A kind of metal sludge conversion treatment process

A technology for conversion treatment and sludge, applied in the fields of sludge treatment, water/sludge/sewage treatment, special treatment targets, etc. The effect of solving sludge accumulation, improving market competitiveness and solving environmental pollution

Active Publication Date: 2022-04-15
浙江合力海科新材料股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main pollutant Cr(OH) in electroplating sludge 3 , when exposed to the air, under alkaline conditions, can be absorbed by the O in the air 2 Oxidation, making Cr 3+ Reversible conversion to Cr 6+ If the electroplating sludge is piled up and landfilled without any treatment, it will cause the pollution to spread and bring more serious consequences to the environment if it is exposed to wind and rain.
[0007] The composition and properties of electroplating sludge are very complex, and its effective treatment has always been the focus and difficulty of research. The current practice of solidifying sludge has the risk of re-pollution to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of metal sludge conversion treatment process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A metal sludge conversion treatment process has the following processing steps:

[0028] 1. The dry sludge and the wet sludge are respectively installed in two sludge tanks, and the sludge is grabbed from the dry and wet sludge tanks 19 by the driving grab 11 to the reamer scale 12 to crush the sludge and weigh it. Then put into dry sludge storage tank 13 and wet sludge storage tank 14 respectively, dry sludge is delivered to mixer 2 after being weighed by belt scale 15, and wet sludge is weighed and crushed by reamer scale 12 and then delivered to mixer. Feeder 2, the sludge additive in the sludge additive tank 17 is weighed and crushed by the reamer scale 12 and then delivered to the mixer 2. The dry sludge accounts for 40%, the wet sludge accounts for 50% and the sludge additive accounts for 10%. %, stir evenly in the mixer 2 and then pour it into the granulator 3 for granulation. Specifically, the fluorite in the sludge additive accounts for 10%, the waste gypsum ac...

Embodiment 2

[0035] A metal sludge conversion treatment process has the following processing steps:

[0036] 1. The dry sludge and the wet sludge are respectively installed in two sludge tanks, and the sludge is grabbed from the dry and wet sludge tanks 19 by the driving grab 11 to the reamer scale 12 to crush the sludge and weigh it. Then put into dry sludge storage tank 13 and wet sludge storage tank 14 respectively, dry sludge is delivered to mixer 2 after being weighed by belt scale 15, and wet sludge is weighed and crushed by reamer scale 12 and then delivered to mixer. Feeder 2, the sludge additive in the sludge additive tank 17 is weighed and crushed by the reamer scale 12 and then delivered to the mixer 2. The dry sludge accounts for 45%, the wet sludge accounts for 40% and the sludge additive accounts for 15%. %, stir evenly in the mixer 2 and then pour it into the granulator 3 for granulation. Specifically, the fluorite in the sludge additive accounts for 12.5%, the waste gypsum ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a metal sludge conversion treatment process, which has the following processing steps: dry sludge, wet sludge and sludge additives are transported to a mixer, stirred evenly in the mixer, poured into a granulator to make granulation; the mixed sludge formed after granulation is conveyed to the sintering furnace for sintering through the conveyor; after sintering is completed, it is sent to the melting furnace by the conveyor combined with molten additives for melting; the molten material after melting is put into the water quenching tank for water Quenching treatment, water quenching treatment forms water quenching slag, puts it in the water quenching slag tank, and then is transported by the elevator to the mill for grinding to form the admixture. Advantages of the present invention: 1. Realize harmless disposal of metal sludge and utilization of resources with high added value. 2. Solve the problem of sludge accumulation, transportation and landfill, and solve the pollution of metal sludge to the environment.

Description

technical field [0001] The invention relates to the field of metal sludge treatment, in particular to a metal sludge conversion treatment process. Background technique [0002] Electroplating sludge refers to heavy metal-containing sludge waste generated after wastewater treatment in the electroplating industry, and is included in the seventeenth category of hazardous waste in the national hazardous waste list. As the "final state" of electroplating wastewater, although its amount is much less than that of wastewater, since heavy metals such as copper, nickel, cadmium, zinc, and iron in wastewater are transferred to sludge, electroplating sludge is harmful to the environment. It is more serious than electroplating wastewater. If there is no disposal of this extremely harmful electroplating sludge, it is self-evident that the damage to the ecological environment is self-evident. On the other hand, if the extremely high-grade heavy metal substances in the electroplating sludg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B18/02C04B20/02C02F11/00C04B18/04
CPCC04B18/026C04B20/026C02F11/00C02F2303/06C04B18/023C04B18/0472C04B18/12C04B18/04C04B14/022C04B14/36C04B14/041C04B14/368C04B22/0013C04B18/0481C04B18/141Y02W30/91
Inventor 丁小富
Owner 浙江合力海科新材料股份有限公司