Water-damage-resistant asphalt reclaimed material and preparation method thereof

A technology for asphalt regeneration and water damage resistance, applied in climate sustainability, sustainable waste treatment, solid waste management, etc., can solve problems such as damage, insufficient pavement durability, insufficient water stability, etc. Improve pavement durability and realize the effect of automatic cleaning process

Pending Publication Date: 2021-10-19
江阴永盛交通工程有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing asphalt recycled materials have insufficient water stability, resulting in insufficient durability of the pavement, especially in low temperature environments where water damage is more serious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-damage-resistant asphalt reclaimed material and preparation method thereof
  • Water-damage-resistant asphalt reclaimed material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The invention provides a kind of asphalt recycled material which can resist water damage, which comprises: 4.10% modified asphalt, 34.50% waste asphalt mixture, 5.84% regenerated agent, and 55.56% aggregate according to weight percentage; The aggregates include: 2.56% mordenite molecular sieve, 2.68% nano-silicon carbide, 2.21% hydrogel, and 92.55% basalt composite material;

[0026] The basalt composite material includes basalt fine material and basalt coarse material, and the basalt fine material and basalt coarse material are compounded according to a weight ratio of 1:1, and the regeneration agent includes a surfactant and a light component regeneration agent;

[0027] The present invention also provides a method for preparing asphalt recycled material that can resist water damage, and the specific preparation steps are as follows:

[0028] Step 1: weighing modified asphalt, waste asphalt mixture, regenerant and aggregate according to the above weight percentage;

...

Embodiment 2

[0036]Different from Example 1, it includes: 5.00% modified asphalt, 35.70% waste asphalt mixture, 6.26% regeneration agent, 53.04% aggregate by weight percentage; the aggregate includes by weight percentage : 2.84% mordenite molecular sieve, 2.92% nano silicon carbide, 2.51% hydrogel, 91.73% basalt composite material.

Embodiment 3

[0038] All different from Examples 1-2, it includes: 4.55% modified asphalt, 35.10% waste asphalt mixture, 6.05% regeneration agent, 54.30% aggregate according to weight percentage; The percentage calculation includes: 2.70% mordenite molecular sieve, 2.80% nano-silicon carbide, 2.36% hydrogel, 92.14% basalt composite.

[0039] Respectively take the asphalt reclaimed material prepared in the above-mentioned embodiments 1-3 and the asphalt reclaimed material of the control group one, the asphalt reclaimed material of the control group two, the asphalt regenerated material of the control group three and the asphalt regenerated material of the control group four, the control group The asphalt recycled material of the first group is the ordinary asphalt recycled material on the market, the asphalt recycled material of the control group 2 has no mordenite molecular sieve compared with the embodiment, and the asphalt recycled material of the control group 3 has no nano-silicon carbid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water-damage-resistant asphalt reclaimed material and a preparation method thereof, and particularly relates to the technical field of asphalt materials. The water-damage-resistant asphalt reclaimed material comprises modified asphalt, a waste asphalt mixture, a regenerant and aggregate. The aggregate comprises a mordenite molecular sieve, nano silicon carbide, hydrogel and a basalt composite material. 35.10% of the waste asphalt mixture and 6.05% of the regenerant are doped in the formula, so that the water damage resistance of the asphalt reclaimed material can be effectively improved, and meanwhile, the low temperature resistance of the asphalt reclaimed material is ensured; and the mordenite molecular sieve, the nano silicon carbide and the hydrogel can realize automatic cleaning treatment of the asphalt pavement, so that the durability of the pavement is effectively improved, the integrated contact effect of nano components in the material and other components can be effectively enhanced, the self performance of the asphalt reclaimed material is improved, the water damage resistance of the asphalt reclaimed material is improved, and the pavement durability is ensured.

Description

technical field [0001] The invention relates to the technical field of asphalt materials, and more specifically, the invention relates to a water damage-resistant asphalt reclaimed material and a preparation method thereof. Background technique [0002] With the rapid development of asphalt pavement technology, the proportion of asphalt pavement will increase. Therefore, it is very necessary to repair or rebuild these pavements in time to improve their performance. Due to the frequent overloading of highways in our country, the actual life of asphalt pavements in our country is often lower than the design life, so a large number of asphalt pavements will be produced every year to be repaired and rebuilt. In the past, the treatment of waste asphalt mixture was often simply discarded or landfilled. However, old asphalt mixture is a resource that can be recycled. If it is simply discarded or landfilled, it will not only cause waste of resources, but also It will also cause lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/26C04B18/16C04B14/04C04B14/32C04B111/27
CPCC04B26/26C04B18/16C04B14/047C04B14/324C04B2111/27C04B2111/0075C04B2111/00008C04B14/14Y02W30/91
Inventor 葛明锋汤晓慧邓万军李泽锋李挺
Owner 江阴永盛交通工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap