Alloy and component

A technology for alloys and components, which is applied in the field of alloys and components using the alloys, and can solve problems such as mold damage

Pending Publication Date: 2022-04-05
株式会社博迈立铖
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Mold damage occurs when casting is repeated using the same mold

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alloy and component
  • Alloy and component
  • Alloy and component

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0103] The alloy of the present invention will be described based on specific examples.

[0104] Samples containing 10 types of alloys listed in Table 2 were prepared. Alloys No. 34 to No. 40 of Examples were produced by arc melting under the following conditions. In addition, as a comparative example, a sample (No. 31) including JIS SKD61, a sample (No. 32) obtained by nitriding the surface of JIS SKD61, and a NbTaTi alloy (No. 33) were prepared. About JIS SKD61, it manufactured with the composition and manufacturing method based on JIS G4404, About NbTaTi alloy (No. 33), it manufactured similarly to an Example.

[0105] In the alloy of the embodiment of Table 2, the content of the constituent elements of No.34 to No.36 is the same amount, the four constituent elements (Nb, Mo, Ta, W) of No.40 are the same amount, and the other elements are 2 times the equivalent amount. In addition, alloys No. 37 to No. 39 have compositions obtained by simulating combinations of elements ...

Embodiment 2

[0175] Hereinafter, application examples of the alloy of the present invention will be specifically described. In addition, the components of the present invention are not limited to the use of these examples.

[0176]

[0177] Various starting materials shown in Table 9 were prepared. The raw material powders are all pure metal powders obtained by chemical reduction. These raw materials were weighed so that they became samples of No. 41 to No. 44 shown in Table 10, and mixed for 30 minutes with a V mixer, whereby a plurality of powders with different specific gravity in each raw material powder were mixed. The ingredients are mixed evenly. The composition of Table 10 is at %.

[0178] [Table 9]

[0179] Raw material powder Nb Mo Ta W Ti Zr f Melting point (°C) 2477 2623 3017 3422 1668 1855 2233 Powder particle size (um) ≤150 4～5 ≤45 0.6-1 ≤45 ≤177 ≤150

[0180] [Table 10]

[0181] No. sample name Nb Mo ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Vickers hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to view more

Abstract

Provided is an alloy having resistance to an aluminum alloy or the like in a molten state. The alloy contains Nb and Mo as a first element group and at least one of Ta, W, Ti, Hf and Zr as a second element group, and when the total of the elements of the first element group and the second element group is 100 at.%, the content range of the contained elements is 5 at.% to 35 at.%, and the lattice mismatch of the alloy with respect to at least one of Al, Cu and Zn is 13% or more. And has tolerance such that the migration barrier energy of dislocation is 310 kJ/mol or more.

Description

technical field [0001] The present invention relates to an alloy having resistance to an alloy in a molten state or a plastic state, especially an aluminum alloy, and a member using the alloy. Background technique [0002] Dies used in low-pressure casting, gravity casting, and die-casting of aluminum alloys are, for example, Japanese Industrial Standards (JIS) SKD61. When casting is repeated using the same mold, the mold will be damaged. The main cause of damage is melting loss. Melting loss occurs due to the lowering of the melting point due to partial alloying of the mold in contact with the molten aluminum alloy. [0003] When the melting loss intensifies, repair the melted part by welding and surfacing. As the repairing material, an alloy having a high melting point and excellent creep resistance at high temperature and corrosion resistance is preferable. An example of such an alloy is disclosed in Patent Document 1. [0004] In the case of requiring high strength ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C30/00C22C30/02C22C30/06
CPCC22C30/00
Inventor 岩崎富生白鸟浩史木村达哉小関秀峰
Owner 株式会社博迈立铖
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap