A method for constructing a baking curve of a lithium-ion battery pole piece and a baking method thereof

A technology for lithium ion batteries and battery pole pieces, which is applied in the field of lithium ion battery processing and manufacturing, can solve the problems of re-baking, difficulty in ensuring qualified moisture, affecting production efficiency, etc., so as to improve efficiency, save baking time and energy consumption, The effect of improving baking efficiency

Active Publication Date: 2021-11-09
华鼎国联四川动力电池有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the above-mentioned conventional vacuum baking process can solve the problem of dehydration of most lithium-ion battery pole pieces, it is difficult to ensure the initial moisture content due to the different initial moisture content of the same system and different batches of pole pieces before baking. The moisture content of pole pieces with high content is qualified after baking
Usually, it is necessary to test the moisture content after the baking is completed. If it is judged to be unqualified, it needs to be baked again, which seriously affects the production efficiency.
[0005] More importantly, when replacing the battery pole piece with a new material system for baking, it is usually difficult to directly select the optimal baking time of the new system. The results of multiple tests have determined the optimal baking conditions; moreover, in the subsequent practical application of this baking condition, there will still be the aforementioned problem that batches of pole pieces with high initial moisture content fail to pass the baking and need to be baked again

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for constructing a baking curve of a lithium-ion battery pole piece and a baking method thereof
  • A method for constructing a baking curve of a lithium-ion battery pole piece and a baking method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment is aimed at baking the lithium-ion battery pole piece of graphite negative electrode material.

[0035] Take a sample of the negative pole piece to be baked, the size of the sample has no effect, use the Karl Fischer moisture tester to test the initial moisture content of the pole piece before baking, and record it as A0 = 838ppm; and take the same batch and the same The pole pieces preserved under storage conditions were loaded into a high-vacuum oven according to the predetermined baking quantity of 27,000 pieces, and set aside. In this embodiment, the pole piece baking setting conditions with different initial moisture contents are exactly the same, and the temperature, pressure, and quantity conditions are completely consistent with the initial curve construction, so that they can be used as the cut-off conditions for the subsequent baking process, and There is no special requirement for the initial moisture content in the curve construction stage, a...

Embodiment 2

[0048] This embodiment is aimed at baking the lithium-ion battery pole piece made of nickel-cobalt-manganese ternary material.

[0049] Take a sample of the positive pole piece to be baked, use the Karl Fischer moisture tester to test the initial moisture content of the pole piece before baking, and record it as A0=440ppm; 27,000 pieces are loaded into a high-vacuum oven according to the predetermined baking quantity and set aside.

[0050] Vacuumize the drying chamber of the oven to ≤200Pa, fill it with nitrogen, and preheat at a preheating temperature of 130°C for 5 hours under the protection of nitrogen, so that all pole pieces in the drying chamber reach a drying temperature of 130°C.

[0051] Under the condition of 130°C heat preservation, the drying chamber was further evacuated to an initial pressure value of 50Pa. At this time, the pole piece had begun to dewater, and the pressure in the drying chamber gradually increased to 200Pa. During this process, the pressure was...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of lithium-ion battery processing and manufacturing, and in particular relates to a method for constructing a baking curve based on different materials for lithium-ion battery pole pieces, and further discloses a baking method for lithium-ion battery pole pieces. The baking curve construction method and baking method of the lithium ion battery pole piece of the present invention, first obtain the baking pressure change rate curves of different material systems through an experiment and data analysis, and characterize the removal process during the baking process through the pressure change rate. Water rate, select the appropriate pressure change rate as the baking end condition, and automatically adjust the vacuum baking time correspondingly, which can quickly determine the baking conditions of the pole pieces of the new material system, and can be used for one-time effective baking of pole pieces with different initial water content conditions Baking, effectively improve the baking efficiency.

Description

technical field [0001] The invention belongs to the technical field of lithium-ion battery processing and manufacturing, and in particular relates to a method for constructing a baking curve based on different materials for lithium-ion battery pole pieces, and further discloses a baking method for lithium-ion battery pole pieces. Background technique [0002] During the processing and manufacturing of lithium-ion batteries, since moisture will have adverse effects on the performance of the battery such as gas production, capacity, internal resistance, and cycle, it is necessary to remove the moisture in the pole pieces through the baking process to ensure that the moisture content in the battery is lower than Certain standards to ensure the performance of the battery. [0003] In the prior art, the dehydration method of lithium-ion battery pole pieces is generally by placing them in a vacuum oven and setting a certain temperature, vacuum degree, and time to bake the pole pie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F26B5/04F26B25/00F26B25/22H01M10/0525G06T11/20
CPCF26B5/04F26B25/00F26B25/22G06T11/203H01M10/0525Y02E60/10
Inventor 安莎李卫红沈修岗
Owner 华鼎国联四川动力电池有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com