Novel glass handicraft processing technology

A processing technology and handicraft technology, applied in the field of glass handicraft processing technology, can solve problems such as affecting the quality of glass handicrafts, and achieve the effects of avoiding air bubbles, reducing defective product rate and high heating efficiency

Inactive Publication Date: 2021-04-09
安徽加隆工艺品股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the production and manufacture of glass handicrafts, since the glass needs to be made in a molten state, and a large amount of gas will be generated when it is sintered, bubbles may be generated inside the glass during the formation of the glass during the sintering process, which will affect The quality of the whole glass crafts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel glass handicraft processing technology
  • Novel glass handicraft processing technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A novel glass handicraft processing technology, comprising the steps of:

[0021] (1) The production and proportioning of raw materials, the main materials such as soda ash, limestone and quartz are fully mixed, and the proportion of the three main materials is 1:2:1, and these mixed materials are crushed by crushing equipment, such as jaw type The crusher crushes the raw materials. After the raw materials are crushed, all the wet raw materials are dried by the drying equipment to form a glass batch. The vacuum dryer can be used to dry the materials. When batching, it is necessary to measure the uniformity of each raw material ;

[0022] (2) The glass batch material is melted, and the glass batch material obtained in step (1) is put into a pool kiln or a crucible kiln for high-temperature heating to form a uniform, bubble-free liquid glass that meets the molding requirements. Carry out two vacuum treatments in the process of vacuum treatment, and vacuum pump can be use...

Embodiment 2

[0031] A novel glass handicraft processing technology, comprising the steps of:

[0032] (1) The production and proportioning of raw materials, the main materials such as soda ash, limestone and quartz are fully mixed, the proportion of the three main materials is 2:4:2, and these mixed materials are crushed by crushing equipment, such as jaw type The crusher crushes the raw materials. After the raw materials are crushed, all the wet raw materials are dried by the drying equipment to form a glass batch. The vacuum dryer can be used to dry the materials. When batching, it is necessary to measure the uniformity of each raw material ;

[0033] (2) The glass batch material is melted, and the glass batch material obtained in step (1) is put into a pool kiln or a crucible kiln for high-temperature heating to form a uniform, bubble-free liquid glass that meets the molding requirements. Carry out two vacuum treatments in the process of vacuum treatment, and vacuum pump can be used fo...

Embodiment 3

[0041] A novel glass handicraft processing technology, comprising the steps of:

[0042] (1) The production and proportioning of raw materials, the main materials such as soda ash, limestone and quartz are fully mixed, the proportion of the three main materials is 2:4:2, and these mixed materials are crushed by crushing equipment, such as jaw type The crusher crushes the raw materials. After the raw materials are crushed, all the wet raw materials are dried by the drying equipment to form a glass batch. The vacuum dryer can be used to dry the materials. When batching, it is necessary to measure the uniformity of each raw material ;

[0043] (2) The glass batch material is melted, and the glass batch material obtained in step (1) is put into a tank kiln for high-temperature heating to form a uniform, bubble-free liquid glass that meets the molding requirements. During the firing process Carry out two vacuum treatments. During the vacuum treatment, a vacuum pump can be used for t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel glass handicraft processing technology, which comprises the following steps: crushing block raw materials, drying wet raw materials, and carrying out iron removal treatment on iron-containing raw materials to ensure the quality of glass; adding agents such as a catalyst into the treated materials to form a glass batch; carrying out high-temperature heating on the glass batch in a tank furnace or a crucible furnace to form uniform and bubble-free liquid glass meeting the molding requirement, and carrying out vacuum treatment twice in the firing process; processing the liquid glass into products with required shapes, such as flat plates, various utensils and the like; subjecting the formed glass products to annealing, quenching and other processes to eliminate or produce stress, phase splitting or crystallization in the glass, and change the structural state of the glass; and packaging the annealed products and delivering the products out of a factory. According to the glass handicraft processing technology, two vacuum processing procedures are added, the quality of the whole glass product is improved, and the defective product rate of the whole glass product is reduced.

Description

technical field [0001] The invention relates to a processing flow technology, in particular to a novel glass handicraft processing technology, which belongs to the technical field of glass handicraft processing technology. Background technique [0002] Glass is formed by melting silicon dioxide and other chemical substances together, forming a continuous network structure during melting, and a silicate non-metallic material whose viscosity gradually increases and hardens during cooling to cause it to crystallize. Glass is a texture A very beautiful material with high plasticity in the molten state, so glass is often used in the production of handicrafts. Due to the high quality of glass craftsmanship and various shapes, it is more and more sought after by people, so glass handicrafts are gradually becoming popular in ordinary families. It appears that some glass handicrafts are more expensive due to their own factors. [0003] In the production and manufacture of glass hand...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/04C03B1/00C03B5/235C03B9/00C03B5/18C03B5/16
CPCC03B1/00C03B5/16C03B5/18C03B5/235C03B9/00C03C1/00
Inventor 袁磊
Owner 安徽加隆工艺品股份有限公司