A technology of filling materials and manufacturing techniques, applied to the specialized techniques of artistic painting, techniques for producing decorative surface effects, decorative arts, etc., which can solve the problems of poisonous, harmful to human health, and polluting the environment

Pending Publication Date: 2021-12-21
广东恩来善新科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In modern traditional paintings, industrial pigments are used as filling pigment compositions, and acrylic pigments and chemical gouache pigments are often used for painting. Most chemical pigments are poisonous and harmful to health. Although most chemical pigments meet environmental protection requirements according to national standards, they still have It pollutes the environment to a certain extent. At present, there is no cloisonné filigree painting that is both environmentally friendly and can improve air quality.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Filling material composition and preparation process for wire inlay painting
  • Filling material composition and preparation process for wire inlay painting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A filling material composition for filigree painting, which comprises: zeolite powder, forming agent and pigment. The above-mentioned zeolite powder is selected from natural zeolite rocks and pulverized, and the purity of the above-mentioned zeolite powder is 97%. The forming agent includes white latex and water, and the ratio of the above white latex to water is 9:1. The above-mentioned pigments are natural mineral pigments.

[0040] The production process of the filigree painting is as follows: draw a line draft on the drawing board, and then use the wire to filigree on the drawing board according to the line draft, place the drawing board horizontally after the filigreeing is completed, and fill the pattern formed by the metal wire with zeolite powder Top; after the filling is completed, mix the white latex and water into the molding agent at a ratio of 9:1, and spray the molding agent on the filled zeolite powder after the blending is completed, and the filling lay...

Embodiment 2

[0042] A filling material composition for filigree painting, which comprises: zeolite powder, forming agent and pigment. The above-mentioned zeolite powder is selected from natural zeolite rocks and pulverized, and the purity of the above-mentioned zeolite powder is 97.5%. The forming agent includes white latex and water, and the ratio of the above white latex to water is 9.5:1. The above-mentioned pigments are natural mineral pigments.

[0043] The production process of the filigree painting is as follows: draw a line draft on the drawing board, and then use the wire to filigree on the drawing board according to the line draft, place the drawing board horizontally after the filigreeing is completed, and fill the pattern formed by the metal wire with zeolite powder Top; after the filling is completed, mix the white latex and water with the molding agent at a ratio of 9.5:1, and spray the molding agent on the filled zeolite powder after the blending is completed, and the filli...

Embodiment 3

[0045] A filling material composition for filigree painting, which comprises: zeolite powder, forming agent and pigment. The above-mentioned zeolite powder is selected from natural zeolite rocks and pulverized, and the purity of the above-mentioned zeolite powder is 98%. The forming agent includes white latex and water, and the ratio of the above white latex to water is 10:1. The above-mentioned pigments are natural mineral pigments.

[0046] The production process of the filigree painting is as follows: draw a line draft on the drawing board, and then use the wire to filigree on the drawing board according to the line draft, place the drawing board horizontally after the filigreeing is completed, and fill the pattern formed by the metal wire with zeolite powder Top; after the filling is completed, mix the white latex and water with the molding agent at a ratio of 10:1, and spray the molding agent on the filled zeolite powder after the mixing is completed, and the filled laye...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a filling material composition and a preparation process for wire inlay painting and relates to the technical field of the wire inlay painting. The filling material composition for the wire inlay painting comprises zeolite powder, a forming agent and a pigment agent, the filling material composition is environmentally friendly and healthy, and the filling material composition for the wire inlay painting can purify air and improve the air quality. The preparation process for the wire inlay painting comprises the steps that a line draft is drawn on a drawing board, then wire inlay is conducted on the drawing board by using metal wires according to the line draft, the drawing board is horizontally placed after the wire inlay is completed, a pattern defined by the metal wires is filled with the zeolite powder, after filling is completed, white latex and water are blended into the forming agent in proportion, the forming agent is sprayed on the filled zeolite powder after blending is completed, a filling layer is obtained after sand solidification and forming of the zeolite powder are completed, and the formed filling layer is colored with natural mineral pigment according to the needed color. The wire inlay painting tool manufactured through the preparation process is more environmentally friendly, and the manufactured wire inlay painting is good in quality and more exquisite.

Description

technical field [0001] The invention relates to the technical field of filigree painting, in particular to a filling material composition and a manufacturing process for filigree painting. Background technique [0002] Filigree is one of the 108 processes in traditional cloisonné production. One of the traditional crafts of ancient metalworking. The gold, silver or other metal filaments are pinched into patterns according to the twists and turns of the ink-like patterns, and then glued and welded on the utensils, which is called filigree. Cloisonne painting is the traditional way of making cloisonne. It can be directly hung on the wall without firing. It is called cloisonné painting, also called filigree painting. It is a new type of painting in traditional cloisonné works. Filigree painting is the key point of the present invention, which evolved from cloisonné filigree painting, and takes painting as the main appreciation work. Existing filigree painting is the traditio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B44C5/04B44C1/18B44C1/00B44D2/00C09D5/06F24F3/14
CPCB44C5/0415B44C1/18B44C1/00B44D2/005C09D5/06F24F3/1411
Inventor 林美玲
Owner 广东恩来善新科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap