Geshi metal glaze with copper red metal texture and processing technology thereof

A technology of metal texture and processing technology, applied in the field of Grignard metallic glaze, can solve the problems of restricting the wide application of glaze, discounting and monotony of decorative embellishment effect of products, and achieve increased added value and market competitiveness, excellent decorative embellishment effect, The effect of considerable economic benefits

Pending Publication Date: 2021-05-18
醴陵市格瑞瓷陶瓷科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Due to the raw material formula and firing process, the application of ordinary metal glazes is not satisfactory in many aspects: or the glaze color is less, monotonous, and lacks the natural change of glaze color and luster, which makes it dull. The decorative embellishment effect of the product is greatly reduced; or the lead and cadmium exceed the standard, which limits the wide applicatio

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Geshi metal glaze with copper red metal texture and processing technology thereof
  • Geshi metal glaze with copper red metal texture and processing technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026]Example 1:

[0027]A Grat metal glaze with copper red metal texture, formulation includes: ultra-white washing, rock silicon fine powder, 120 # melt block, sodium lactose, phosphate, zinc oxide, transmissions and cerium oxide, group The mass content of the division is: 6% of the super white washing, 3% rock silicon fine powder, 23% 120 # melt block, 35% sodium, 16% iron phosphate, 2% oxidation Zinc, 6% of the developing agents and 9% cerium oxide.

[0028]A machining process with a copper red metal texture, including the following steps, steps 1, ingredients; step two, raw material processing; step three, roller furnace processing; step four, residual use;

[0029]In the above steps, in the above steps, the mass content of each component is: 6% over white washing, 3% rock silicon fine powder, 23% 120 # melt block, 35% sodium longstone, 16 % Of the cerium iron oxide, 6% of the zinc oxide, 6% of the chromotherapy, and 9% cerium oxide, and weigh according to the weight of 1%; the stack de...

Example Embodiment

[0039]Example 2:

[0040]A Grat metal glaze with copper red metal texture, formulation includes: ultra-white washing, rock silicon fine powder, 120 # melt block, sodium lactose, phosphate, zinc oxide, transmissions and cerium oxide, group The mass content of the division is: 6% super white washing, 3% rock silicon fine powder, 32% 120 # melt block, 30% sodium longite, 12% iron phosphate, 2% oxidation Zinc, 6% of the developing agents and 9% cerium oxide.

[0041]A machining process with a copper red metal texture, including the following steps, steps 1, ingredients; step two, raw material processing; step three, roller furnace processing; step four, residual use;

[0042]In the above steps, in the above steps, the mass content of each component is: 6% over white washing, 3% rock silicon fine powder, 32% 120 # melt block, 30% sodium longstone, 12 % Of the cerium iron oxide, 6% of the zinc oxide, 6% of the chromotherapy, and 9% cerium oxide, and weigh according to the weight of 1%; the stack d...

Example Embodiment

[0052]Example 3:

[0053]A Grat metal glaze with copper red metal texture, formulation includes: ultra-white washing, rock silicon fine powder, 120 # melt block, sodium lactose, phosphate, zinc oxide, transmissions and cerium oxide, group The mass content of the division is: 6% over white washing, 3% rock silicon fine powder, 28% 120 # melt block, 38% sodium stones, 18% iron phosphate, 2% oxidation Zinc, 6% of the developing agents and 9% cerium oxide.

[0054]A machining process with a copper red metal texture, including the following steps, steps 1, ingredients; step two, raw material processing; step three, roller furnace processing; step four, residual use;

[0055]In the above steps, the mass content of each component is: 6% over white washing, 3% rock silicon fine powder, 28% 120 # melt block, 38% sodium longstone, 18 % Of the cerium iron oxide, 6% of the zinc oxide, 6% of the chromotherapy, and 9% cerium oxide, and weigh according to the weight of 1%; the stack density of iron-contain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Geshi metal glaze with copper red metal texture, which is prepared from the following components: ultra-white washing mud, lithiated silica powder, 120# frit, albite, iron phosphate, zinc oxide, a color developing agent and cerium oxide according to the mass percentage ratio as follows: 4-10% of ultra-white washing mud, 1-6% of petrolated silica powder, 15-30% of 120# frit, 30-45% of albite, 10-25% of iron phosphate, 1-3% of zinc oxide, 5-10% of a color developing agent and 5-15% of cerium oxide. The processing technology comprises the following steps: 1, material preparation and selection; 2, processing of the raw materials; 3, processing in a roller kiln; and 4, excess materials utilization. According to the Geshi metal glaze disclosed by the invention, raw materials which are relatively environment-friendly and non-toxic to a human body are adopted, so that a reliable guarantee is provided for green and environment-friendly production and non-toxic and safe use of a product; the Geshi metal glaze has excellent decoration and embellishment effects, and various physicochemical indexes also reach or are superior to related standards, so that the application of the Geshi metal glaze can greatly improve the grade of domestic ceramic products.

Description

technical field [0001] The invention relates to the technical field of Grignard metal glaze, in particular to a Grignard metal glaze with copper-red metal texture and a processing technology thereof. Background technique [0002] Due to the raw material formula and firing process, the application of ordinary metal glazes is not satisfactory in many aspects: or the glaze color is less, monotonous, and lacks the natural change of glaze color and luster, which makes it dull. The decorative embellishment effect of the product is greatly reduced; or the lead and cadmium exceed the standard, which limits the wide application of glazes in the field of daily-use ceramics; in view of the above-mentioned problems of ordinary metal glazes, in order to enhance the decorative embellishment effect of metal glazes, improve the physical and chemical properties of metal glazes. Therefore, it is very necessary to invent a kind of Grignard metallic glaze with copper-red metal texture and its p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/14C04B41/86
CPCC03C8/14C04B41/5022C04B41/86
Inventor 王亮
Owner 醴陵市格瑞瓷陶瓷科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap