Antibacterial cotton fabric with good air permeability

A breathable, cotton fabric technology, applied in the field of fabric processing, can solve the problems of insufficient elasticity, general comfort, easy shrinkage and deformation, etc., and achieve the effects of prolonging service life, good moisture absorption, breathability, and good resilience

Pending Publication Date: 2021-12-31
有内(厦门)科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The common inner fabrics on the market do not use good materials and techniques. They have insufficient elasticity, are easy to shrink and deform, and the fabrics are hard. The comfort and wearing experience are not enough. Although most merchants are promoting their products with antibacterial functions, But the antibacterial function is only partially added, there is no way to make consumers feel very at ease, and the comfort is average when wearing it.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial cotton fabric with good air permeability
  • Antibacterial cotton fabric with good air permeability
  • Antibacterial cotton fabric with good air permeability

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A kind of antibacterial cotton fabric with good air permeability, its manufacture comprises the following steps:

[0047] (1) Preparation of raw materials:

[0048] Select 80 high-quality Xinjiang long-staple cotton and 20D U.S. DuPont high-elastic Lycra spandex as raw materials, and weave 80 Xinjiang long-staple cotton and 20D U.S. DuPont high-elastic Lycra spandex into plain weave fabric according to the weight ratio of 90:10 for later use;

[0049] (2) Magnetic field-proton irradiation coupling treatment:

[0050] The fabric in step (1) is placed in a stable magnetic field, and proton irradiation treatment is carried out at the same time. The strength of the magnetic field is 700G, and the irradiation dose of proton irradiation is 200c. After 1 hour of treatment, take it out for use;

[0051] (3) singeing and desizing treatment:

[0052] Singeing is performed on the treated fabric in step (2), the flame temperature is 800°C, and then desizing is performed for subse...

Embodiment 2

[0060] A kind of antibacterial cotton fabric with good air permeability, its manufacture comprises the following steps:

[0061] (1) Preparation of raw materials:

[0062] Select 80 high-quality Xinjiang long-staple cotton and 20D U.S. DuPont high-elastic Lycra spandex as raw materials, and weave 80 Xinjiang long-staple cotton and 20D U.S. DuPont high-elastic Lycra spandex into plain weave fabric according to the weight ratio of 91:9 for later use;

[0063] (2) Magnetic field-proton irradiation coupling treatment:

[0064] The fabric in step (1) is placed in a constant magnetic field, and proton irradiation treatment is carried out at the same time. The strength of the magnetic field is 750G, and the irradiation dose of proton irradiation is 450c. After 1.5h of treatment, take it out for use;

[0065] (3) singeing and desizing treatment:

[0066] Singeing is performed on the treated fabric in step (2), the flame temperature is 850°C, and then desizing is performed for subseq...

Embodiment 3

[0074] A kind of antibacterial cotton fabric with good air permeability, its manufacture comprises the following steps:

[0075] (1) Preparation of raw materials:

[0076] Select 80 high-quality Xinjiang long-staple cotton and 20D U.S. DuPont high-elastic Lycra spandex as raw materials, and weave 80 Xinjiang long-staple cotton and 20D U.S. DuPont high-elastic Lycra spandex into plain weave fabric according to the weight ratio of 92:8 for later use;

[0077] (2) Magnetic field-proton irradiation coupling treatment:

[0078] The fabric in step (1) is placed in a constant magnetic field, and proton irradiation treatment is carried out at the same time. The strength of the magnetic field is 800G, and the irradiation dose of proton irradiation is 700c. After 2 hours of treatment, take it out for use;

[0079] (3) singeing and desizing treatment:

[0080] Singeing is performed on the treated fabric in step (2), the flame temperature is 900°C, and then desizing is performed for sub...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibacterial cotton fabric with good air permeability, and belongs to the technical field of fabric processing. A manufacturing method comprises the following steps that 1, raw material preparation; (2) magnetic field-proton irradiation coupling treatment; (3) singeing and desizing treatment; (4) boiling off; (5) cold plasma treatment; and (6) finished product preparation. The cotton fabric prepared by the method is good in moisture absorption and air permeability and high in skin-friendly degree; the fabric is worn without feeling and has good resilience; after multiple times of washing, the antibacterial and deodorizing effects are up to 99%, and the fabric can be worn without worries for sensitive skin; and the quality is good, the phenomena of damage and laddering are avoided, and the service life is prolonged to a great extent.

Description

technical field [0001] The invention belongs to the technical field of fabric processing, and in particular relates to an antibacterial cotton fabric with good air permeability. Background technique [0002] The common inner fabrics on the market do not use good materials and techniques. They have insufficient elasticity, are easy to shrink and deform, and the fabrics are hard. The comfort and wearing experience are not enough. Although most merchants are promoting their products with antibacterial functions, However, the antibacterial function is only partially added, and there is no way to make consumers feel very at ease, and the comfort is average when wearing it. For this reason, we have developed a kind of antibacterial cotton fabric with good air permeability based on the shortcomings of the market and the comfort experience of consumers. Contents of the invention [0003] The object of the present invention is to provide an antibacterial cotton fabric with good ai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More