Electrode treated by persulfate and application thereof

A persulfate and electrode technology, which is applied in battery electrodes, circuits, fuel cells, etc., can solve the problems of high production cost, poor electrocatalytic activity, and many processes, and achieve prolonging service life, simple preparation method, and high comprehensive performance Effect

Pending Publication Date: 2021-06-11
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Alkaline zinc-iron redox flow battery electrode materials in the prior art have probl

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrode treated by persulfate and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] Cut out a carbon felt with a thickness of 6 mm in an appropriate size, soak it in an aqueous solution of 0.5 mol / L potassium persulfate at 80 °C, take out the electrode after 12 hours, wash it repeatedly with water, and dry it for later use.

[0023] The prepared electrode materials are used as the positive and negative electrodes, the bipolar plate is a graphite plate, and the ion exchange membrane is a Nafion membrane produced by DuPont, with an effective area of ​​48 cm. 2 , assemble an alkaline zinc-iron flow battery with a current density of 80 mA / cm 2 . Among them, the positive electrolyte is containing ferrocyanide ion (Fe(CN) 6 4- ) alkaline solution, wherein the concentration of ferrocyanide ion is 1mol L -1 , the concentration of hydroxide ions is 3mol / L; the negative electrolyte is an alkaline solution containing zincate ions, wherein the concentration of zincate ions is 0.5mol L -1 , the concentration of hydroxide ions was 3mol / L; the...

Example Embodiment

[0030] Embodiment 2 (soaking time is non-optimal condition)

[0031] Compared with Example 1, the soaking time was changed to 0.2h, and other conditions remained unchanged. After testing, the battery coulombic efficiency was 94.7%, the voltage efficiency was 85.2%, and the energy efficiency was 80.7%. Battery life is 80 cycles.

[0032] Compared with Comparative Example 1, the coulombic efficiency, energy efficiency and cycle stability of the alkaline system zinc-iron flow battery of the electrode material soaked in the non-preferable time have been improved to a certain extent, but it is different from that of the present invention in Example 1. There is still a small gap compared with the preferred soaking time.

Example Embodiment

[0033] Embodiment 3 (solution concentration is non-optimal condition)

[0034] Compared with Example 1, the potassium persulfate concentration was changed to 0.1 mol / L, and other conditions remained unchanged. After testing, the battery coulombic efficiency was 96.4%, the voltage efficiency was 87.0%, and the energy efficiency was 83.9%. Battery life is 80 cycles.

[0035] Compared with Comparative Example 1, the coulombic efficiency, energy efficiency and cycle stability of the alkaline system zinc-iron flow battery of the electrode material treated in the non-preferred solution concentration have been improved to a certain extent, but the present invention in Example 1 has improved. There is still a small gap compared with the preferred soaking time.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an electrode treated by persulfate and application of the electrode in a zinc-iron flow battery, an electrode material is soaked in an aqueous solution of persulfate for treatment, and compared with an original untreated electrode material, the electrode material has higher electrode activity, the conductivity of the battery can be effectively improved, and the cycle performance and the efficiency of the battery are improved; meanwhile, the charge-discharge capacity and the energy density of the battery are greatly improved.

Description

technical field [0001] The invention relates to a zinc-iron liquid flow battery with a positive electrode treated with persulfate. Background technique [0002] Liquid flow energy storage battery is a new electrochemical energy storage technology. Compared with other energy storage technologies, it has high energy conversion efficiency, flexible system design, large storage capacity, free location selection, deep discharge, safety and environmental protection, and maintenance. With the advantages of low cost, it can be widely used in wind energy, solar energy and other renewable energy generation and energy storage, emergency power system, backup power station and power system peak shaving and valley filling. Due to the advantages of high safety, good stability, long life (life > 15 years), and low cost, the alkaline system zinc-iron flow battery is considered to be a kind of flow energy storage battery with high development potential. [0003] At present, the main limit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/96H01M8/18
CPCH01M4/96H01M8/188Y02E60/50
Inventor 段寅琦李先锋张华民袁治章
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap