium nitrate 1%, the rest is deionized Water, the sum of the mass percentages of the above raw materials is 100%;

[0072] Step 2, prepare PVA17-99 mixed solution

[0073] Slowly add PVA17-99 to 1 / 4 volume of deionized water at 20°C, and at the same time use a mixer to stir evenly at 320r / h until PVA17-99 is fully swollen and dispersed, then raise the temperature to 95°C and stir evenly until PVA17-99 is completely Dissolve and keep warm for 2h to obtain PVA17-99 solution;

[0074] Add ammonium dichromate to 1 / 4 volume of deionized water, stir evenly to obtain ammonium dichromate solution, set aside;

[0075] A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses ultraviolet light-cured water-based flexographic printing ink. The printing ink is prepared from the following raw materials in percentage by mass: 5%-9% of a binder, 2%-7% ofa photosensitizer, 13%-17% of pigment, 3%-4% of industrial ethanol, 5%-8% of an additive, 0.5%-2% of sodium nitrate and the balance of deionized water, wherein the sum of the mass percentages of the raw materials is 100%. The invention further discloses a preparation method of the ultraviolet light-cured water-based flexographic printing ink. The problem that in the prior art, the water-based flexographic printing ink is large in viscosity, low in mobility, low in adhesion fastness, poor in stability, low in drying rate and high in cost is solved.

Description

technical field [0001] The invention belongs to the technical field of printing and reproduction, and relates to an ultraviolet light-curable water-based flexo printing ink, and also relates to a preparation method of the above-mentioned ultraviolet light-curable water-based flexo printing ink. Background technique [0002] Water-based flexo printing inks are made by mixing polymer resins, emulsions, pigments, solvents (mainly water) and related additives through physical and chemical processes. Water-based ink has the characteristics of no volatile organic solvents, non-flammability, no damage to the health of printing operators, and no pollution to the environment. As a new type of printing ink, water-based ink eliminates the hazards of toxic and harmful substances in solvent-based inks to humans and packaging and printing products, and is especially suitable for packaging that requires strict hygiene conditions such as food, beverages, and pharmaceuticals. Printed produc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/106C09D11/037C09D11/03C09D11/033
CPCC09D11/106C09D11/037C09D11/03C09D11/033
Inventor 刘昕郭蕊毛旭王龙飞刘澎
Owner XIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products