Fishing tool plummet and preparation method thereof

A sinker and fishing gear technology, applied in fishing, animal husbandry, application, etc., can solve the problems of short service life, easy oxidation and rust, environmental pollution, etc., and achieve the effect of long service life, smooth surface and not easy to fall off

Pending Publication Date: 2021-11-30
河南双立仕智能家居有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the fishing net pendants commonly used in fishing nets and fishing gear are mostly made of pure metals such as iron, lead, copper, and stainless steel, which have the advantage of high specific gravity, but the preparation process is polluted and consumes a lot of energy.
In this era that emphasizes reducing carbon emissions and energy consumption, this pure metal fishing net sinker is a product with high energy consumption and high consumables, which pollutes the environment during production and use, is easy to oxidize and rust, and has a short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0047] The embodiment of the present invention also relates to a method for preparing the fishing tackle weight, which includes uniformly mixing the components with a high-speed mixer, and then injection molding with an injection molding machine to obtain the fishing tackle weight. Because the polymer organic material has the characteristics of anti-oxidation and non-rust, and has water resistance. When it is mixed with the metal material, the metal material is completely wrapped in the polymer organic material, which isolates the metal material from the air and realizes the anti-oxidation effect.

[0048] In one embodiment of the present invention, the injection molding temperature is 150-300° C., and the injection molding time is 10s-10 minutes.

experiment example 1

[0050]A fishing tackle sinker containing organic polymer materials and metal materials, comprising the following components in parts by weight: 20-50 parts of organic polymer materials, 50-80 parts of metal materials, and 0-80 parts of inorganic compound materials. The distribution ratio of each group of embodiment and comparative example is shown in Table 1.

[0051] The preparation method of the fishing tackle weight includes uniformly mixing the components with a high-speed mixer, and then injection molding at 200-250° C. for 1-2 minutes by an injection molding machine to obtain the fishing tackle weight. Specifically, in injection molding, the heating temperature of the barrel is divided into several areas to control. The small injection molding machine is divided into three areas (also called three sections). (section), three districts (section). The temperature of the first and second stages is 260°C, and the temperature of the third stage is 250°C.

[0052] Table 1

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Heat distortion temperatureaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a fishing gear plummet containing an organic polymer material and a metal material. The raw materials comprise the organic polymer material and the metal material, and an inorganic compound material can be selectively added. According to the invention, the original technical field of preparing the fishing tool plummet from the single metal material is changed, the raw material is changed from the single metal material to a mixture of the organic polymer material and the metal material, and the preparation method is changed from metal casting to injection molding. The obtained product has the advantages of smooth surface, no fishing net hooking, difficulty in falling, no oxidation rust, low cost and long service life, and the weight can meet the requirements of fishing nets of different specifications. The invention also provides a preparation method of the fishing gear plummet, which comprises the following steps: uniformly mixing the components through a high-speed mixer, and then carrying out injection molding through an injection molding machine to obtain the fishing gear plummet.

Description

technical field [0001] The invention relates to the technical field of fishing nets and fishing gear, in particular to a fishing gear weight containing organic polymer materials and metal materials, and a method for preparing the fishing gear weight. Background technique [0002] At present, the fishing net pendants commonly used in fishing nets and fishing gear are mostly made of pure metals such as iron, lead, copper, stainless steel, etc., which have the advantage of high specific gravity, but the preparation process is polluted and consumes a lot of energy. In this era that emphasizes the reduction of carbon emissions and energy consumption, this pure metal fishing net sinker is a product with high energy consumption and high consumables, which pollutes the environment during production and use, is easy to oxidize and rust, and has a short service life. Therefore, it is necessary to adopt new synthetic materials to prepare fishing net pendants, so that it has the advanta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L23/06C08L55/02C08K3/08C08K3/30A01K95/00
CPCC08K3/08C08K3/30A01K95/005C08K2003/0856C08K2003/3045C08K2003/085C08L23/12C08L23/06C08L55/02
Inventor 田卫刚
Owner 河南双立仕智能家居有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com