Wire harness protector and wire harness

A wire harness protection and modification technology, which is applied in the field of pressure-sensitive adhesives to achieve the effects of improving the stability of use, increasing the strength, and enhancing protection

Inactive Publication Date: 2020-11-06
上海元一电子有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still some shortcomings in its mechanical properties in actual use, which need to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wire harness protector and wire harness
  • Wire harness protector and wire harness

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] The preparation method of described modified polylactic acid fiber comprises the steps:

[0029] (1) Rinse the kaolin once with deionized water, then put it into the calciner for calcining, and take it out for subsequent use after completion;

[0030] (2) Immerse the kaolin treated in step (1) into the silane coupling agent solution, and filter out after 30-35 minutes for later use;

[0031] (3) The kaolin, nano-silver, and polylactic acid slices processed in step (2) are mixed together, firstly mixed, and taken out after 50 to 55 minutes to obtain the mixed material for subsequent use;

[0032] (4) Put the compounded material obtained in step (3) into a twin-screw extruder for extrusion processing, and then carry out spinning processing after completion, and finally go through cooling, drawing, and cutting.

[0033] During the calcination treatment described in step (1), the temperature in the calcination furnace is controlled to be 800-850° C., and the treatment time...

Embodiment 1

[0043] A wire harness protector, specifically, a non-woven fabric composed of mixed fibers containing polypropylene resin fibers, modified polylactic acid fibers, and modified basalt fibers is formed into a predetermined shape.

[0044] The corresponding weight fractions of the polypropylene resin fiber, modified polylactic acid fiber and modified basalt fiber in the non-woven fabric are 55%, 30% and 15% respectively.

[0045] The preparation method of described modified polylactic acid fiber comprises the steps:

[0046] (1) Rinse the kaolin once with deionized water, then put it into the calciner for calcining, and take it out for subsequent use after completion;

[0047] (2) Immerse the kaolin treated in step (1) in the silane coupling agent solution, and filter out after 30 minutes for subsequent use;

[0048] (3) The kaolin, nano-silver, and polylactic acid slices processed in step (2) are mixed together, and the mixing process is carried out first, and the mixing materi...

Embodiment 2

[0060] A wire harness protector, specifically, a non-woven fabric composed of mixed fibers containing polypropylene resin fibers, modified polylactic acid fibers, and modified basalt fibers is formed into a predetermined shape.

[0061] The corresponding weight fractions of the polypropylene resin fiber, modified polylactic acid fiber and modified basalt fiber in the non-woven fabric are 58%, 32% and 10% respectively.

[0062] The preparation method of described modified polylactic acid fiber comprises the steps:

[0063] (1) Rinse the kaolin once with deionized water, then put it into the calciner for calcining, and take it out for subsequent use after completion;

[0064] (2) Immerse the kaolin treated in step (1) in the silane coupling agent solution, and filter out after 31 minutes for subsequent use;

[0065] (3) The kaolin, nano-silver, and polylactic acid slices processed in step (2) are mixed together, and the mixing process is carried out first, and the mixing materi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wire harness protection piece, which belongs to the technical field of pressure-sensitive adhesives. The wire harness protection piece is particularly is formed by forming non-woven fabric composed of mixed fibers containing polypropylene resin fibers, modified polylactic acid fibers and modified basalt fibers into a preset shape. According to the invention, the componentcomposition of the wire harness protection piece is changed; the polypropylene resin fibers, the modified polylactic acid fibers and the modified basalt fibers are mixed to prepare the non-woven fabric, the use quality of the wire harness protection piece is effectively improved, the polypropylene resin fibers serve as a main body, the cost is reduced, the two kinds of modified fibers are added,and the overall strength, weather resistance and temperature resistance are improved; after the three fibers are mixed and woven into the non-woven fabric, the overall mechanical quality, the use stability and the like of the non-woven fabric are remarkably improved, and the protection on the wire harness is effectively enhanced.

Description

technical field [0001] The invention belongs to the technical field of pressure-sensitive adhesives, and in particular relates to a conductive pressure-sensitive adhesive and a preparation method thereof. Background technique [0002] In recent years, high performance and high functionality have been developed centering on motor vehicles and electrical products. In order for various electronic devices such as automobiles and electric products to operate accurately, multiple electric wires are used for internal wiring of automobiles and electric products. Generally, these multiple wires are used in a wire harness. [0003] In the wire harness, a wire bundle composed of a plurality of electric wires is pre-assembled into a form required for wiring. For example, a wire harness is formed by forming necessary branches and attaching connectors to the ends thereof, and then wrapping a wire harness protector in various shapes such as a belt, a tube, or a sheet around the outer per...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B60R16/02D01F6/92D01F1/10D01F9/08C03C13/06C03B37/06C03B5/16C03C25/626D04H1/4382D04H1/4291D04H1/435D04H1/4209
CPCB60R16/0215C03B5/16C03B37/06C03C13/06C03C25/626D01F1/10D01F6/92D01F9/08D04H1/4209D04H1/4291D04H1/435D04H1/4382
Inventor 沈军
Owner 上海元一电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More