Door and window sealing water-blocking material
A water-blocking, door and window technology, applied in the field of water-blocking materials, can solve problems such as weak crack resistance and oxidation resistance, damage to water-blocking materials, shortening the service life of water-blocking materials, etc., and achieve good crack resistance and oxidation resistance , reduce the probability of damage, and improve the effect of water isolation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] The door and window sealing water-blocking material includes the following raw materials and their weight fractions: 45 parts by mass of butyl rubber; 20 parts by mass of epoxy resin; 25 parts by mass of polyethylene glue; and 2% by mass of antistatic agent; The antioxidant is 3% by mass; the cross-linking agent is 5% by mass.
[0034] The preparation steps are as follows:
[0035] a. Weigh the above-mentioned raw materials according to parts by weight;
[0036] b. After step a is completed, mix the butyl rubber, epoxy resin and polyethylene glue in an internal mixer for mixing to obtain a mixed rubber. The mixing temperature is 100-130°C, and the mixing time is 10- 15min, after mixing, place it in an open mill for heat dissipation;
[0037] c. After step b is completed, add calcium chloride, sodium carbonate, sodium dodecyl sulfate and polyacrylamide into the mixer, and then add an appropriate amount of water to the mixer for mixing, and the rotating speed during mix...
Embodiment 2
[0041] The door and window sealing water-blocking material includes the following raw materials and their weight fractions: 35 parts by mass of butyl rubber; 15 parts by mass of epoxy resin; 20 parts by mass of polyethylene glue; 5 parts by mass of calcium chloride; Sodium is 3 parts by mass; sodium lauryl sulfate is 2 parts by mass; polyacrylamide is 4% by mass; antistatic agent is 2% by mass; antioxidant is 3% by mass; softener is 6% by mass ; The crosslinking agent is 5% by mass.
[0042] The preparation steps are as follows:
[0043] a. Weigh the above-mentioned raw materials according to parts by weight;
[0044] b. After step a is completed, mix the butyl rubber, epoxy resin and polyethylene glue in an internal mixer for mixing to obtain a mixed rubber. The mixing temperature is 100-130°C, and the mixing time is 10- 15min, after mixing, place it in an open mill for heat dissipation;
[0045] c. After step b is completed, add calcium chloride, sodium carbonate, sodium ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap