Vacuum tempered glass substrate processing technology

A technology of glass substrate and processing technology, which is applied in glass tempering, glass manufacturing equipment, manufacturing tools, etc. It can solve the problems of high stress value of glass substrate and glass breakage, so as to ensure fire prevention and UV protection performance, The effect of increasing the stress value and ensuring the fire performance

Pending Publication Date: 2022-05-10
HEILONGJIANG JIANZHONG SPECIAL GLASS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the existing vacuum glass, the operation mode of vacuuming to form a protective layer will cause the glass to break. In addition, in the existing preparation process, in order to ensure a good vacuum degree of the vacuum glass, the glass substrate is vacuum-operated. Therefore, the stress value of the glass substrate is extremely high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Take the glass substrate and carry out cutting and edge grinding successively;

[0027] (2) Rinse the glass substrate after the above-mentioned edging treatment with ethanol, then carry out acid treatment with 3% nitric acid solution, and then continue to wash with ethanol for 3 times;

[0028] (3) Dry the above-mentioned cleaned glass substrate in an oven at 70°C for 50 minutes, and then put it into a cesium potassium solution to strengthen it for 120 minutes, wherein the cesium potassium solution uses water as a solvent, including the following mass: Fractional components: potassium nitrate 65%, cesium nitrate 2%, rubidium nitrate 0.1%, stannous sulfide 0.7%, sodium tetraborate 7%;

[0029] (4) carrying out Low-E coating film to the glass substrate after above-mentioned gained strengthening;

[0030] (5) Carry out physical toughening treatment on the above-mentioned coated glass substrate at 695° C., the time of the physical toughening treatment is to heat 80 sec...

Embodiment 2

[0033] (1) Take the glass substrate and carry out cutting and edge grinding successively;

[0034] (2) Rinse the glass substrate after the above-mentioned edging treatment with ethanol, then carry out acid treatment with 4% phosphoric acid solution, and then continue to wash with ethanol for 4 times;

[0035] (3) Dry the above-mentioned cleaned glass substrate in an oven at 70°C for 50 minutes, and then put it into a cesium potassium solution for strengthening for 150 minutes, wherein the cesium potassium solution uses water as a solvent, including the following mass: Fractional components: potassium nitrate 70%, cesium nitrate 3%, rubidium nitrate 0.2%, stannous sulfide 0.8%, sodium tetraborate 8%;

[0036] (4) carrying out Low-E coating film to the glass substrate after above-mentioned gained strengthening;

[0037] (5) Carrying out physical toughening treatment to the above-mentioned glass substrate after coating under the condition of 705°C, the time of said physical toug...

Embodiment 3

[0040] (1) Take the glass substrate and carry out cutting and edge grinding successively;

[0041] (2) Rinse the glass substrate after the above-mentioned edging treatment with ethanol, and then carry out acid treatment with 5% nitric acid solution, and then continue to wash with ethanol for 5 times;

[0042] (3) Dry the above-mentioned cleaned glass substrate in an oven at 70°C for 50 minutes, and then put it into a cesium potassium solution for strengthening for 180 minutes, wherein the cesium potassium solution uses water as a solvent, including the following mass: Fractional components: potassium nitrate 75%, cesium nitrate 4%, rubidium nitrate 0.3%, stannous sulfide 0.9%, sodium tetraborate 9%;

[0043] (4) carrying out Low-E coating film to the glass substrate after above-mentioned gained strengthening;

[0044] (5) Carry out physical toughening treatment on the above-mentioned glass substrate after coating at 715°C, the time of said physical toughening treatment is to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Stress valueaaaaaaaaaa
Stress valueaaaaaaaaaa
Stress valueaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of tempered glass manufacturing, and provides a vacuum tempered glass substrate processing technology. The invention provides a vacuum tempered glass substrate processing technology. The vacuum tempered glass substrate processing technology specifically comprises the steps of cutting, edge grinding, alcohol washing, acid treatment, strengthening treatment, film coating treatment, physical tempering treatment, air cooling forming and the like. The prepared vacuum tempered glass substrate is subjected to special chemical cesium-potassium dipping treatment, the ion exchange effect of sodium ions and cesium and potassium ions is enhanced, the fireproof performance of glass is guaranteed, meanwhile, the stress value of the glass substrate is remarkably increased, and the situation that a vacuum glass cavity bursts under the external atmospheric pressure is improved.

Description

technical field [0001] The invention relates to the technical field of vacuum tempered glass manufacturing, in particular to a vacuum tempered glass substrate processing technology. Background technique [0002] At present, the vacuum glass on the market is generally separated by two pieces of flat glass with a support, and the edge of the two pieces of flat glass is sealed and vacuumized to form a vacuum layer between the two glass products. Heat preservation, sound insulation and noise reduction, etc. However, in the existing vacuum glass, the operation mode of vacuuming to form a protective layer will cause the glass to break. In addition, in the existing preparation process, in order to ensure a good vacuum degree of the vacuum glass, the glass substrate is vacuum-operated. Therefore, the stress value of the glass substrate is extremely high. Therefore, in order to overcome the cracking or even self-explosion in the preparation of the vacuum layer of the glass substrat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C21/00C03B27/00C03C17/00
CPCC03C21/002C03B27/00C03C17/00
Inventor 李珩民张伟
Owner HEILONGJIANG JIANZHONG SPECIAL GLASS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com