Preparation method of microcrystalline glass resistance paste

A technology of resistance paste and glass ceramics, which is applied in the direction of cable/conductor manufacturing, conductive materials dispersed in non-conductive inorganic materials, circuits, etc., can solve the problems of high preparation cost, many precious raw materials, and slow promotion speed. Achieve the effect of reducing production cost, reducing usage, and improving market competitiveness

Inactive Publication Date: 2021-03-05
TAIYANG ELECTRONICS DONGGUAN
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Resistance paste, also known as electronic paste, is the basic material for the manufacture of thick film components. It is a paste made of solid powder and organic solvents that are uniformly mixed by three-roll rolling. According to the application, it can be divided into medium paste and resistance paste. Material and conductive paste: according to the type of substrate, it can be divided into ceramic substrate, polymer substrate, glass substrate and metal insulating substrate electronic paste, etc.; according to the sintering temperature, it can be divided into high temperature, medium and low temperature drying electronic paste According to the purpose, it can be divided into general electronic paste (making general thick film circuit) and special electronic paste (stainless steel substrate electronic paste, thermistor paste); according to the price of the conductive phase, it can be divided into precious metal electronic paste materials (silver-palladium, ruthenium and gold paste, etc.) and base metal electronic paste (molybdenum-manganese paste), but the existing resistance paste uses more expensive raw materials, which leads to high preparation costs and reduces its promotion. Speed, for this reason, we propose a glass-ceramic resistance paste preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for preparing a glass-ceramic resistance paste, the method comprising the following steps:

[0024] A. Material selection: select the required raw materials;

[0025] B. Drying: Put each raw material into a drying box for drying treatment;

[0026] C. Impurity removal: put each raw material into the impurity removal box for impurity removal treatment;

[0027] D, pulverization: put each raw material into pulverizer respectively and carry out pulverization treatment, and pulverization order number is 40 orders;

[0028] E. Grinding: Put the pulverized raw materials into a grinder for grinding, and the grinding mesh is 100 mesh;

[0029] F, mixing: put each raw material after grinding into the stirring dish according to parts by weight and carry out stirring process;

[0030] G. Binding and forming: put the mixed slurry into the three-roll rolling machine for binding;

[0031] H. Performance test: test the viscosity, rheology, silver content and thermal deter...

Embodiment 2

[0040] A method for preparing a glass-ceramic resistance paste, the method comprising the following steps:

[0041] A. Material selection: select the required raw materials;

[0042] B. Drying: Put each raw material into a drying box for drying treatment;

[0043] C. Impurity removal: put each raw material into the impurity removal box for impurity removal treatment;

[0044] D, pulverization: put each raw material into the pulverizer respectively and carry out pulverization treatment, and the pulverization mesh number is 80 mesh;

[0045] E. Grinding: Put the pulverized raw materials into a grinder for grinding, and the grinding mesh is 150 mesh;

[0046] F, mixing: put each raw material after grinding into the stirring dish according to parts by weight and carry out stirring process;

[0047] G. Binding and forming: put the mixed slurry into the three-roll rolling machine for binding;

[0048] H. Performance test: test the viscosity, rheology, silver content and thermal ...

Embodiment 3

[0057] A method for preparing a glass-ceramic resistance paste, the method comprising the following steps:

[0058] A. Material selection: select the required raw materials;

[0059] B. Drying: Put each raw material into a drying box for drying treatment;

[0060] C. Impurity removal: put each raw material into the impurity removal box for impurity removal treatment;

[0061] D, pulverization: put each raw material into pulverizer respectively and carry out pulverization treatment, and pulverization mesh number is 100 mesh;

[0062] E. Grinding: Put the pulverized raw materials into a grinder for grinding, and the grinding mesh is 200 mesh;

[0063] F, mixing: put each raw material after grinding into the stirring dish according to parts by weight and carry out stirring process;

[0064] G. Binding and forming: put the mixed slurry into the three-roll rolling machine for binding;

[0065] H. Performance test: test the viscosity, rheology, silver content and thermal deterio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of microcrystalline glass resistance paste. The method comprises the following steps: A, material selecting: selecting required raw materials; B, drying: respectively putting the raw materials into a drying box for drying treatment; C, impurity removal: respectively putting the raw materials into an impurity removal box for impurity removal treatment; D, crushing: respectively putting the raw materials into a crusher for crushing treatment, wherein the crushing mesh number is 40100 meshes; e, grinding: putting the smashed raw materials into a grinding machine to be ground, wherein the grinding mesh number is 100-200; F, mixing: putting the ground raw materials into a stirring vessel in parts by weight, and stirring. By adding the compound resin,graphene, metal powder and other raw materials, the use amount of precious raw materials can be reduced, thereby lowering the production cost, enhancing the viscosity and heat resistance and loweringthe rheological property on the existing basis, effectively enhancing the market competitiveness of the product, and conforming to the benefits of the enterprise.

Description

technical field [0001] The invention relates to the technical field of resistance paste, in particular to a method for preparing a glass-ceramic resistance paste. Background technique [0002] Resistance paste, also known as electronic paste, is the basic material for the manufacture of thick film components. It is a paste made of solid powder and organic solvents that are uniformly mixed by three-roll rolling. According to the application, it can be divided into medium paste and resistance paste. Material and conductive paste: according to the type of substrate, it can be divided into ceramic substrate, polymer substrate, glass substrate and metal insulating substrate electronic paste, etc.; according to the sintering temperature, it can be divided into high temperature, medium and low temperature drying electronic paste According to the purpose, it can be divided into general electronic paste (making general thick film circuit) and special electronic paste (stainless steel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B1/22H01B13/00
CPCH01B1/22H01B13/00
Inventor 刘应华陈凯罗国强谢化东
Owner TAIYANG ELECTRONICS DONGGUAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap