Sleeve grouting material for low-temperature steel bar connection and using method thereof

A sleeve grouting, low temperature technology, which is applied in the field of cement-based building materials and prefabricated building materials, can solve the problems that cannot meet construction requirements, cannot be used for ultra-low temperature steel bar connection sleeves, etc., so as to avoid the loss of grouting material strength. , to ensure the quality of construction, to ensure the effect of liquidity

Active Publication Date: 2020-07-24
CNBM ZHONGYAN TECH
View PDF12 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To sum up, low-temperature grouting materials cannot meet the construction requirements at temperatures below -10°C or lower, and cann

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sleeve grouting material for low-temperature steel bar connection and using method thereof
  • Sleeve grouting material for low-temperature steel bar connection and using method thereof
  • Sleeve grouting material for low-temperature steel bar connection and using method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] 25 parts of fast setting rapid hardening high belite sulfoaluminate cement;

[0047] Portland cement 23 parts;

[0048] 3 parts of ultra-high strength sulfoaluminate cement;

[0049] 0.7 parts of gypsum;

[0050] 2 parts of superfine fly ash;

[0051] 45 parts of aggregate;

[0052] 0.3 parts of nanocrystalline core;

[0053] 0.5 parts of sodium nitrite;

[0054] 0.2 parts of powder polycarboxylate high-performance water reducer;

[0055] 0.08 part of polyether defoamer;

[0056] 0.11 parts of expansion agent, including 0.1 part of HCSA expansion agent and 0.01 part of plastic expansion agent;

[0057] 0.001 parts of cellulose ether, the viscosity is 400mPa·s;

[0058] Viscosity reducer 0.15 parts;

[0059] Mix the above-mentioned raw materials in proportion to prepare the sleeve grouting material for low-temperature steel bar connection, mix it with a mixer with 12% water consumption, and put it aside for 2 minutes to defoam before construction and application...

Embodiment 2

[0064] 30 parts of fast setting rapid hardening high belite sulfoaluminate cement;

[0065] Portland cement 15 parts;

[0066] 5 parts of ultra-high strength sulfoaluminate cement;

[0067] 1.4 parts of gypsum;

[0068] 5 parts of silica fume;

[0069] 40 parts of aggregate;

[0070] 1.0 parts of nanocrystalline core;

[0071] 1.5 parts of sodium nitrite;

[0072] 0.48 parts of powder polycarboxylate high-performance water reducer;

[0073] 0.09 part of polyether defoamer;

[0074] 0.13 parts of expansion agent, including 0.1 part of HCSA expansion agent and 0.03 part of plastic expansion agent;

[0075] 0.001 parts of cellulose ether, the viscosity is 400mPa·s;

[0076] 0.4 parts of viscosity reducer;

[0077] Mix the above-mentioned raw materials in proportion to prepare the sleeve grouting material for low-temperature steel bar connection, mix it with a mixer with 11% water consumption, and put it aside for 2 minutes to defoam before construction and application. ...

Embodiment 3

[0083] 20 parts of fast setting rapid hardening high belite sulfoaluminate cement;

[0084] Portland cement 30 parts;

[0085] 0.5 parts of ultra-high strength sulfoaluminate cement;

[0086] 0.1 parts of gypsum;

[0087] 3.6 parts of superfine fly ash;

[0088] 45 parts of aggregate;

[0089] 0.1 part of nanocrystalline core;

[0090] Calcium nitrite 0.2 parts;

[0091] 0.3 parts of powder polycarboxylate high-performance water reducer;

[0092] 0.03 part of polyether defoamer;

[0093] 0.11 parts of expansion agent, including 0.1 part of HCSA expansion agent and 0.01 part of plastic expansion agent;

[0094] 0.001 parts of cellulose ether, the viscosity is 400mPa·s;

[0095] Viscosity reducer 0.1 part;

[0096] Mix the above-mentioned raw materials in proportion to prepare the sleeve grouting material for low-temperature steel bar connection, mix it with a mixer with 11% water consumption, and put it aside for 2 minutes to defoam before construction and application....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a sleeve grouting material for low-temperature steel bar connection and a using method thereof. Fast-setting, fast-hardening and high-belite sulphoaluminate cement, Portland cement, ultrahigh-strength sulphoaluminate cement, gypsum, an admixture, aggregate, nanocrystalline nucleuses, an antifreeze agent, a powder polycarboxylic acid high-performance water reducing agent, apolyether defoamer, an expanding agent, cellulose ether and a viscosity reducer are used as raw materials, and the ultralow-temperature construction requirement of-15 DEG C to 10 DEG C can be met.

Description

technical field [0001] The invention belongs to the field of cement-based building materials, in particular to the field of prefabricated and assembled building materials, in particular to a grouting material for sleeve grouting construction for steel bar connection under low temperature conditions. Background technique [0002] With the development of prefabricated buildings, the construction technology of steel bar sleeve grouting connection is becoming more and more mature. The steel bar sleeve grouting connection technology is not limited by the diameter of the steel bar, the type of load and the height of the building. It has a wide range of applications and is recognized worldwide as a PC The most valuable technology for connecting components. It means that after the prefabricated components are hoisted, the sleeve grouting material for steel bar connection is injected into the sleeve. After the slurry solidifies and hardens, the steel bar, sleeve and slurry form a who...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/14C04B111/70
CPCC04B28/14C04B2111/70C04B2201/50C04B2111/00008C04B7/32C04B7/02C04B18/08C04B18/146C04B18/12C04B14/06C04B18/0481C04B18/0409C04B14/08C04B14/303C04B2103/601C04B24/24C04B24/32C04B22/126C04B24/125C04B24/085C04B24/2623C04B22/062C04B22/10C04B14/28C04B14/042C04B24/383C04B24/124
Inventor 瞿海洋朱玉雪范德科马凯李婷王泽瀚张帅王健
Owner CNBM ZHONGYAN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap