A preparation method of heat-not-burn cigarette core material

A heat-not-burn, heat-conducting material technology, applied in tobacco, tobacco processing, application, etc., can solve the problems of poor smoothness, poor thermal conductivity, and poor product quality of cigarette core materials, achieve good sensory quality, improve thermal conductivity, The effect of reducing thermal resistance problems

Active Publication Date: 2021-11-23
云南佩林科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the core material of heat-not-burn cigarettes adopts a coating process. The coating liquid is sprayed on the substrate and then dried. The smoke core material produced by this process has poor smoothness, low density, and poor thermal conductivity. problems, resulting in poor product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of heat-not-burn cigarette core material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] S1. Perform high-temperature puffing treatment on 5 parts by weight of the heat-conducting material, the treatment time is 20s, the treatment temperature is 300°C, and the discharge temperature is 80°C to obtain a fluffy heat-conducting material;

[0028] S2, performing anhydrous fibrillation treatment on 5 parts by weight of the fiber material to obtain the treated fiber material with a length of 0.1 mm;

[0029] S3, pulverizing and sieving the tobacco raw material of 40 parts by weight to obtain smoke powder, the particle size is 50 mesh, and the smoke powder is a powder;

[0030] S4. Mix the treated thermally conductive material with powder and fiber material uniformly to obtain mixture A, mix uniformly 5 parts by weight of fuming agent and 1 part by weight of auxiliary materials to obtain mixture B, and mix mixture A and mixture B Mix evenly, after cloth, pre-pressing, multi-stage precision pressing, drying and rolling, the heat-not-burn cigarette core material can ...

Embodiment 2

[0033] S1. Perform high-temperature puffing treatment on 30 parts by weight of the heat-conducting material, the treatment time is 1200s, the treatment temperature is 1200°C, and the discharge temperature is 100°C to obtain a fluffy heat-conducting material;

[0034] S2, performing anhydrous fibrillation treatment on 30 parts by weight of the fiber material to obtain the treated fiber material with a length of 4.0 mm;

[0035] S3, pulverize and sieve 90 parts by weight of tobacco raw materials to obtain smoke powder, with a particle size of 1000 mesh; take 100% by weight of tobacco powder, extract, separate solid-liquid, concentrate, and dry to obtain a concentrated extract, and then Crush the concentrated extract to 1000 mesh, then adjust the density to 1.5g / m with distilled water 3 , to obtain liquid material; the solid slag produced in the solid-liquid separation step is crushed to obtain soot residue, which is powder;

[0036] S4. Mix the treated heat-conducting material ...

Embodiment 3

[0039] S1. Perform high-temperature puffing treatment on 17.5 parts by weight of heat-conducting material, the treatment time is 610s, the treatment temperature is 750°C, and the discharge temperature is 90°C to obtain a fluffy heat-conducting material;

[0040] S2, performing anhydrous fibrillation treatment on 17.5 parts by weight of the fiber material to obtain the treated fiber material with a length of 2.0 mm;

[0041] S3, pulverize and sieve 65 parts by weight of tobacco raw materials to obtain tobacco powder with a particle size of 525 mesh; take 50% by weight of tobacco powder, extract, separate solid-liquid, concentrate, and dry to obtain a concentrated extract, and then Crush the concentrated extract to 700 mesh, then adjust the density to 1.25g / m with distilled water 3 , to obtain a liquid material; the solid slag produced in the solid-liquid separation step is crushed to obtain smoke residue, and the smoke residue is mixed with the remaining smoke powder to obtain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
elongationaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a heat-not-burn cigarette core material, which comprises the steps of pretreatment and mixing of raw materials, cloth distribution, pre-pressing, multi-stage fine pressing, drying and rolling. The present invention can be integrally molded into a heat-not-burn cigarette core material with smooth surface, high density and high thermal conductivity without carrier coating, and meanwhile, the smooth surface and high density of the core material can minimize the impact on the surface and internal voids of the core material. The addition of heat-not-burning materials can improve the heat-conducting performance of the core material, ensuring efficient smoke generation and effective volatilization of smoke in the formed heat-not-burn cigarettes, so that heat-not-burn cigarette products have good sensory quality and user satisfaction sense of experience.

Description

technical field [0001] The invention belongs to the technical field of heat-not-burn cigarettes, in particular to a method for preparing a core material of heat-not-burn cigarettes. Background technique [0002] Under the background of increasingly severe tobacco control environment, the sales of traditional tobacco products have stagnated or even declined in some developed and developing countries. With the general improvement of people's health awareness and the rapid development of smart microelectronics technology, new tobacco products The development of products is developing in a blowout style. Representative non-guided tobacco products on the market mainly include heat-not-burn tobacco products and smokeless tobacco products. As a major product in new tobacco products, heat-not-burn cigarettes have generally been valued by tobacco companies in their research and development. In the prior art, the core material of heat-not-burn cigarettes adopts a coating process. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A24B15/167
CPCA24B15/167
Inventor 周欣成郭天荣其他发明人请求不公开姓名
Owner 云南佩林科技有限公司