Soil conditioner and preparation method and use method thereof

A soil conditioner and coconut soil technology, applied in the field of soil remediation, can solve problems such as inability to play a regulating role, incomplete improvement of soil problems, environmental impact, etc. Effect

Inactive Publication Date: 2020-07-10
武汉市秀谷科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, there are still some problems in the existing soil conditioners: (1) there are still deficiencies in increasing production and improving the quality of crops; (2) most of the soil conditioners used are chemical components. On the contrary, it causes a more serious impact on the environment; (3) Often only one or two kinds of soil problems are improved, but in reality, many situations often coexist, and the soil problems cannot be completely improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soil conditioner and preparation method and use method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] (1) Composition of raw materials: coconut soil 43kg, oyster shell powder 24kg, distiller's grains 20kg, sodium alginate 12kg, humic acid 10kg and titanium oxide 1kg.

[0036] (2) Preparation method:

[0037] ① The ultrafine pulverization powder of each raw material component is obtained by superfine pulverization of each raw material component, the pulverization pressure of superfine pulverization is 0.56Mpa, and the feed pressure is 0.56Mpa;

[0038] ② Weigh the ultrafine pulverized powder of each raw material component, mix and stir, and mix and stir at a speed of 20r / min for 8 minutes to obtain a premix;

[0039] ③ Prepare the premixed material into particles with a particle size of 1 mm to obtain the finished product.

[0040] In order to further optimize the above-mentioned technical scheme, oyster shell powder is prepared according to the following scheme: ① Oyster shells are calcined in two stages to obtain high-temperature calcined oyster shells, wherein, the f...

Embodiment 2

[0042] (1) Composition of raw materials: coconut soil 58kg, oyster shell powder 32kg, distiller's grains 28kg, sodium alginate 17kg, humic acid 16kg and titanium oxide 5kg.

[0043] (2) Preparation method:

[0044] ① The ultrafine pulverization powder of each raw material component is obtained by superfine pulverization of each raw material component, the pulverization pressure of superfine pulverization is 0.56Mpa, and the feed pressure is 0.56Mpa;

[0045] ② Weigh the ultrafine pulverized powder of each raw material component, mix and stir, and mix and stir at a speed of 25r / min for 15min to obtain a premix;

[0046] ③ Prepare the premixed material into particles with a particle size of 4mm to obtain the finished product.

[0047] In order to further optimize the above technical scheme, oyster shell powder is prepared according to the following scheme: ① Oyster shells are calcined in two stages to obtain high-temperature calcined oyster shells, wherein, the first calcining ...

Embodiment 3

[0049] (1) Composition of raw materials: coconut soil 48kg, oyster shell powder 29kg, distiller's grains 23kg, sodium alginate 15kg, humic acid 13kg and titanium oxide 3kg.

[0050] (2) Preparation method:

[0051] ① The ultrafine pulverization powder of each raw material component is obtained by superfine pulverization of each raw material component, the pulverization pressure of superfine pulverization is 0.56Mpa, and the feed pressure is 0.56Mpa;

[0052] ② Weigh the ultrafine pulverized powder of each raw material component, mix and stir, and mix and stir at a speed of 22r / min for 10min to obtain a premix;

[0053] ③ Prepare the premix into particles with a particle size of 3mm to obtain the finished product.

[0054] In order to further optimize the above-mentioned technical scheme, oyster shell powder is prepared according to the following scheme: ① Oyster shells are calcined in two stages to obtain high-temperature calcined oyster shells, wherein, the first calcination...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a soil conditioner which is prepared from the following components in parts by mass: 43 to 58 parts of coconut soil, 24 to 32 parts of oyster shell powder, 20 to 28 parts of vinasse, 12 to 17 parts of sodium alginate, 10 to 16 parts of humic acid and 1 to 5 parts of titanium oxide. Compared with the soil conditioners in the prior art, the soil conditioner has the beneficialeffects that (1) all the components have a synergistic effect so that various soil problems such as acidification, trace element deficiency, salinization, hardening, heavy metal pollution and continuous cropping obstacles are effectively improved; (2) the yield and the quality of crops are effectively improved; and (3) most of the raw materials are natural components and have no pollution to theenvironment.

Description

technical field [0001] The invention relates to the technical field of soil remediation, and more specifically relates to a soil conditioner and its preparation and use methods. Background technique [0002] About 50% of the soil in my country has many problems such as acidification, lack of trace elements, imbalance of flora, salinization, compaction, heavy metal pollution, lack of organic matter, obstacles to continuous cropping, etc., which seriously affect the yield and quality of crops, and some even fail to harvest. [0003] However, there are still some problems in the existing soil conditioners: (1) there are still deficiencies in increasing production and improving the quality of crops; (2) most of the soil conditioners used are chemical components. On the contrary, it causes a more serious impact on the environment; (3) Often only one or two kinds of soil problems are improved, but in reality, many situations often coexist, and the soil problems cannot be completel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K17/40C09K101/00C09K109/00
CPCC09K17/40C09K2101/00C09K2109/00
Inventor 冯才声张质
Owner 武汉市秀谷科技有限公司