A kind of 304 stainless steel with pattern and rolling method thereof

A technology of 304 stainless steel and stainless steel plate, which is applied in the direction of metal rolling, metal rolling, rolling force/roll gap control, etc., can solve the problem of harmful stress corrosion resistance of austenitic stainless steel, long duration of high temperature heating section, rolling Solve problems such as high cost and use status, and achieve the effects of faster replacement, reduced safety accidents, and reduced energy consumption

Active Publication Date: 2022-02-15
山东盛阳金属科技股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1) During the rough rolling process, the surface of the work rolls will stick to scale and other debris to make the surface uneven, and the surface of the work rolls must be cleaned and polished regularly; the existing work rolls need to be disassembled and replaced as a whole, and special large-scale cleaning is required The equipment is specially cleaned, and the back-and-forth hoisting and transportation of the work rolls not only increases the workload, but also poses serious safety hazards;
[0004] 2) The heating time of the existing stainless steel hot rolling is too long during the rolling process, the high temperature heating section lasts for a long time, and the energy consumption is relatively large, so that the rolling cost is maintained at a relatively high use state;
[0005] 3) In order to improve the corrosion resistance of stainless steel, a small amount of Mo element will be added, but too high Mo element will be harmful to the stress corrosion resistance of austenitic stainless steel; so it is necessary to determine an appropriate range of Mo element addition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 304 stainless steel with pattern and rolling method thereof
  • A kind of 304 stainless steel with pattern and rolling method thereof
  • A kind of 304 stainless steel with pattern and rolling method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A rolling method of 304 stainless steel with patterns, the chemical composition weight percentage of heat-resistant steel is: C=0.055%, Mn=0.50%, Ni=7.5%, N=0.05%, Si=0.32%, Cr=17.5% , Cu=0.03%, P=0.03%, S=0.0045%, Mo=0.8%, the balance is Fe element and unavoidable impurities;

[0034] Its process steps are as follows:

[0035] 1) Prepare the raw material slabs of the above components and heat them in a heating furnace. The thickness of the slabs is controlled at 200-220mm. The heating steps are successively divided into a preheating section, a heating section, a heating section, and a soaking section; Control at 675°C, and set the heating time to 78 minutes; after the preheating section is completed, enter the heating section for heating, the temperature is controlled at 1120°C, and the heating time is set to 50 minutes; after the heating section is completed, enter the heating section 2 for heating, and the temperature is controlled at 1268 ℃, the heating time is set...

Embodiment 2

[0049] Compared with Example 1, the difference is:

[0050] Step 1) In the preheating section, the temperature is controlled at 658°C, and the heating time is set to 73.5min; after the preheating section is completed, enter the heating section for heating, the temperature is controlled at 1125°C, and the heating time is set to 45min; after the heating section is completed, enter the heating section Heating in the second stage, the temperature is controlled at 1278°C, and the heating time is set to 50 minutes; after the second stage of heating is completed, it enters the soaking section, the temperature is controlled at 1250°C, and the heating time is set to 55 minutes; the total heating of the second stage and the soaking section The time is high temperature section time = 105min, total furnace time = 223.5min.

[0051] In step 3), the finish rolling start temperature is set to 1085°C; the finish rolling end temperature is controlled at 995°C; the steel ingot is rolled for 8 p...

Embodiment 3

[0053] Compared with the embodiment, the difference is:

[0054] Step 1) In the preheating section, the temperature is controlled at 650-680°C, and the heating time is set to 70 minutes; after the preheating section is completed, enter the heating section for heating, and the temperature is controlled at 1080-1130°C, and the heating time is set at 45 minutes; after the heating section is completed Enter the second stage of heating for heating, the temperature is controlled at 1255-1285°C, and the heating time is set to 60min; after the second stage of heating is completed, enter the soaking section, the temperature is controlled at 1250-1270°C, and the heating time is set to 55min; The total heating time in the soaking section is high temperature section time = 115min, and the total furnace time = 230min.

[0055] In step 3), the finish rolling start temperature is set to 1072°C; the finish rolling end temperature is controlled at 956°C; the steel ingot is rolled for 8 passes ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rolling method of 304 stainless steel with patterns. The weight percentage of chemical composition is: C≤0.064%, Mn≤0.70%, Ni≤8.0%, N≤0.055%, Si≤0.40%, Cr≤18 %, Cu ≤ 0.045%, P ≤ 0.036%, S ≤ 0.006%, Mo ≤ 1.0%, and the balance is Fe element and unavoidable impurities; the process steps are as follows: 1) Prepare the raw material slab of the above components to the heating furnace Heating; 2) rough rolling: the heated steel ingot is sent to the rough rolling mill through the transfer roller; 3) finishing rolling: the steel plate is transported into the finishing rolling mechanism; 4) coiling: after finishing rolling, it is sent to the coiling mechanism for coiling; 5) Uncoiling welding: welding and fixing the adjacent two groups of steel plates by welding mechanism; 6) Annealing: annealing the stainless steel plate by annealing mechanism; 7) Phosphorus breaking shot blasting; 8) Pickling: 9) Drying. The preparation process provided by the invention is simple and reliable, low in cost, energy-saving and environment-friendly, and the prepared 304 stainless steel has high strength and plasticity.

Description

technical field [0001] The invention belongs to the technical field of stainless steel rolling, in particular to a rolling method of 304 stainless steel with patterns. Background technique [0002] At present, the rough rolling mechanism used in the rolling process of the patterned 304 stainless steel plate is equipped with upper and lower corresponding work rolls and support rolls, and the steel billets are rough rolled by the work rolls; [0003] 1) During the rough rolling process, the surface of the work rolls will stick to scale and other debris to make the surface uneven, and the surface of the work rolls must be cleaned and polished regularly; the existing work rolls need to be disassembled and replaced as a whole, and special large-scale cleaning is required The equipment is specially cleaned, and the back-and-forth hoisting and transportation of the work rolls not only increases the workload, but also poses serious safety hazards; [0004] 2) The heating time of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/42C22C38/44C21D8/02C21D1/26B21B1/22B21B3/02B21B27/03B21B37/58B21B37/74
CPCC22C38/04C22C38/001C22C38/02C22C38/42C22C38/44C21D8/0205C21D8/0226C21D8/0247C21D1/26B21B1/227B21B3/02B21B27/032B21B37/58B21B37/74B21B2001/225
Inventor 肖亮明
Owner 山东盛阳金属科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products