Emulsified oil for cutting glass balls

A technology of emulsified oil and glass balls, applied in the field of emulsified oil, can solve the problems of insufficiency of tools, slow emulsification, sticking to the knife, etc., and achieve the effect of improving extreme pressure lubricity, increasing pH value, and good high temperature lubrication

Pending Publication Date: 2022-03-01
山东三晶润滑科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Now cutting glass ball oil is generally poor in function, rusty, slow in emulsification, sticky to the knife, low in cutting efficiency, and not durable in use. Some manufacturers use butter as the lubricant, which is easy to rot and stink if the lubrication is not achieved.
The cost of the current ester lubrication is too expensive, the water-based one is not good, it cannot form a film, the oil-based one is too expensive, I don’t know the standard for its ease of use, and the oil is still not easy to use when it is diluted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Glass ball cutting emulsified oil, including raw materials in the following proportions by weight: machine oil: 100 parts, the viscosity of machine oil is 46 viscosity, 702:1 part, 702 adopts petroleum sodium sulfate specially used for emulsified oil, triethanolamine boron Ester: 0.5 parts, Swire oil: 1 part, Swire oil with high content, and Swire oil is acidic, MBM: 0.1 part, MBM as preservative, vulcanized cottonseed oil: 2 parts, vulcanized cottonseed oil as extreme pressure agent , NP-10: 1, NP-10 is a non-ionic emulsifier, S-80: 2.1 parts, S-80 is a lipophilic emulsifier;

[0020] Preparation of emulsified oil includes the following steps:

[0021] S1: Choose mechanical oil and Taikoo oil with high pH value;

[0022] S2: For the selection of each raw material, select the one with high viscosity, and the viscosity at 40°C must be greater than 77;

[0023] S3: The wear scar when lubricating 40kgf is not more than 0.312, that is, the Pb value is more than 50kgf;

...

Embodiment 2

[0027] Glass ball cutting emulsified oil, including the following raw materials in parts by weight: machine oil: 154 parts, the viscosity of machine oil is 46 viscosity, 702: 10 parts, 702 adopts petroleum sodium sulfate special for emulsified oil, triethanolamine boron Ester: 5 parts, Taikoo oil: 10 parts, Taikoo oil is high in content, and Taikoo oil is acidic, MBM: 2 parts, MBM is used as a preservative, vulcanized cottonseed oil is 8 parts, vulcanized cottonseed oil is used as an extreme pressure agent, NP-10: 5, NP-10 is a non-ionic emulsifier, S-80: 6.1 parts, S-80 is a lipophilic emulsifier;

[0028] Preparation of emulsified oil includes the following steps:

[0029] S1: Choose mechanical oil and Taikoo oil with high pH value;

[0030] S2: For the selection of each raw material, select the one with high viscosity, and the viscosity at 40°C must be greater than 77;

[0031] S3: The wear scar when lubricating 40kgf is not more than 0.312, that is, the Pb value is more ...

Embodiment 3

[0035] Glass ball cutting emulsified oil, including raw materials in the following proportions by weight: Machine oil: 110 parts, the viscosity of the machine oil is 46 viscosity, 702: 2 parts, 702 adopts petroleum sodium sulfate specially used for emulsified oil, triethanolamine boron Ester: 0.8 parts, Swire oil: 2 parts, Swire oil with high content, and Swire oil is acidic, MBM: 0.2 parts, MBM as preservative, vulcanized cottonseed oil: 3 parts, vulcanized cottonseed oil as extreme pressure agent , NP-10: 2, NP-10 is a non-ionic emulsifier, S-80: 3.1 parts, S-80 is a lipophilic emulsifier;

[0036] Preparation of emulsified oil includes the following steps:

[0037] S1: Choose mechanical oil and Taikoo oil with high pH value;

[0038] S2: For the selection of each raw material, select the one with high viscosity, and the viscosity at 40°C must be greater than 77;

[0039] S3: The wear scar when lubricating 40kgf is not more than 0.312, that is, the Pb value is more than 50...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses emulsified oil for cutting glass balls. The emulsified oil is prepared from the following raw materials in parts by weight: 100 to 154 parts of machine oil, 1 to 10 parts of 702, 0.5 to 5 parts of triethanolamine borate and 1 to 10 parts of Turkey red oil. According to the glass ball cutting emulsified oil, the pH value is increased through triethanolamine borate, the extreme pressure lubricity is improved, high-temperature lubrication is better, the problems of high base number and easy layering are solved, MBM serves as a preservative, the glass ball cutting emulsified oil is a green and environment-friendly product, the body health of an operator is considered, the good preservative effect is also considered, and the glass ball cutting emulsified oil does not deteriorate after being used by two amounts; vulcanized cottonseed oil is used as an extreme pressure agent, high-temperature lubrication in the glass water cutting process at the temperature of more than 1 thousand DEG C is just catered, the vulcanized cottonseed oil has the characteristics that the higher the temperature is, the better the lubrication is, the cutting task is well completed, a precious cutter is well protected, the cutting speed is high, the efficiency is very high, and the cleaning property and effectiveness of the formula are improved by adding NP-10; the cleaning agent of NP-10 is very good and has very strong emulsifying ability.

Description

technical field [0001] The invention relates to the technical field of emulsified oil, in particular to glass ball cutting emulsified oil. Background technique [0002] Now cutting glass ball oil is generally poor in function, rusty, slow in emulsification, sticky to the knife, low in cutting efficiency, and not durable in use. Some manufacturers use butter as the lubricant, which is easy to rot and stink if the lubrication is not achieved. . The cost of the current ester lubrication is too expensive, the water-based ones are not good, and cannot form a film, the oil-based ones are too expensive, and the standard of ease of use is unknown, and the oil is still not easy to use when it is diluted. For this purpose, we present glass spheres cutting emulsified oil. Contents of the invention [0003] (1) Solved technical problems [0004] Aiming at the deficiencies of the prior art, the present invention provides glass ball cutting emulsified oil, which solves the problems r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N30/04C10N30/06C10N30/08C10N30/12C10N40/22
CPCC10M169/044C10M2219/042C10M2227/061C10M2219/024C10N2030/12C10N2030/06C10N2030/08C10N2030/04C10N2040/22C10N2010/02
Inventor 李祥柱李祥田解锡龙
Owner 山东三晶润滑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.