Embossed gold porcelain manufacturing technology
A production process and embossing technology, which is applied in the printing process, the process for producing decorative surface effects, decorative art, etc., can solve the problems of flower surface decoration that cannot satisfy high-consumption groups, insufficient relief effect, and insufficient mechanical strength. Achieve the effect of obvious three-dimensional sculpture, excellent gloss and simple processing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0045] The production process of embossed golden flower paper with one-time baking flower forming includes:
[0046] Design decorative styles and patterns;
[0047] Color-separate plate-making according to the design pattern and output the plate-making film;
[0048] Raw material pretreatment: mainly embossing powder C2Y-277 produced by Shenzhen Windsor Ceramic Glass Material Co., Ltd.;
[0049]Ink preparation: according to the mass ratio of C2Y-277 embossing powder produced by Shenzhen Windsor Ceramic Glass Material Co., Ltd.: varnish Y-607 = 99:64, weigh and feed the materials, grind them through a three-roll mill, grind them 4 times, and wait for the machine print;
[0050] Screen plate preparation: according to the pure water: Japanese KAHU brand KH8000 type diazo photosensitive glue: photosensitizer = 3.5:90:2 mass ratio to prepare photosensitive glue, let it stand for 2-3 hours to defoam, use 120-160 mesh for relief plate For the nylon screen screen, apply the photose...
Embodiment 2
[0055] The production process of the second baking embossed embossed golden decal paper includes:
[0056] Design decorative style, pattern.
[0057] Color-separate plate-making according to the design pattern and output the plate-making film.
[0058] Raw material pretreatment: mainly relief powder C2Y-275 produced by Shenzhen Windsor Ceramic Glass Material Co., Ltd.
[0059] Ink preparation: weighing and feeding according to the mass ratio of relief powder C2Y-275: 7020 type varnish: 8030 type varnish = 99: 35: 47, grinding by a three-roll mill, grinding 4 times, and set aside.
[0060] The screen preparation is the same as in Example 1.
[0061] According to the conventional screen printing method, print according to the color separation sequence, according to the design requirements, the embossed pattern will be printed multiple times (generally more than 3 times) without dismantling the plate, and after each printing, it will be dried by 35°C drying wind. Seal the oil ...
Embodiment 3
[0065] The production process of embossed gold porcelain with secondary baking, including:
[0066] 1. Design decoration style and pattern.
[0067] 2. Color-separate and plate-making according to the design pattern and output the plate-making film.
[0068] 3. Preparation of printing screen: according to the ratio (mass ratio) of pure water: diazo photosensitive glue: photosensitizer = 3.5:90:2, prepare the photosensitive glue, let it stand for 2 to 3 hours to defoam, and print the relief part with 120 mesh For the screen plate, apply the photosensitive glue 4 times according to the method of the first 4 and the last 24, and put the printed screen into a drying oven below 30°C for 20 minutes to dry for 20 minutes. Developed, dried and set aside.
[0069] 4. Ink preparation: Weigh and feed according to the ratio of embossing powder: varnish = 99:82, grind with a three-roll mill, and grind 4 times to obtain the ink for the embossed part.
[0070] The preparation method of Ga...