Anionic enamel and manufacturing method thereof

A negative ion and enamel technology, applied in the field of functional enamel and its preparation, can solve the problems of enamel with single performance and no functional function, and achieve the effects of simple production process, stimulating cell activity, and strengthening polarization ability

Inactive Publication Date: 2006-05-17
DONGHUA UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The performance of the current enamel is relatively simple and has no functional effect. Therefore, how to improve its performance and further expand its use is a topic of great concern to people.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The black tourmaline produced in Xinjiang is used. Firstly, the selected tourmaline is cleaned to remove the surrounding rock and impurities on the mineral, dried at 600°C, and ultrafinely pulverized with a pulverizer until the particle size reaches about 2.5um.

[0026] Take a cast iron with a thickness of 2 mm and a diameter of 60 mm, use 10% HCl and 1% NaOH solution to remove rust and decontamination, remove and dry for later use.

[0027] Spray the base glaze on the treated cast iron surface first, and then fire it after drying. Make the surface glaze (i.e. enamel base material) frit again, and its formula is as table 1:

[0028] raw material

quartz

Borax

Feldspar

Soda ash

Sodium nitrate

Antimony oxide

ice crystal

calcium fluoride

barium carbonate

Zinc oxide

composition

26.2

31.3

8.8

3.1

1.6

8.1

8.0

2.4

1.0

9.5

[0029] According to the compos...

Embodiment 2

[0033] The black tourmaline produced in Xinjiang is used. Firstly, the selected tourmaline is cleaned to remove the surrounding rock and impurities on the mineral, dried at 600°C, and ultrafinely pulverized with a pulverizer until the particle size reaches about 2.5um.

[0034] Take a cast iron with a thickness of 2 mm and a diameter of 60 mm, use 10% HCl and 1% NaOH solution to remove rust and decontamination, remove and dry for later use.

[0035] Spray the base glaze on the treated cast iron surface first, and then fire it after drying. Make the surface glaze (i.e. enamel base material) frit again, and its formula is as table 2:

[0036] raw material

quartz

Borax

Feldspar

Soda ash

Sodium nitrate

Antimony oxide

ice crystal

calcium fluoride

barium carbonate

Zinc oxide

composition

25

31

8.8

3.1

1.5

6.9

8.0

2.5

1.0

9.5

[0037] Using the same method as in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a negative ion enamel and a manufacturing method thereof. The components and percentage by weight of the negative ion enamel of the present invention include: 80-95% of enamel base material, 5-20% of tourmaline. The present invention uses enamel as the carrier of tourmaline powder, which can maximize the function of tourmaline to produce negative ions. After the enamel added with tourmaline powder is made into various products, such as bathtubs, wash basins, tea mugs, etc., different effect. The invention has the advantages of simple manufacturing process, low cost, safety and reliability, and can be produced in batches.

Description

technical field [0001] The invention relates to an enamel and a preparation method thereof, in particular to a functionalized enamel and a preparation method thereof. Background technique [0002] Enamel is a widely used material, which has important uses in chemical industry, medicine and daily life products. [0003] The performance of the current enamel is relatively simple and has no functional effect. Therefore, how to improve its performance and further expand its use is a subject of great concern. Contents of the invention [0004] The technical problem to be solved in the present invention is to disclose a kind of negative ion enamel and its manufacturing method, so as to meet the needs of people's daily life. [0005] Component and weight percent content of negative ion enamel of the present invention comprise: [0006] Enamel base material 80~95% [0007] Tourmaline 5-20% [0008] Said enamel base material can adopt conventional formula, as the technology dis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/22C03C8/04C03C8/06C23D1/00
Inventor 王瑛蒋伟忠陈丽芸叶正涛
Owner DONGHUA UNIV
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com