Catalytic combustion heating and drying process for domestic ceramic product

A catalytic combustion, heating and drying technology, applied in the direction of burners, combustion types, heating devices, etc., can solve the problems of product storage space, occupation of plant resources, low work efficiency, etc., to shorten the drying time, improve efficiency, Guaranteed quality effect

Pending Publication Date: 2022-08-02
广州市蓝炬能源科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of the deficiencies of the prior art, the purpose of the present invention is to provide a catalytic combustion heating drying process for daily-use ceramic products. Storage space is required for placement, occupying plant resources, and the next drying operation needs to wait for the previous batch of products to be dried and taken out, which is a technical problem of low work efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] When using the catalytic combustion heating and drying process of this technical solution, step 1: the air is fed into the filter and the activated carbon adsorption box under the action of the gravitational force of the fan, and the gas is filtered by the filter to remove impurities in the gas; Remove foreign matter molecules in the gas; the filter is provided with 5 layers, from outside to inside, they are primary filter, medium efficiency filter, sub-efficient filter, high-efficiency filter and ultra-high-efficiency filter. The pore size of the filter membrane is 5um, 1.0um, 0.5um, 0.3um and 0.1um, and the initial resistance of the filter is ≤50Pa, ≤80Pa, ≤1200Pa, ≤220Pa and ≤280Pa, the air purification in step 1 can reach the level: particle size ≥ 5.0μm; Step 2: Start the electric heater in the catalytic burner to heat up the inside of the catalytic burner and carry out catalytic combustion; the catalytic combustion reaction can only occur when the catalytic combust...

Embodiment 2

[0037] When using the catalytic combustion heating and drying process of this technical solution, step 1: the air is fed into the filter and the activated carbon adsorption box under the action of the gravitational force of the fan, and the gas is filtered by the filter to remove impurities in the gas; Remove foreign matter molecules in the gas; the filter is provided with 5 layers, from outside to inside, they are primary filter, medium efficiency filter, sub-efficient filter, high-efficiency filter and ultra-high-efficiency filter. The pore size of the filter membrane is 5um, 1.0um, 0.5um, 0.3um and 0.1um, and the initial resistance of the filter is ≤50Pa, ≤80Pa, ≤1200Pa, ≤220Pa and ≤280Pa, the air purification in step 1 can reach the level: particle size ≥ 5.0 μm; Step 2: Start the electric heater in the catalytic burner to heat up the inside of the catalytic burner and carry out catalytic combustion; the catalytic combustion reaction occurs at 75 ° C, there are three activa...

Embodiment 3

[0039] When using the catalytic combustion heating and drying process of this technical solution, step 1: the air is fed into the filter and the activated carbon adsorption box under the action of the gravitational force of the fan, and the gas is filtered by the filter to remove impurities in the gas; Remove foreign matter molecules in the gas; the filter is provided with 5 layers, from outside to inside, they are primary filter, medium efficiency filter, sub-efficient filter, high-efficiency filter and ultra-high-efficiency filter. The pore size of the filter membrane is 5um, 1.0um, 0.5um, 0.3um and 0.1um, and the initial resistance of the filter is ≤50Pa, ≤80Pa, ≤1200Pa, ≤220Pa and ≤280Pa, the air purification in step 1 can reach the level: particle size ≥ 5.0μm; Step 2: Start the electric heater in the catalytic burner to heat up the inside of the catalytic burner to carry out catalytic combustion; the catalytic combustion occurs at 100 ° C for catalytic combustion reaction...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a catalytic combustion heating and drying process for domestic ceramic products, and aims to solve the problems that in the prior art, products are prone to cracking, and dried products need to be placed in a storage space; and the next drying operation can be carried out after the previous batch of products are dried and taken out. The catalytic combustion heating and drying process comprises the following steps: 1, feeding air into a filter and an activated carbon adsorption box under the action of attraction of a fan, and filtering the air by the filter to remove impurities in the air; foreign matter molecules in the gas are removed by the activated carbon adsorption box; secondly, an electric heater in the catalytic combustor is started, the temperature of the interior of the catalytic combustor is increased, and catalytic combustion and the like are carried out; according to the catalytic combustion heating and drying process, the catalytic combustion technology is utilized, ceramic products cannot be cracked, continuous production can be achieved, and the dried products directly enter the next procedure.

Description

technical field [0001] The invention belongs to the technical field of daily-use ceramic shaping, in particular to a catalytic combustion, heating and drying process for daily-use ceramic products. Background technique [0002] Daily-use ceramic products mainly refer to food-use ceramics, that is, ceramic products such as plates, bowls, cups, saucers, etc., which are produced to meet people's needs for daily life. Ceramic products have the advantages of being easy to wash and keep clean. Porcelain glaze is bright and delicate, and it is easy to wash off after being stained. [0003] The current drying methods of ceramic products mainly include hot air drying and natural air drying. When the natural air drying process is adopted, the products are formed by high-pressure molds and then placed on the storage rack in the workshop to dry naturally. This method has the following defects: 1) Long process drying time: easily affected by the uncertainty of season, temperature, humid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): F26B23/02F26B21/10F23D14/18B01D53/04B01D46/62
CPCF26B23/02F26B21/10F23D14/18B01D53/04B01D46/62Y02A50/20
Inventor 张大金张仲凌
Owner 广州市蓝炬能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap