Insulating coating composition for electrical steel sheet, and electrical steel sheet comprising insulating coating

A technology for electrical steel sheets and insulating coatings, applied to inorganic insulators, metal oxides, metal material coating processes, etc., can solve problems such as dust generation, heat resistance deterioration, surface whitening defects, etc., and achieve good efficiency effects

Active Publication Date: 2021-04-30
浦项股份有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the characteristics of phosphate with strong absorption resistance, this method has the problem of dust generation during product processing due to whitening defects on the surface, and there is a problem that heat resistance deteriorates on the part where whitening defects occur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Insulating coating composition for electrical steel sheet, and electrical steel sheet comprising insulating coating
  • Insulating coating composition for electrical steel sheet, and electrical steel sheet comprising insulating coating
  • Insulating coating composition for electrical steel sheet, and electrical steel sheet comprising insulating coating

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1-1

[0220] Experimental Example 1-1: According to the characteristics of the type of silane compound

Embodiment 1-1

[0222] Prepare a slab containing silicon (Si): 3.4% by weight, aluminum (Al): 0.80% by weight, manganese (Mn): 0.17% by weight, titanium (Ti): 0.0015% by weight, tin (Sn): 0.03 % by weight, nickel (Ni): 0.01% by weight, carbon (C): 0.003% by weight, nitrogen (N): 0.0013% by weight, phosphorus (P): 0.012% by weight, sulfur (S): 0.001% by weight, balance Composed of Fe and other unavoidable impurities.

[0223] The slab was heated at 1130° C. and then cold-rolled to a thickness of 2.3 mm to produce a hot-rolled sheet.

[0224] Coil the hot-rolled sheet at 650°C, then cool it in the air, anneal the hot-rolled sheet at 1040°C for 2 minutes, then quickly cool it in water and pickle it, and then cold-roll it to a thickness of 0.35mm. Manufacture of cold rolled sheet.

[0225] The cold-rolled sheet was subjected to final annealing at 1040°C for 50 seconds in a 20% hydrogen, 80% nitrogen atmosphere with the dew point adjusted to produce an annealed steel sheet.

[0226] As an insul...

Embodiment 1-2 to 1-12

[0228] The implementation method was the same as that of Example 1-1, but the contents and types of the silane compound, metal hydroxide and metal nitride in the insulating coating composition were replaced as shown in Table 1 below to form an insulating coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

One embodiment of the present invention comprises: an electrical steel sheet material; and an insulating coating which is on one or both sides of the electrical steel sheet material, wherein the insulating coating comprises a silane compound and a metal hydroxide.

Description

technical field [0001] The invention relates to an insulating coating composition for electrical steel sheets and an electrical steel sheet with insulating coatings. More specifically, the present invention relates to an insulating-coating composition for electrical steel sheets and an electrical steel sheet having an insulating coating, which are excellent in heat resistance and thermal conductivity during stress relief annealing by using a silane compound having a specific chemical structure. Background technique [0002] Insulation coatings of electrical steel sheets used in engines and transformers require not only interlayer resistance but also various characteristics such as convenience in processing and molding, stability in storage and use, and the like. In addition, since electrical steel sheets are used in various ways, various insulating coatings have been developed according to the uses. [0003] For example, when an electrical steel sheet is subjected to punchi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/00C09D7/61C09D7/40B05D7/24B05D7/14B05D3/02C21D8/12C23C22/24
CPCB05D3/02B05D7/24C21D8/12C09D4/00B05D7/14C09D7/40C23C22/24C09D7/61B05D1/28B05D3/0254B05D2202/10C08K3/22C08K5/5419C09D7/63C23C22/20C23C22/26C23C22/50C23C22/74C23C2222/10C23C2222/20C08F230/08C08F130/08H01B3/10
Inventor 权玟锡沈昊敬高炫喆金柄澈崔攇曺金正雨卢泰英
Owner 浦项股份有限公司