Preparation method of water-soluble magnetic sphere
A water-soluble, magnetic sphere technology, applied in the field of macro-scale preparation of magnetic nano-microspheres, can solve problems such as poor dispersibility, and achieve the effects of good magnetic susceptibility, easy scale-up production, and simple and easy-to-obtain raw materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0049] The present invention provides a method of preparing a water soluble magnetic ball comprising the steps of:
[0050] Preparation of citric acid modified oil-soluble tetrasoxide three iron nanoparticles, supplied hydroxyethyl starch or / and glucan solution, adding the hydroxyethyl starch or / and glucan solution to the decoration of citric acid The oil-soluble tetracted three iron nanoparticle solution is reacted to collect water soluble magnetic balls;
[0051] Among them, the steps of preparing the oil-soluble tetrasoxide three-iron nanoparticle solution modified by citric acid include:
[0052] The oil-soluble nanopartrioma solution wrapped in oleic acid was prepared, and a citric acid solution was provided, and the citric acid solution droplets were added to the oil-soluble tetraned iron nanoparticle solution of the oleic acid with stirring. The resulting product was mixed with methyl tert-butyl ether to collect precipitation.
[0053] It will be appreciated that in ord...
Example Embodiment
[0077] Example 1:
[0078] A method of preparing small particle soluble magnetic balls, is achieved by the following steps:
[0079] (1) take 10.8g of ferric chloride hexahydrate was dissolved in 36.5g of sodium oleate 80mL of anhydrous ethanol, 60 mL of deionized water and a mixed solvent consisting of 140mL of n-hexane, magnetic stirring, temperature was raised to 70 ℃, reflux condenser The reaction 4h, a separatory funnel and the upper organic layer was taken, washed with 30mL three times with deionized water, hexane and water removed by rotary evaporation to give a viscous reddish brown iron - oleate complex;
[0080] (2) from step (1) prepared in iron - 36g of oleic acid and 64.4g complex and oleyl alcohol ether miscible 200g, magnetic stirring, temperature 100 deg.] C under vacuum deaerator 1h and heated to 200 ℃ thermostat 0.5h, to give a black liquid, 25g 250g the reaction was precipitated with acetone, 7000rpm centrifugal 25min, dried 110 ℃, tri-iron tetroxide to give ult...
Example Embodiment
[0084] Example 2:
[0085] A method of preparing small particle soluble magnetic balls, is achieved by the following steps:
[0086] (1) take 10.8g of ferric chloride hexahydrate was dissolved in 36.5g of sodium oleate 80mL of anhydrous ethanol, 60 mL of deionized water and a mixed solvent consisting of 140mL of n-hexane, magnetic stirring, temperature was raised to 70 ℃, reflux condenser The reaction 4h, a separatory funnel and the upper organic layer was taken, washed with 30mL three times with deionized water, hexane and water removed by rotary evaporation to give a viscous reddish brown iron oleate complex;
[0087] (2) from step (1) prepared in iron - 64.4g and 36g of oleic acid and oleyl alcohol ether miscible 200g, magnetic stirring, temperature 100 deg.] C under vacuum deaerator 1h and heated to 200 ℃ temperature 0.5h, to give a dark liquid, 25g 250g the reaction was precipitated with acetone, 7000rpm centrifugal 25min, dried 110 ℃, tri-iron tetroxide to give ultra-small p...
PUM
Property | Measurement | Unit |
---|---|---|
Concentration | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap