Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A lightweight isolation pier material

An isolation pier, lightweight technology, applied in the direction of carbon preparation/purification, etc., can solve the problems of no cushioning effect, isolation pier is not easy to move, etc., to achieve the effect of enhancing mechanical properties, reducing material cracking, and increasing stability

Active Publication Date: 2022-02-01
湖南翰坤实业有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to provide a lightweight isolation pier material to solve the problem that the existing isolation pier is not easy to move and has no cushioning effect when it is hit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The lightweight isolation pier material of this embodiment is prepared from the following raw materials, and the parts by weight of each component of the raw materials are as follows:

[0038] 90 parts of cement, 20 parts of clay, 20 parts of coarse sand, 10 parts of biochar, 5 parts of asbestos, 15 parts of chitosan, 15 parts of ABS, 30 parts of EVA, 40 parts of polypropylene, 15 parts of epoxy resin, polyvinyl chloride 8 servings.

[0039] The preparation method of the above-mentioned lightweight isolation pier material is as follows:

[0040] (1) Mix and stir ABS, EVA, polypropylene, epoxy resin, and polyvinyl chloride at 100°C and 100KPa at a speed of 500r / min to obtain mixture A;

[0041] (2) Chitosan and water are mixed and swelled at a ratio of 1:5 to obtain a chitosan swelling solution; cement, clay, coarse sand, asbestos, biochar, chitosan swelling solution and an appropriate amount of water are mixed continuously at 800r / min After stirring to form a gel-like...

Embodiment 2

[0050] The lightweight isolation pier material of this embodiment is prepared from the following raw materials, and the parts by weight of each component of the raw materials are as follows:

[0051] 100 parts of cement, 30 parts of clay, 50 parts of coarse sand, 20 parts of biochar, 10 parts of asbestos, 10 parts of chitosan, 10 parts of ABS, 25 parts of EVA, 30 parts of polypropylene, 10 parts of epoxy resin, polychloride 4 parts vinyl.

[0052] The preparation method of the above-mentioned lightweight isolation pier material is as follows:

[0053] (1) Mix and stir ABS, EVA, polypropylene, epoxy resin, and polyvinyl chloride at 120°C and 120KPa at a speed of 650r / min to obtain mixture A;

[0054] (2) Chitosan and water are mixed and swelled at a ratio of 1:1 to obtain a chitosan swelling solution; cement, clay, coarse sand, asbestos, biochar, chitosan swelling solution and an appropriate amount of water are mixed continuously at 1000r / min After stirring to form a gel-like...

Embodiment 3

[0063] The lightweight isolation pier material of this embodiment is prepared from the following raw materials, and the parts by weight of each component of the raw materials are as follows:

[0064] 95 parts of cement, 25 parts of clay, 30 parts of coarse sand, 15 parts of biochar, 8 parts of asbestos, 12 parts of chitosan, 12 parts of ABS, 25 parts of EVA, 35 parts of polypropylene, 12 parts of epoxy resin, polyvinyl chloride 5 servings.

[0065] The preparation method of the above-mentioned lightweight isolation pier material is as follows:

[0066] (1) Mix and stir ABS, EVA, polypropylene, epoxy resin, and polyvinyl chloride at 110°C and 110KPa at a speed of 600r / min to obtain mixture A;

[0067] (2) Chitosan and water are mixed and swelled at a ratio of 1:8 to obtain a chitosan swelling solution; cement, clay, coarse sand, asbestos, biochar, chitosan swelling solution and an appropriate amount of water are mixed continuously at 900r / min After stirring to form a gel-like...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of isolation facilities, and specifically discloses a lightweight isolation pier material, which is prepared from the following raw materials: cement, clay, coarse sand, biochar, asbestos, chitosan, ABS, EVA, polypropylene, Epoxy resin, polyvinyl chloride; the preparation steps are as follows: (1) Mix and stir ABS, EVA, polypropylene, epoxy resin, and polyvinyl chloride to obtain mixture A; (2) Mix cement, clay, coarse sand, asbestos, Mix biochar, chitosan swelling solution and appropriate amount of water to obtain mixture B; (3) place the prepared alloy skeleton in the mold according to the required specifications of the isolation pier, pour mixture B into it, and release it after natural drying The embryo body of the bottom tire is obtained by curing; (4) a casing made of the mixture A coated on the periphery of the embryo body of the bottom tire; (5) a fluorescent pattern is painted on the side of the casing, and an isolation pier material is obtained after drying. The isolation pier material prepared by the invention has good noise reduction and sound absorption performance, and can ensure driving safety.

Description

technical field [0001] The invention relates to the technical field of isolation facilities, in particular to a lightweight isolation pier material. Background technique [0002] Isolation piers are one of the main traffic facilities, which can effectively eliminate vehicles from occupying sidewalks, sidewalks, and fire exits, and play the role of dividing roads, separating areas, diverting traffic, and guiding warnings. With the continuous improvement of people's pursuit of driving safety and comfort, more and more roads have been built for noise protection. At the same time, as there are more and more vehicles on the road, the road is built longer and wider, and the emission of vehicle exhaust and the dust raised by traffic flow are important factors of air pollution. The smog weather formed by PM2.5 seriously affects people's health. The living space, the road absorbs the heat energy of the sun, the metal shell of the car absorbs heat and the hot smoke emitted by the exh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00C01B32/05C08L23/12C08L55/02C08L23/08C08L63/00C08L27/06C04B111/40C04B111/52
CPCC04B28/00C08L23/12C01B32/05C08L2205/035C04B2111/40C04B2111/52C08L55/02C08L23/0853C08L63/00C08L27/06C04B18/0418C04B14/06C04B14/022C04B14/40C04B24/38C04B32/02
Inventor 康望才
Owner 湖南翰坤实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More