Manufacturing method of aluminum alloy formwork for building
A technology of aluminum alloy formwork and manufacturing method, which is applied in the field of building aluminum formwork manufacturing, can solve the problems of high cost, cumbersome aluminum formwork processing technology, and low output, and achieve the effects of improving efficiency, streamlining processing equipment, and reducing processing procedures
Inactive Publication Date: 2020-12-29
SNTO TECH GRP
View PDF8 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0004] In order to solve the technical problems of cumbersome aluminum formwork processing technology, high cost and low yield, the invention provides a method for manufacturing aluminum alloy formwork for construction, which includes the following steps:
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0034] The present invention will be further described below in conjunction with the accompanying drawings and embodiments.
[0035] A method for manufacturing an aluminum alloy formwork for construction, comprising the steps of:
[0036] S1, casting, splitting the aluminum alloy formwork for construction to be manufactured into two or more parts according to the principle of facilitating casting, and casting each part separately to form multiple castings;
[0037] S2, welding, according to the shape of the aluminum alloy formwork for construction that needs to be manufactured, welding the multiple castings in step S1 to form an integral weldment;
[0038] S3, fine polishing, the integral weldment in step S2 is finely polished to form a shot blasted part, the working surface of the shot blasted part is free of cement, oil stains, oxide layers, and rust spots, and the surface roughness of the template meets the design requirements, without scratches The depth does not exceed 0...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention belongs to the technical field of building aluminum formwork manufacturing, and discloses a manufacturing method of an aluminum alloy formwork for building. The manufacturing method comprises the following steps that S1, conducting casting, wherein the needed aluminum alloy formwork for building is divided into two or more components according to the principle beneficial to casting parting, each component is independently cast, and a plurality of castings are formed; S2, conducting welding, wherein the multiple castings in the step S1 are welded according to the shape of the needed aluminum alloy formwork for building, and an integral welded piece is formed; and S3, conducting fine polishing, wherein the integral welded piece in the step S2 is subjected to fine polishing treatment to form a shot-blasted piece, the working face of the shot-blasted piece is free of cement, oil stains, oxidation layers and rust spots, the surface roughness of the formwork meets the design requirement, and the scratching depth does not exceed 0.5 mm. Compared with the relevant technique, the manufacturing method adopts the casting manner to form the formwork, so that the number of machining procedures is reduced, and meanwhile machining equipment is simplified; and beneficially, the efficiency is improved, and the cost is reduced.
Description
technical field [0001] The invention belongs to the technical field of building aluminum formwork manufacturing, and discloses a manufacturing method of an aluminum alloy formwork for building. Background technique [0002] At present, building aluminum alloy formwork is widely used, and in related technologies, the processing route of aluminum formwork is long, specifically: after aluminum water smelting and casting into aluminum rods, extrusion into profiles, and then through sawing, stamping, milling, welding , fine polishing, spraying and other processes. There are many types of equipment needed in these processes, and the cost is high, and each type of equipment completes a process independently, and the processing efficiency is slow. On the other hand, the processing technology is cumbersome and the quality is unstable. [0003] Therefore, it is necessary to provide a new manufacturing method of aluminum alloy formwork for construction to solve the above technical pr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00
CPCB23P15/00
Inventor 李冰刘正宏袁潇
Owner SNTO TECH GRP