Modifier for repairing heavy metal contaminated soil and preparation method and application of modifier
A technology that pollutes soil and heavy metals, applied in the field of ecological environmental protection, can solve the problems of land reclamation and reuse, difficulty in meeting the pollution of various mixed heavy metals in soil, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0030] An improving agent for repairing heavy metal polluted soil, in parts by weight, the improving agent consists of 45 parts of modified zeolite, 25 parts of lime, 5 parts of blast furnace slag, 10 parts of organic fertilizer, 10 parts of humic acid and 5 parts of microbial inoculant mixed; the modified zeolite is mixed with calcined zeolite and a mixed modifier, the quality of the mixed modifier accounts for 15wt% of the quality of the modified zeolite, and the mixed modifier is composed of ammonium phosphate and Cyanex 301 is mixed at a mass ratio of 3:1.
[0031] Above-mentioned improver is obtained by following method:
[0032] (1) Weigh each raw material according to parts by weight;
[0033] (2) Mix the modified zeolite, blast furnace slag, and organic fertilizer to obtain a mixture 1, and mix the lime and humic acid to obtain a mixture 2;
[0034] (3) Let the mixture 1 and the mixture 2 stand for 0.5 hours respectively, combine and mix well, then add the microbial ...
Embodiment 2
[0038] An improving agent for repairing heavy metal polluted soil, in parts by weight, the improving agent consists of 40 parts of modified zeolite, 20 parts of lime, 5 parts of blast furnace slag, 15 parts of organic fertilizer, 10 parts of humic acid and 10 parts of microbial inoculant mixed; the modified zeolite is mixed with calcined zeolite and a mixed modifier, the quality of the mixed modifier accounts for 15wt% of the quality of the modified zeolite, and the mixed modifier is composed of ammonium phosphate and Cyanex 301 is mixed at a mass ratio of 3:1.
[0039] The above improving agent was prepared according to the method of Example 1, except that in step (3), mixture 1 and mixture 2 were left to stand for 2 hours respectively.
[0040] Wherein, the modified zeolite is prepared according to the method of Example 1, the difference is that the microwave irradiation power is 1100W, and the ultrasonic power is 1800W.
Embodiment 3
[0042] An improving agent for repairing heavy metal polluted soil, in parts by weight, the improving agent consists of 30 parts of modified zeolite, 40 parts of lime, 5 parts of blast furnace slag, 15 parts of organic fertilizer, 5 parts of humic acid and 5 parts of microbial bacterial agent mixed; the modified zeolite is mixed with calcined zeolite and a mixed modifier, the quality of the mixed modifier accounts for 15wt% of the quality of the modified zeolite, and the mixed modifier is composed of ammonium phosphate and Cyanex 301 is mixed at a mass ratio of 3:1.
[0043] The above improving agent was prepared according to the method of Example 1, except that in step (3), mixture 1 and mixture 2 were left to stand for 1 hour respectively.
[0044]Wherein, the modified zeolite is prepared according to the method of Example 1, the difference is that the microwave irradiation power is 1200W, and the ultrasonic power is 2000W.
PUM
Property | Measurement | Unit |
---|---|---|
particle size (mesh) | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com