Cow mat rubber and preparation method thereof

A rubber and bullpen technology, applied in the field of rubber mats, can solve the problems of affecting service life, lack of antibacterial function, and easy aging, etc., and achieve the effects of prolonging service life, good flex cracking level, and wide application prospects

Pending Publication Date: 2022-05-13
青岛升恒明橡塑有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The patent application number is CN201811518754.0 for "a rubber and its preparation method". Better, less prone to cracking, discoloration or mildew, less hardening or softening, good heat resistance and oil resistance; in addition, the natural antioxidant ingredients contained in polyvinylpyrrolidone can prolong the storage period of the rubber produced", the above Although the patent can have certain mechanical properties, it is prone to aging during use, which affects its service life. At the same time, it also lacks a certain antibacterial function, which affects its application in the livestock breeding industry and cannot satisfy users. usage requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cow mat rubber and preparation method thereof
  • Cow mat rubber and preparation method thereof
  • Cow mat rubber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The invention provides a cowpen mat rubber, which comprises the following raw materials in parts by weight: 20 parts of tetrapropylene fluoro rubber, 1 part of stearic acid, 2 parts of calcium carbonate, 4 parts of nanofibers, 2 parts of clove oil, and 5 parts of carbon black N219 4 parts of modified ZnO, 3 parts of paraffin, 6 parts of sulfur, 1 part of accelerator, and 2 parts of anti-aging agent.

[0032] Further, the nanofiber is a meta-aramid fiber, and its particle size is 20um.

[0033] Further, modified ZnO, its preparation method is:

[0034] Put nano-sized ZnO in a three-necked bottle, then add 2 times the modifier and mix well; put it in an ultrasonic disperser for ultrasonic dispersion for 1 hour, and then transfer it to an oven for drying; crush the dried nano-sized ZnO to obtain Modified ZnO;

[0035] Wherein, the modifying agent is sodium laurate solution, and its concentration is 0.04mol / L.

[0036] Further, the accelerator is zinc di-n-butyldithiocar...

Embodiment 2

[0047] The invention provides a cowpen mat rubber, comprising the following raw materials in parts by weight: 30 parts of tetrapropylene fluoro rubber, 3 parts of stearic acid, 4 parts of calcium carbonate, 12 parts of nanofibers, 8 parts of clove oil, and 12 parts of carbon black N219 8 parts, 8 parts of modified ZnO, 6 parts of paraffin, 10 parts of sulfur, 4 parts of accelerator, 4 parts of anti-aging agent.

[0048] Further, the nanofiber is a meta-aramid fiber, and its particle size is 30um.

[0049] Further, modified ZnO, its preparation method is:

[0050] Put nano-sized ZnO in a three-necked bottle, then add 2 times the modifier and mix well; put it in an ultrasonic disperser for ultrasonic dispersion for 2 hours, then transfer to an oven for drying; crush the dried nano-sized ZnO to obtain Modified ZnO;

[0051] Wherein, the modifying agent is sodium laurate solution, and its concentration is 0.04mol / L.

[0052] Further, the accelerator is zinc di-n-butyldithiocarb...

Embodiment 3

[0063] The invention provides a cowpen mat rubber, which comprises the following raw materials in parts by weight: 25 parts of tetrapropylene fluorine rubber, 2 parts of stearic acid, 3 parts of calcium carbonate, 8 parts of nanofibers, 6 parts of clove oil, and 8 parts of carbon black N219 6 parts, 6 parts modified ZnO, 4 parts paraffin, 8 parts sulfur, 2 parts accelerator, 3 parts antioxidant.

[0064] Further, the nanofiber is a meta-aramid fiber, and its particle size is 30um.

[0065] Further, modified ZnO, its preparation method is:

[0066] Put the nano-sized ZnO in a three-necked bottle, then add 2 times the modifier and mix well; then place it in an ultrasonic disperser for ultrasonic dispersion for 1.5 hours, and then transfer it to an oven for drying; crush the dried nano-sized ZnO, Obtain modified ZnO;

[0067] Wherein, the modifying agent is sodium laurate solution, and its concentration is 0.04mol / L.

[0068] Further, the accelerator is zinc di-n-butyldithioca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of rubber pads, in particular to cattle mat rubber and a preparation method thereof. Comprising the following raw materials in parts by weight: 20-30 parts of tetrafluoroethylene-propylene rubber, 1-3 parts of stearic acid, 2-4 parts of calcium carbonate, 4-12 parts of nanofibers, 2-8 parts of clove oil, 5-12 parts of carbon black N219, 4-8 parts of modified ZnO, 3-6 parts of paraffin, 6-10 parts of sulfur, 1-4 parts of an accelerant and 2-4 parts of an anti-aging agent. The prepared cattle mat rubber not only has beneficial hardness performance, tensile strength performance and stretch rate performance, but also has a good deflection cracking grade, so that the service life of the cattle mat rubber is prolonged, and particularly, the cattle mat rubber can also effectively play an antibacterial role when being applied to livestock breeding.

Description

technical field [0001] The invention relates to the technical field of rubber mats, in particular to a cowpen mat rubber and a preparation method thereof. Background technique [0002] Rubber refers to a highly elastic polymer material with reversible deformation. It is elastic at room temperature, can produce large deformation under a small external force, and can return to its original shape after the external force is removed. It not only provides daily and medical light industrial rubber products that are indispensable for people’s daily life, but also provides various rubber production equipment or rubber parts for mining, transportation, construction, machinery, electronics and other heavy industries and emerging industries. [0003] The patent application number is CN201811518754.0 for "a rubber and its preparation method". Better, less prone to cracking, discoloration or mildew, less hardening or softening, good heat resistance and oil resistance; in addition, the n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/18C08L91/06C08L91/00C08L77/10C08K5/09C08K3/26C08K3/04C08K3/22C08K9/04C08K3/06C08K5/39C08K5/3437C08K13/06
CPCC08L27/18C08K2003/265C08K2003/2296C08K2201/011C08L2205/16C08L91/06C08L91/00C08L77/10C08K5/09C08K3/26C08K3/04C08K3/22C08K9/04C08K3/06C08K5/39C08K5/3437C08K13/06
Inventor 丁振全高波
Owner 青岛升恒明橡塑有限公司