Metal wire preparation method

A metal wire and shaving technology, which is applied in metal processing equipment, metal processing machinery parts, manufacturing tools, etc., can solve the problems of low tensile strength of indium, reduce the purity of indium wire, and easily broken wire, etc., so as to improve the efficiency of wire making , easy to promote and use, good effect

Active Publication Date: 2021-10-22
先导薄膜材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]Currently, most of the high-purity indium wires on the market are prepared by extrusion and wire drawing, but because indium is relatively soft, its strength is around HV4. During the extrusion process, the outer skin is prone to curling, causing some impurities to enter the core of the wire, thereby reducing the purity of the indium wire
At the same time, the elongation of indium is relatively poor, and it is easy to break the wire, so the general length of the wire is limited to less than 40 meters.
[0003]On the other hand, the higher the purity of the indium, the lower the tensile strength. For example, the tensile strength of indium with a penetration of more than 6N will be below 0.5Pa, which cannot be used in traditional Preparation of indium wire by drawing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal wire preparation method
  • Metal wire preparation method
  • Metal wire preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] The specific implementation manners of the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. The following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention.

[0028] like figure 1 As shown, a method for preparing a metal wire according to a preferred embodiment of the present invention is characterized in that it includes the following steps:

[0029] The molten indium is evenly cast on the stainless steel pipe 1 to form an indium rod 2 . Since the strength and hardness of indium are relatively low, it cannot be made into a rod independently, and the support of the stainless steel tube 1 can facilitate the next step of the indium rod 2 to rotate along its axis. Preferably, the amount of indium cast at one time is more than 100 kilograms;

[0030] The stainless steel tube 1 containing the indium rod 2 is installed on a rotatin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensionaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of metal wires, and discloses a metal wire preparation method. The method comprises the following steps of uniformly casting molten indium on a stainless steel tube to form an indium rod; mounting the stainless steel tube containing the indium rod on a rotating device; and a grater is attached to the indium rod, the rotating device is started to drive the indium rod to rotate, and indium wire forming is achieved. By adopting the device for preparing the indium wire, the wire breakage is avoided, the length of the indium wire can be increased, the wire preparation efficiency is improved, the cross section of the grater is the same as the grater hole of the grater, the phenomenon that the outer skin is turned up is avoided, so that the condition that impurities are rolled into the core part of the wire is avoided, and the purity of the indium wire is ensured; and the method is simple to operate, good in using effect and easy to popularize and use.

Description

technical field [0001] The invention relates to the technical field of metal wires, in particular to a method for preparing ultrafine high-purity low-melting-point metal wires, and more particularly to a method for preparing indium wires. Background technique [0002] At present, most of the high-purity indium wires on the market are prepared by extrusion and wire drawing, but because indium is relatively soft and its strength is around HV4, the outer skin is prone to curling during the extrusion process, causing some impurities to enter the wire. core, thereby reducing the purity of the indium wire. At the same time, the elongation of indium is relatively poor, and it is easy to break the wire, so the general length of the wire is limited to less than 40 meters. [0003] On the other hand, the higher the purity of indium, the lower the tensile strength. For example, the tensile strength of indium with a penetration of more than 6N will be below 0.5Pa, and the traditional d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21C37/04B23D5/02B23D13/00B23Q11/10
CPCB21C37/04B23D5/02B23D13/00B23Q11/10
Inventor 黄宇彬童培云朱刘
Owner 先导薄膜材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products