Production method of double-color thread

A production method and color thread technology, applied in the direction of yarn, non-woven fabrics, textiles and papermaking, etc., can solve problems such as easy to be broken, loose structure of spunlace cloth, poor rubbing fastness, etc., to solve the problem of easy breakage and broken Hole problem, improve weaving efficiency, avoid the effect of weaving process

Inactive Publication Date: 2021-06-29
常熟市永得利水刺无纺布有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The conventional spunlace dyeing method is paint dyeing, which is easy to operate, but has poor rubbing fastness and is rarely used in clothing.
However, due to the loose structure and poor strength of the spunlaced cloth, when the traditional overflow method, air flow method and continuous method are used for dyeing, due to the impact of large tension and large water flow, it is easy to be broken or have holes. therefore cannot be dyed by these methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The present embodiment provides a kind of production method of acrylic viscose two-color thread, comprising:

[0023] (1) The acrylic fiber with a mass fraction of 50% and the viscose fiber with a mass fraction of 50% are carded respectively, and then flattened into a double-layer fiber web with viscose fiber web on the upper layer and acrylic fiber web on the lower layer, and enters the spunlace Machine, after spunlace compounding, drying into rolls, the thickness of the spunlace composite cloth is 0.6mm;

[0024] (2) Use a cutting machine to cut the spunlace composite cloth into strips to make a spunlace composite line, and the width of the spunlace composite line is 6mm;

[0025] (3) Use cationic yellow X-8GL with a weight of 1% to the fabric, use a cylinder dyeing machine to dye acrylic fibers, and then use reactive dark blue 2GLN with a weight of 0.5% o.w.f. to the fabric, use a cylinder dyeing machine to dye viscose, wash and dry A two-color thread with one side ...

Embodiment 2

[0028] This embodiment provides a kind of production method of polyester viscose two-color thread, comprising:

[0029] (1) The polyester fiber with a mass fraction of 60% and the viscose fiber with a mass fraction of 40% are carded respectively, and flattened into a double-layer fiber web with viscose fiber web on the upper layer and polyester fiber web on the lower layer, and enters the spunlace machine, after spunlace compounding, it is dried into rolls, and the thickness of the spunlace composite cloth is 0.7mm;

[0030] (2) Use a cutting machine to cut the spunlace composite cloth into strips to make a spunlace composite line, and the width of the spunlace composite line is 5mm;

[0031] (3) Use disperse blue S-GL with a weight of 0.5% to the fabric, use a cylinder dyeing machine to dye polyester, and then use a reactive red 3BS with a weight of 1% to the fabric, use a cylinder dyeing machine to dye viscose, wash and dry to obtain Two-color thread with blue on one side a...

Embodiment 3

[0034] The present embodiment provides a kind of production method of wool cotton two-color thread, comprising:

[0035] (1) The wool fiber with a mass fraction of 50% and the cotton fiber with a mass fraction of 50% are carded respectively, and flattened into a double-layer fiber web with the upper layer of wool fiber web and the lower layer of cotton fiber web, and enters the hydroentanglement machine. After spunlace compounding, it is dried into a roll, and the thickness of the spunlace composite cloth is 0.4mm;

[0036] (2) Use a strip cutter to cut the spunlace composite cloth into strips to make a spunlace composite line, and the width of the spunlace composite line is 7mm;

[0037] (3) Weak acid red B with 1% weight to the fabric and reactive yellow 3RS with 1% weight to the fabric are used to dye wool and cotton respectively with a cylinder dyeing machine. After washing and drying, a double color with red on one side and yellow on the other side is obtained. Wire.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

A production method of a double-color thread comprises the following steps: firstly, preparing spunlace composite cloth with different fibers on an upper layer and a lower layer, slitting, and dyeing by adopting bobbin dyeing to obtain the double-color thread with different colors on front and back sides. The front side and the back side of the double-color thread produced through the production method of the double-color thread have different colors, a sweater woven by the double-color thread has the good color collision effect, the complex weaving process during weaving of the two threads is avoided, the weaving difficulty is reduced, the weaving efficiency is improved, and meanwhile, the spunlace composite thread is dyed through a bobbin dyeing method, so that the problem that the spunlace cloth is easy to break and hole in a dyeing process is solved.

Description

technical field [0001] The invention belongs to the field of textile engineering, and in particular relates to a production method of a two-color thread. Background technique [0002] Sweaters made of two-color threads are popular because of their unique color contrast effect. The sweater is usually knitted with two threads at the same time, the weaving process is relatively complicated, and the weaving is difficult and the efficiency is low. However, the traditional blended yarn is difficult to achieve a color contrast effect because the two fibers are evenly mixed in the yarn. [0003] Spunlace non-woven fabric is to spray high-pressure fine water onto one or more layers of fiber webs to entangle the fibers with each other, so that the fiber webs can be reinforced and have a certain strength. The obtained fabric is spunlace non-woven fabric. Spunlaced fabric has the characteristics of high strength, soft hand feeling and good drapability. [0004] Spunlace composite fabr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D02G3/22D04H1/4374
CPCD02G3/04D02G3/22D04H1/4374D10B2201/00D10B2211/00D10B2321/10D10B2331/04
Inventor 靳小军程学伟
Owner 常熟市永得利水刺无纺布有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com