Plasticizer composition, and resin composition comprising same
A resin composition and composition technology, applied in the field of plasticizer composition and resin composition containing the plasticizer composition, to achieve the effects of high stability, excellent basic performance and excellent performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation Embodiment 1
[0142] Preparation Example 1: Diisononylcyclohexane-1,2-diester
[0143] Into a 3 L four-neck reaction vessel equipped with a cooler, condenser, decanter, reflux pump, temperature controller, stirrer, etc., were added 516.5 g of cyclohexane-1,2-dicarboxylic acid, 1,296 g of iso nonanol and 1.55 g of tetraisopropyl titanate as a catalyst, and the temperature of the reaction vessel was set at 230°C. Then, direct esterification was performed for about 6 hours while continuously introducing nitrogen gas, and was terminated when the acid value reached 0.1.
[0144] After the reaction, vacuum distillation and extraction were performed to remove unreacted raw materials. Thereafter, neutralization, dehydration, and filtration processes were performed to prepare 1,240 g of diisononyl cyclohexane-1,2-dicarboxylate (DINCH) (yield: 97%).
preparation Embodiment 2
[0145] Preparation Example 2: Bis(2-propylheptyl)cyclohexane-1,2-diester
[0146] 1,320 g (yield: 97 %) of bis(2-propylheptyl)cyclohexane-1,2-dicarboxylate (DPHpCH).
preparation Embodiment 3
[0147] Preparation Example 3: Tri(n-butyl) citrate
[0148] Except adding 384.2 g of citric anhydride and 670 g of n-butanol in the reaction vessel, 700 g (yield: 97%) of tri(n-butyl) citrate ( TnBC).
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com