Method for rapidly and effectively removing HW61-1 paint layer

A paint layer and fast technology, applied in the direction of cleaning methods using liquids, cleaning methods and utensils, chemical instruments and methods, etc., can solve problems such as surface damage of parts, long acetone treatment cycle, hidden safety hazards, etc., to improve production efficiency , Efficient, fast and safe removal method effect

Pending Publication Date: 2021-09-03
AECC AVIATION POWER CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the disadvantages of the above-mentioned prior art, such as mechanical removal of the paint layer causing damage to the surface of the parts, acetone treatment with a long processing cycle, inability to completely remove it, and potential safety hazards, and to provide a method for quickly and effectively removing the paint layer of HW61-1 Methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for quickly and effectively removing the paint layer of HW61-1, comprising the following steps:

[0028] (1) Immerse the parts in a 40°C degreasing solution (3% by mass APC-1 water-based cleaning agent solution) for 30 minutes;

[0029] (2) Immerse the parts in hot water at 60°C for 1 min;

[0030] (3) Dry the parts with clean and oil-free compressed air;

[0031] (4) Immerse the part in a CQ-S aqueous solution (35% by mass percent CQ-S aqueous solution) at 100°C to remove the paint layer for 60 minutes;

[0032] (5) Immerse the parts in a newly prepared degreasing solution (3% by mass of APC-1 water-based cleaning agent solution) at 40°C for 30 minutes;

[0033] (6) Immerse the parts in hot water at 60°C for 1 min;

[0034] (7) Dry the parts with clean and oil-free compressed air;

[0035] (8) Dry the parts at 190°C for 4 hours;

[0036] (9) Check whether the paint layer on the surface of the parts is removed.

Embodiment 2

[0038] A method for quickly and effectively removing the paint layer of HW61-1, comprising the following steps:

[0039] (1) Immerse the parts in a degreasing solution (4% by mass of APC-1 water-based cleaning agent solution) at 60°C for 15 minutes;

[0040] (2) Immerse the parts in hot water at 80°C for 0.5 minutes;

[0041] (3) Dry the parts with clean and oil-free compressed air;

[0042] (4) Immerse the part in a CQ-S aqueous solution (40% by mass percent CQ-S aqueous solution) at 120°C to remove the paint layer for 50 minutes;

[0043] (5) Immerse the parts in a freshly prepared degreasing solution (4% by mass APC-1 water-based cleaning agent solution) at 60°C for 15 minutes;

[0044] (6) Immerse the parts in hot water at 80°C for 0.5 minutes;

[0045] (7) Dry the parts with clean and oil-free compressed air;

[0046] (8) Bake the parts at 210°C for 3H;

[0047] (9) Check whether the paint layer on the surface of the parts is removed.

Embodiment 3

[0049] A method for quickly and effectively removing the paint layer of HW61-1, comprising the following steps:

[0050] (1) Immerse the parts in a 50°C degreasing solution (5% APC-1 water-based cleaning agent solution by mass percent) for 20 minutes;

[0051] (2) Immerse the parts in hot water at 70°C for 0.8 minutes;

[0052] (3) Dry the parts with clean and oil-free compressed air;

[0053] (4) Immerse the parts in CQ-S aqueous solution (45% by mass percent CQ-S aqueous solution) at 110°C to remove the paint layer for 55 minutes;

[0054] (5) Immerse the parts in a freshly prepared degreasing solution (5% by mass APC-1 water-based cleaning agent solution) at 50°C for 25 minutes;

[0055] (6) Immerse the parts in hot water at 70°C for 0.5 minutes;

[0056] (7) Dry the parts with clean and oil-free compressed air;

[0057] (8) Bake the parts at 200°C for 5H;

[0058] (9) Visual inspection to check whether the paint layer on the surface of the parts is removed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for rapidly and effectively removing an HW61-1 paint layer. The method comprises the following steps of firstly, removing oil stains on the surface of a part by adopting an oil removal solution, cleaning by hot water to remove traces of the oil removal solution on the surface of the part, removing paint by using a paint removal solution, and then removing oil, cleaning by the hot water, blow-drying and drying. By using the method provided by the invention, the solution or medium in the previous process cannot pollute the solution in the subsequent process, in order to enable the part to be in a relatively clean state, the oil removal solution needs to dissolve the oil stains on the surface, cleaning is thorough, it can be guaranteed that the paint layer on the surface of the part and the solution have a certain reaction, by means of the method, the HW61-1 paint layer can be completely decomposed and removed, high efficiency and safety are achieved, the engine manufacturing and repairing period can be shortened, and the production efficiency is greatly improved.

Description

technical field [0001] The invention belongs to the technical field of HW61-1 paint layer removal, and relates to a method for quickly and effectively removing the HW61-1 paint layer. Background technique [0002] The surface of ultra-high-strength steel shaft parts of aero-engines is coated with HW61-1 paint layer, which is a kind of epoxy organosilicon aluminum powder paint. When the paint layer has defects that do not meet the design requirements during the production process or after use, Paint needs to be removed and reapplied. Removal by mechanical methods will cause damage to the surface of the parts. Currently, the commonly used technical method is to use acetone to remove. However, when the method of soaking in acetone is used to remove, there are problems such as long cycle time, potential safety hazards and inability to completely remove. Contents of the invention [0003] The purpose of the present invention is to overcome the disadvantages of the above-menti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B08B3/08B08B3/10B08B13/00
CPCB08B3/08B08B3/10B08B13/00B08B2203/007
Inventor 陈晓彦胡婷婷白亚波蒲胜利王振北马嘉悦唐兴
Owner AECC AVIATION POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com