High-crack-resistance and high-bending-resistance assembled plate based on waste gypsum board and preparation method thereof

A high-bending and assembly-type technology, applied in the field of building materials, can solve the problems of high value-added utilization such as crack resistance and poor bending resistance, so as to achieve high value-added utilization, speed up the reaction rate, and solve the problem of crystal transformation Effect

Active Publication Date: 2020-10-09
CHINA CONSTR TECH WUHAN CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main purpose of the present invention is to provide a high-crack-resistant gypsum board prepared by using waste gypsum board to solve the deficiencies in the existing technology, such as the difficulty of high value-added utilization of waste gypsum board, and the poor crack resistance and flexural performance of ordinary cement-based fabricated plates. High-bending-resistant prefabricated boards, the waste gypsum boards are converted into crystal forms to prepare regenerated α-type hemihydrate gypsum powder and regenerated α-type semi-crystal whiskers, and replace them with cement and other cementitious materials to prepare high-crack-resistant Assembled plates with high flexural resistance; and the preparation method involved is simple, low in cost, and environmentally friendly, suitable for popularization and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A high-crack-resistant and high-fold-resistant assembled board based on waste gypsum boards, the preparation method of which comprises the following steps:

[0031] 1) Fully crush the waste gypsum board with a crusher, dry it in an oven at 40°C to constant weight, then fully grind the crushed gypsum board with a ball mill, pass through a 50-mesh sieve, and remove the inert components with larger particle sizes Sorting and protective paper, sorting out waste gypsum powder;

[0032] 2) a part of the waste gypsum powder of step 1) gained is mixed with calcium chloride solution (15wt%) and activator (tartaric acid, succinic acid, nano silicon dioxide, sulfuric acid in a molar ratio of 20:10:5:1 Mix and form (wherein, tartaric acid, succinic acid are analytically pure grade; Nano silicon dioxide is analytically pure, average particle diameter 37nm; The concentration of sulfuric acid is 10wt%, and its consumption is based on the introduced H 2 SO 4 ), fully mixed at a mass ...

Embodiment 2

[0037] A high-crack-resistant and high-fold-resistant assembled board based on waste gypsum boards, the preparation method of which comprises the following steps:

[0038] 1) Fully crush the waste gypsum board with a crusher, dry it in an oven at 45°C to constant weight, then use a ball mill to fully grind the broken gypsum board, pass through a 100-mesh sieve, and remove the inert components with larger particle sizes Sorting and protective paper, sorting out waste gypsum powder;

[0039] 2) a part of the waste gypsum powder in step 1) gained is mixed with calcium chloride solution (20wt%) and activator (tartaric acid, succinic acid, nano silicon dioxide, sulfuric acid by the mole of 20:13:6:1.3) than mixed (wherein, tartaric acid, succinic acid are analytically pure grades; nano silicon dioxide is analytically pure, with an average particle diameter of 37nm; the concentration of sulfuric acid is 10wt%, and its consumption is based on the H 2 SO 4 ), fully mixed according t...

Embodiment 3

[0044] A high-crack-resistant and high-fold-resistant assembled board based on waste gypsum boards, the preparation method of which comprises the following steps:

[0045] 1) Fully crush the waste gypsum board with a crusher, dry it in an oven at 43°C to constant weight, then fully grind the crushed gypsum board with a ball mill, pass through a 100-mesh sieve, and remove the inert components with larger particle sizes Sorting and protective paper, sorting out waste gypsum powder;

[0046] 2) a part of the waste gypsum powder in the step 1) gained is mixed with calcium chloride solution (17wt%) and activator (tartaric acid, succinic acid, nano silicon dioxide, sulfuric acid in a molar ratio of 20:15:7:2 Mix and form (wherein, tartaric acid, succinic acid are analytically pure grade; Nano silicon dioxide is analytically pure, average particle diameter 37nm; The concentration of sulfuric acid is 10wt%, and its consumption is based on the introduced H 2 SO 4 ), fully mixed accor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-crack-resistance and high-bending-resistance assembled plate based on a waste gypsum board. The high-crack-resistance and high-bending-resistance assembled plate comprises the following components in parts by weight: 75-90 parts of regenerated alpha-type semi-hydrated gypsum powder, 10-25 parts of regenerated alpha-type semi-crystal whisker, 5-10 parts of EPS light aggregate and 30-35 parts of water, wherein the regenerated alpha-type semi-hydrated gypsum powder and the regenerated alpha-type semi-crystal whiskers are respectively formed by performing crystal form conversion treatment on waste gypsum boards. According to the invention, the waste gypsum board is used as a main raw material to respectively prepare the regenerated alpha-type semi-hydrated gypsumpowder and the regenerated alpha-type semi-crystal whiskers, and the regenerated alpha-type semi-hydrated gypsum powder and the regenerated alpha-type semi-crystal whiskers are used for completely replacing cementing materials such as cement to prepare the high-crack-resistance and high-bending-resistance assembled board so that a brand new thought is provided for preparing low-cost and high-strength anti-crack-resistance boards; and high-added-value utilization of the waste gypsum board can be achieved, and important economic and environmental benefits are achieved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a high-crack-resistant and high-bending-resistant assembled board based on waste gypsum boards and a preparation method thereof. Background technique [0002] Abandoned gypsum board is a kind of construction waste produced in large quantities, which occupies a large amount of land and wastes resources, and has not yet been effectively utilized as a resource. From the perspective of the basic composition characteristics and technical principles of the material, the main material of the waste gypsum board is dihydrate gypsum, which can be converted into hemihydrate gypsum as a cementitious material after a certain process, and then the prefabricated board can be produced. However, because the dihydrate gypsum crystal form in the waste gypsum board is messy and finely divided, and the components are complex, it is difficult to realize the crystal transformatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B11/26C04B11/032C04B11/024C04B20/02C04B111/34C04B18/04
CPCC04B11/024C04B11/032C04B11/262C04B20/023C04B28/146C04B2111/343C04B2201/50C04B14/383C04B16/08C04B18/0445Y02W30/91
Inventor 卢文达潘寒廖峰张磊吴世明
Owner CHINA CONSTR TECH WUHAN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap