390MPa-grade cold-rolled dual-phase steel and welding method of acid rolling process thereof
A welding method, 1.390mpa technology, applied in the direction of welding equipment, welding medium, welding equipment, etc., can solve the problems of thin welding thickness, unable to provide guidance and basis for welding methods, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0045] 390MPa grade cold-rolled dual-phase steel (chemical composition: 0.065%C, 0.01%Si, 0.65%Mn, 0.011%P, 0.005%S, 0.032%Als) with a coil temperature of 58°C and a size of 3.65*1450mm, Its carbon equivalent is 0.176) after cutting off 2.4mm from the tail of the steel coil, it is compared with 390LA (chemical composition: 0.050%C, 0.080%Si, 0.28%Mn, 0.010%) with a temperature of 55℃ and a size of 3.50*1420mm. P, 0.008% S, 0.033% Als, 0.020% Nb, its carbon equivalent is 0.092), the head of the steel coil is sheared 3.3mm, and the welding current is 12.5kW and the speed of 5.7m / min is used for welding. The welding seam after welding by the above welding process is smooth and smooth, no nodules, no welding scars, no welding penetration, no cracking along the welding seam, and good crescent bending effect in the cupping test. A belt breakage accident caused by a weld occurs.
Embodiment 2
[0047] 390MPa grade cold-rolled dual-phase steel (chemical composition: 0.072%C, 0.02%Si, 0.70%Mn, 0.010%P, 0.004%S, 0.037%Als) with a coil temperature of 53°C and a size of 3.25*1360mm Its carbon equivalent is 0.183) after cutting off 3.5mm from the tail of the steel coil, it is combined with St37-2G (chemical composition: 0.09%C, 0.01%Si, 0.35%Mn, 0.015%P, 0.008%S, 0.045%Als, its carbon equivalent is 0.15) the head of the steel coil is cut 3.4mm, and the welding current is 12.3kW and the speed of 5.8m / min is used for welding. The welding seam after welding by the above welding process is smooth and smooth, no nodules, no welding scars, no welding penetration, no cracking along the welding seam, and good crescent bending effect in the cupping test. A belt breakage accident caused by a weld occurs.
PUM
Property | Measurement | Unit |
---|---|---|
size | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com