Lubricating oil modifying aid and preparation method and application thereof

A lubricating oil and modification technology, which is applied in the field of lubricating oil, can solve the problems of poor lubricity of perfluoropolyether lubricating oil, etc., and achieve the effects of reducing friction coefficient, high specific surface area and strong adsorption capacity

Active Publication Date: 2020-10-23
CHIAPHUA COMPONENTS SHENZHEN +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of this application is to provide a lubricating oil modification additive and its preparation method, aiming at solving the problem of poor lubricity of perfluoropolyether lubricating oil under low temperature conditions in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The second aspect of the embodiment of the present application provides a method for preparing a lubricating oil modification additive, comprising the following steps:

[0031] S01. Provide fluorinated expanded graphite;

[0032] S02. Mixing fluorinated expanded graphite and permanent magnetic material particles to obtain a first mixture, and performing ball milling and magnetizing treatment on the first mixture to obtain a lubricating oil modification additive.

[0033] The preparation method uses expanded graphite as a raw material, and the expanded graphite is subjected to fluorination treatment; then mixed with permanent magnetic material particles and post-treated; the preparation method is simple and convenient to operate, does not require complicated equipment, and is favorable for wide application.

[0034] Specifically, in the above step S01, expanded graphite is provided, and the preparation method of expanded graphite includes: using graphite as a raw materia...

Embodiment 1

[0061]A kind of lubricating oil modification auxiliary agent and preparation method thereof

[0062] The lubricating oil modification aid includes fluorinated expanded graphite as a support, and permanent magnetic material particles adsorbed on the surface of the support. The lubricating oil modification aid is worm-like; wherein, the permanent magnetic material particles are selected from ferric oxide particles, And the mass ratio of the fluorinated expanded graphite support to the ferric oxide particles is 5:1; the particle size of the ferric oxide particles is 400 mesh.

[0063] The preparation method of lubricating oil modification auxiliary agent:

[0064] Provides N at a volume ratio of 3:1 2 and F 2 In a mixed atmosphere, the expanded graphite was reacted at 300°C for 12 hours for fluorination treatment to obtain fluorinated expanded graphite;

[0065] Mix fluorinated expanded graphite and iron ferric oxide particles to obtain the first mixture, provide grinding ball...

Embodiment 2

[0068] A kind of lubricating oil modification auxiliary agent and preparation method thereof

[0069] The lubricating oil modification aid includes fluorinated expanded graphite as a support, and permanent magnetic material particles adsorbed on the surface of the support. The lubricating oil modification aid is worm-like; wherein, the permanent magnetic material particles are selected from ferric oxide particles, And the mass ratio of the fluorinated expanded graphite support to the ferric oxide particles is 6:1; the particle size of the ferric oxide particles is 500 mesh.

[0070] The preparation method of lubricating oil modification auxiliary agent:

[0071] Provides N at a volume ratio of 3:1 2 and F 2 In a mixed atmosphere, the expanded graphite was reacted at 400°C for 12 hours for fluorination treatment to obtain fluorinated expanded graphite;

[0072] Mix fluorinated expanded graphite with ferric oxide particles to obtain the first mixture, provide grinding balls t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention provides a lubricating oil modifying aid. The lubricating oil modifying aid comprises fluorinated expanded graphite as a supporter and permanent magnet material particles adsorbed on thesurface of the supporter, and the lubricating oil modifying aid is worm-shaped. The lubricating oil modifying aid is low in friction coefficient, good in lubricating effect and high in adsorption capacity, modification treatment of lubricating oil is facilitated, the lubricating performance of lubricating oil under the low-temperature condition is improved, and therefore the problem of resonancesqueal caused by starting impact at the low temperature and the normal temperature is completely eradicated.

Description

technical field [0001] The application belongs to the technical field of lubricating oil, and in particular relates to a lubricating oil modification aid, a preparation method thereof, and a modified lubricating oil. Background technique [0002] As far as the current automobile industry is concerned, the supporting small motors such as the electronic parking system (EPB) generally adopt the design of powder metallurgy bearings at the non-torque output end. Powder metallurgy bearing is a kind of porous material. The load and speed of small motors in automobiles determine that it is mostly Cu-Zn system. It can use capillary action to suck lubricating oil under vacuum conditions, and then pump and Thermal expansion is released to form a lubricating film. Based on safety considerations, perfluoropolyether, which has stable chemical properties and superior comprehensive lubricating properties, is currently used as the lubricating oil for powder metallurgy bearings in the mainst...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M125/00C10M177/00C10N30/06C10N30/08C10N40/02
CPCC10M125/00C10M177/00C10M2201/042C10M2201/062C10M2213/0606Y02T10/86
Inventor 何亮谢盛辉刘栋材肖春林廖相
Owner CHIAPHUA COMPONENTS SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap