Wall putty material as well as preparation method and use method thereof

A putty, wall technology, applied in the direction of filling slurry, etc., can solve the problems of low surface tension and strong permeability

Active Publication Date: 2020-12-18
GUANGDONG BOZHILIN ROBOT CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Based on this, the present invention provides a wall putty material, which is suitable for mechanical spraying, has low surface tension, strong penetrating ability, high leveling, good appearance effect, and improves poor construction defects on rough and dry wall surfaces, dry Wall construction is free of pre-treatment such as water spray and interface agent, and the bonding strength and construction are convenient and efficient.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wall putty material as well as preparation method and use method thereof
  • Wall putty material as well as preparation method and use method thereof
  • Wall putty material as well as preparation method and use method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0080] A preparation method of wall putty material, comprising the following steps: mixing base material, calcium carbonate whisker, polyethylene glycol and filler to obtain component A;

[0081] Get fumed silica to obtain component B;

[0082] The parts by weight of the base material are 3 parts-31 parts; the parts by weight of the calcium carbonate whiskers are 3 parts-7 parts; the parts by weight of polyethylene glycol are 0.5 parts-1 part; the parts by weight of the filler It is 30-60 parts; the weight part of fumed silica is 15-25 parts.

[0083] A method for using a wall putty material, comprising the following steps:

[0084] Mix component B and water, stir for the first time, add component A, stir for the second time, let it stand, stir for the third time.

[0085] The purpose of the first stirring and the second stirring is to mix the raw materials evenly, and high-speed stirring can be used, preferably the stirring speed is 1200r / min-1500r / min. This will generate ...

Embodiment 1

[0098] This embodiment provides a wall putty material and its preparation method and use method, the steps are as follows:

[0099] In parts by weight, weigh 3.5 parts of polymer latex powder, 25 parts of white cement, 50 parts of heavy calcium, 15 parts of fumed silica, 3 parts of calcium carbonate whiskers, 0.5 parts of polyethylene glycol, 0.5 parts of hydroxypropyl Methyl cellulose ether, 0.5 part of defoamer, 1 part of water repellent, 0.5 part of modified hydroxypropyl starch ether, 0.5 part of antifungal agent.

[0100] Preparation method: polymer latex powder, white cement, heavy calcium, calcium carbonate whiskers, polyethylene glycol, hydroxypropyl methylcellulose ether, defoamer, water repellent, modified hydroxypropyl starch ether, The antifungal agent is poured into the mixing equipment, mixed evenly, weighed and packaged to obtain component A; the fumed silica is weighed and packaged separately to obtain component B.

[0101] How to use: Mix component B and 40 p...

Embodiment 2

[0103] This embodiment provides a wall putty material and its preparation method and use method, which are basically the same as in Embodiment 1, the only difference being that the weight parts of heavy calcium and calcium carbonate whiskers are different, and the steps are as follows:

[0104] In parts by weight, weigh 3.5 parts of polymer latex powder, 25 parts of white cement, 48 parts of heavy calcium, 15 parts of fumed silica, 5 parts of calcium carbonate whiskers, 0.5 parts of polyethylene glycol, 0.5 parts of hydroxypropyl Methyl cellulose ether, 0.5 part of defoamer, 1 part of water repellent, 0.5 part of modified hydroxypropyl starch ether, 0.5 part of antifungal agent.

[0105] Preparation method: polymer latex powder, white cement, heavy calcium, calcium carbonate whiskers, polyethylene glycol, hydroxypropyl methylcellulose ether, defoamer, water repellent, modified hydroxypropyl starch ether, The antifungal agent is poured into the mixing equipment, mixed evenly, w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a wall putty material as well as a preparation method and a use method thereof. The wall putty material comprises a component A and a component B, wherein the component A is prepared from the following raw materials in parts by weight: 3 parts of a base material, 3-7 parts of calcium carbonate whisker, 0.5-1 part of polyethylene glycol, 30-60 parts of a filler, 0.1-1 partof modified hydroxypropyl starch ether; and the component B is prepared from the following raw materials in parts by weight: 15-25 parts of fumed silica. The wall putty material is suitable for mechanical spraying, low in surface tension, high in infiltration capacity, high in leveling property, good in apparent effect, capable of overcoming the defects of poor construction on rough and dry wall surfaces, free of pretreatment such as water spraying and interface agents in dry wall construction, high in bonding strength, convenient and fast to construct and high in efficiency.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a wall putty material and a preparation method and application method thereof. Background technique [0002] Existing building walls often have a low moisture content, the base material of the wall is too rough, and there are many small holes in the gaps of the wall, and air bubbles will often be generated if the plastering is too fast and the construction is too thick. In view of these situations, the existing construction technology generally adopts the first construction of thick putty, reducing the speed and thickness of plastering, or first wetting the wall with water, and then scraping after there is no clear water. This kind of process often brings other uncertain factors, such as inconsistent putty before and after, easy to mix up, resulting in the performance of the putty can not be guaranteed, and the bond strength is reduced; and such construction efficiency is low, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/34
CPCC09D5/34
Inventor 陈驰辉唐振中彭路希
Owner GUANGDONG BOZHILIN ROBOT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com