Water-based release agent for prefabricated part and preparation method of water-based release agent
A prefabricated component and release agent technology, applied in the field of release agent, prefabricated component water-based release agent and its preparation, can solve the problem of odor affecting workers' health and construction, the length of time required for demoulding construction, and the easy deterioration of products, etc. problem, to achieve good demoulding effect, low cost, and reduced porosity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0016] A water-based release agent for prefabricated components and a preparation method thereof, comprising the following raw materials in parts by mass: 15 parts of oil, 2 parts of membrane reactants, 30 parts of emulsion, 0.3 parts of interface release agent, 4 parts of emulsifier, and 0.2 parts of defoamer part, 100 parts of water.
[0017] S1 Put 15 parts of oil and 2 parts of membrane reactants into the reactor for stirring, and heat to 40°C, then stop, and stir until it becomes a transparent and uniform liquid;
[0018] S2 Add 30 parts of emulsion, 0.3 parts of interfacial release agent, 4 parts of emulsifier, and 0.2 parts of defoamer to the transparent and uniform liquid. Stir with dispersant at 500 r / min. After stirring for 30 minutes, the material is removed. mold oil mixture;
[0019] S3 Add 100 parts of water in proportion to the stirred release oil mixture for mixing to finally obtain a release agent for concrete components.
Embodiment 2
[0021] A water-based release agent for prefabricated components and a preparation method thereof, comprising the following raw materials in parts by mass: 15 parts of oil, 2 parts of membrane reactants, 30 parts of emulsion, 0.3 parts of interface release agent, 4 parts of emulsifier, and 0.2 parts of defoamer part, 100 parts of water.
[0022] S1 Put 15 parts of oil and 2 parts of membrane reactants into the reactor for stirring, and heat to 40°C, then stop, and stir until it becomes a transparent and uniform liquid;
[0023] S2 Add 30 parts of emulsion, 0.3 part of interfacial release agent, 4 parts of emulsifier, and 0.2 part of defoamer to the transparent and uniform liquid. Stir with dispersant at 700 r / min. After stirring for 30 minutes, the material is discharged. mold oil mixture;
[0024] S3 Add 100 parts of water in proportion to the stirred release oil mixture for mixing to finally obtain a release agent for concrete components.
Embodiment 3
[0026] A water-based release agent for prefabricated components and a preparation method thereof, comprising the following raw materials in parts by mass: 40 parts of oil, 8 parts of film reactants, 60 parts of emulsion, 12 parts of interface isolation agent, 18 parts of emulsifier, and 0.8 parts of defoamer parts, 1000 parts of water.
[0027] S1 Put 40 parts of oil and 8 parts of film reactants into the reactor for stirring, and heat to 50°C, then stop, and stir until it becomes a transparent and uniform liquid;
[0028] S2 Add 60 parts of emulsion, 12 parts of interfacial release agent, 18 parts of emulsifier, and 0.8 part of defoamer to the transparent and uniform liquid. Stir with dispersant at a speed of 1000 r / min. After stirring for 40 minutes, the material is removed mold oil mixture;
[0029] S3 Add 1000 parts of water in proportion to the stirred release oil mixture for mixing to finally obtain a release agent for concrete components.