A preparation method of polyimide/polytetrafluoroethylene composite film for wire and cable insulation
A technology of polytetrafluoroethylene and polyimide, applied in the direction of conductor/cable insulation, insulator, circuit, etc., can solve the problems of high cost, complicated process, inability to accurately control the amount of production process, etc., to reduce the contact angle , Increase the effect of hydrophilicity
Active Publication Date: 2021-06-11
扬泰氟(清远)电线电缆有限公司
View PDF0 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] At present, there are some preparation methods of polyimide / polytetrafluoroethylene composite film for cable and wire insulation, but the process is complicated, the cost is high, and the amount used in the production process cannot be accurately controlled, resulting in low comprehensive performance.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0039] In order to make the objects and advantages of the present invention clearer, the present invention will be further described below in conjunction with the examples; it should be understood that the specific examples described here are only for explaining the present invention, and are not intended to limit the present invention.
[0040] Preferred embodiments of the present invention are described below with reference to the accompanying drawings. Those skilled in the art should understand that these embodiments are only used to explain the technical principle of the present invention, and are not intended to limit the protection scope of the present invention.
[0041] It should be noted that, in the description of the present invention, terms such as "upper", "lower", "left", "right", "inner", "outer" and other indicated directions or positional relationships are based on the terms shown in the accompanying drawings. The direction or positional relationship shown is ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to a preparation method of a polyimide / polytetrafluoroethylene composite film for wire and cable insulation, comprising: obtaining a polytetrafluoroethylene solution and a polyimide solution; Tetrafluoroethylene solution, the first feeding port adds surfactant into the reactor, stirs to form a hydrophilic polytetrafluoroethylene solution; the casting film forming equipment casts the hydrophilic polytetrafluoroethylene solution into a film to obtain a hydrophilic polytetrafluoroethylene solution. Polytetrafluoroethylene film; the first application device applies adhesive on both sides of the hydrophilic polytetrafluoroethylene film to form a sticky hydrophilic polytetrafluoroethylene film; the second coating device applies the polyimide solution on both sides of the sticky hydrophilic polytetrafluoroethylene film, dried, and then put into a soaking tank for soaking, the second feeding port adds the first remover to the soaking tank, filters, and dries. Therefore, the insulation performance of the polyimide / polytetrafluoroethylene composite film for wire and cable insulation can be effectively improved, and the process is simple and the cost is saved.
Description
technical field [0001] The invention relates to the field of preparation methods of plastic films, in particular to a preparation method of a polyimide / polytetrafluoroethylene composite film for wire and cable insulation. Background technique [0002] Polyimide (PI) is a material with excellent comprehensive properties. It is a kind of polymer material containing imide rings in the main chain. It has excellent heat resistance, low temperature resistance, solvent resistance, and self-lubricating properties. Properties such as resistance and flame retardancy. Polytetrafluoroethylene (PTFE) is a white waxy thermoplastic. The composition and structure of PTFE determine that it has the following characteristics: a wide range of high and low temperature applications, excellent corrosion resistance, excellent weather resistance, high insulation, high Lubricity, excellent surface non-stickiness, minimal water absorption, excellent thermal stability, non-toxic, and physiologically i...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): H01B19/00H01B19/02H01B19/04H01B13/06
CPCH01B13/06H01B19/00H01B19/02H01B19/04
Inventor 黄平钦
Owner 扬泰氟(清远)电线电缆有限公司