Concrete crack repairing technology based on microorganisms

A technology of concrete and microorganisms, applied in the field of concrete crack repair based on microorganisms, can solve the problems of low repair efficiency and quality, achieve the effect of improving efficiency and quality, and ensuring work efficiency

Inactive Publication Date: 2020-10-27
TIANJIN XINBIN ENG TECH INSPECTION
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a microbial-based concrete crack repair technology, which has the advantages of high repair efficiency and high quality, and solves the problems of low repair efficiency and quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A technology for repairing concrete cracks based on microorganisms, comprising the following raw materials in parts by weight: 15 parts of calcium carbonate, 5 parts of Bacillus sphaericus, 5 parts of Bacillus lentus, 15 parts of calcium lactate, 3 parts of peptone, glutamate 5 parts, 10 parts of spore powder, 80 parts of oxygen release agent, 6 parts of nutrients and 3 parts of acid-base regulator.

[0023] A technology for repairing concrete cracks based on microorganisms, comprising the following steps:

[0024] 1) Pulverizing and grinding corresponding parts of calcium carbonate, bacillus sphaericus, bacillus lentus, calcium lactate, peptone, glutamate, spore powder, oxygen release agent, nutrients and acid-base regulator;

[0025] 2) The ground mixed material is fully mixed by a mixer to obtain a uniform mixed material;

[0026] 3) The homogeneous mixed material is processed by a tablet press, and the mixed powder is added each time it is punched to make particles...

Embodiment 2

[0029] A technology for repairing concrete cracks based on microorganisms, comprising the following raw materials in parts by weight: 20 parts of calcium carbonate, 8 parts of Bacillus sphaericus, 8 parts of Bacillus lentus, 20 parts of calcium lactate, 6 parts of peptone, glutamate 9 parts, 15 parts of spore powder, 110 parts of oxygen release agent, 12 parts of nutrients and 6 parts of acid-base regulator.

[0030] A technology for repairing concrete cracks based on microorganisms, comprising the following steps:

[0031] 1) Pulverizing and grinding corresponding parts of calcium carbonate, bacillus sphaericus, bacillus lentus, calcium lactate, peptone, glutamate, spore powder, oxygen release agent, nutrients and acid-base regulator;

[0032] 2) The ground mixed material is fully mixed by a mixer to obtain a uniform mixed material;

[0033] 3) The homogeneous mixed material is processed by a tablet press, and the mixed powder is added each time it is punched to make particl...

Embodiment 3

[0036] A technology for repairing concrete cracks based on microorganisms, comprising the following raw materials in parts by weight: 25 parts of calcium carbonate, 10 parts of Bacillus sphaericus, 10 parts of Bacillus lentus, 25 parts of calcium lactate, 9 parts of peptone, glutamate 12 parts, 18 parts of spore powder, 150 parts of oxygen release agent, 18 parts of nutrients and 9 parts of acid-base regulator.

[0037] A technology for repairing concrete cracks based on microorganisms, comprising the following steps:

[0038] 1) Pulverizing and grinding corresponding parts of calcium carbonate, bacillus sphaericus, bacillus lentus, calcium lactate, peptone, glutamate, spore powder, oxygen release agent, nutrients and acid-base regulator;

[0039] 2) The ground mixed material is fully mixed by a mixer to obtain a uniform mixed material;

[0040] 3) The homogeneous mixed material is processed by a tablet press, and the mixed powder is added each time it is punched to make part...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of concrete crack repairing, and further discloses a concrete crack repairing technology based on microorganisms. The technology involves the following rawmaterials by weight: 15-5 parts of calcium carbonate, 5-10 parts of bacillus sphaericus, 5-10 parts of bacillus lentus, 15-25 parts of calcium lactate, 3-9 parts of peptone, 5-12 parts of glutamate,10-18 parts of spore powder, 80-150 parts of an oxygen release agent, 6-18 parts of nutrient substance and 3-9 parts of an acid-base regulator. According to the concrete crack repairing technology based on the microorganisms, calcium carbonate deposition is driven through urea metabolism of bacillus sphaericus and bacillus lentus, and then calcium carbonate is rapidly catalyzed by the microorganisms for precipitation, so that the effect of improving the concrete crack repairing efficiency and quality is achieved.

Description

technical field [0001] The invention relates to the technical field of concrete crack repair, in particular to a microorganism-based concrete crack repair technology. Background technique [0002] Concrete is referred to as concrete for short, which refers to the general designation of engineering composite materials that aggregate aggregates into a whole by cementitious materials. The term concrete usually refers to the use of cement as cementitious material, sand and stone as aggregates, and water ( It can contain admixtures and admixtures) in a certain proportion, and the cement concrete obtained by stirring is also called ordinary concrete, which is widely used in civil engineering. [0003] With the increasing use of concrete, the requirements for concrete repair technology have also increased. However, the existing concrete crack repair agents cannot precipitate calcium carbonate well, resulting in longer calcium carbonate crystal formation time, which greatly It affe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B30/00E04G23/02C12N1/20C12R1/07C04B111/72
CPCC04B30/00C04B2111/72C12N1/20E04G23/0203C04B14/28C04B2103/0001C04B24/14C04B24/06C04B24/123C04B2103/0068C04B2103/0094
Inventor 杨兴亮郭少敏裴俊萍范建刚裴丽梅刘倩玉
Owner TIANJIN XINBIN ENG TECH INSPECTION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap