Epoxy resin mortar and preparation method

A technology of epoxy resin and mortar, which is applied in the field of epoxy resin mortar, can solve problems such as erosion, abrasion, and restriction, and achieve the effects of good mechanical properties and durability, high strength, and good construction performance

Inactive Publication Date: 2006-09-13
CHINA HYDROPOWER ELEVENTH ENG BUREAU ZHENGZHOU CO LTD +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, hydropower projects are developing in the direction of high dams and high water heads, which puts forward higher requirements for the anti-erosion and anti-cavitation performance of the high-speed flow surface. Abrasive materials can no longer meet these requirements well. In addition, a large number of hydropower projects that have been built after long-term operation also have abrasion and erosion to varying degrees. Commonly used repair materials such as high-strength cement mortar and polymer cement mortar are affected by their strength, Performance limitations such as durability and adhesion to base materials also do not lend themselves well to the repair and reinforcement requirements of these buildings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The raw materials of the epoxy resin mortar provided by the invention are epoxy resin, medium sand, diluent and curing agent.

[0013] The weight ratio of each raw material can be:

[0014] Epoxy resin: 12%-16%,

[0015] Medium sand: 73%-82%,

[0016] Thinner: 1.5%-2.5%,

[0017] Curing agent: 4.5%-8.5%.

[0018] The preferred weight ratio of each raw material is:

[0019] Epoxy resin: 13.5%-14.5%,

[0020] Medium sand: 76%-79%,

[0021] Thinner: 2%-2.3%,

[0022] Curing agent: 5%-7.7%.

[0023] The further optimized ratio is:

[0024] Epoxy resin: 14.18%,

[0025] Medium sand: 78.36%-76.24%,

[0026] Thinner: 2.13%,

[0027] Curing agent: 5.33%-7.45%.

[0028] For example:

[0029] Proportion one:

[0030] Epoxy resin: 16%,

[0031] Medium sand: 73%,

[0032] Thinner: 2.5%,

[0033] Curing agent: 8.5%.

[0034] Proportion two:

[0035] Epoxy resin: 12%,

[0036] Medium sand: 82%,

[0037] Thinner: 1.5%,

[0038] Curing agent: 4.5%.

[0039] Propo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

In the invention, epoxy, meidum plain emergy, diluent and curing agent are used as raw material, their weight percentage are (wt%): epoxy 12-16, medium plain emergy 73-82, diluent 1.5-2.5, curing agent 4.5-8.5. epoxy is optimum selected A-type E44 epoxy, medium plain emery can be river sand or quartz sand, diluent can be epoxy propane butyl ether, curing agent is optimum selected modified M-phthalic amine curing agent. Modifying method of said M-phthalic amine curing agent is that M-phthalic amine curing agent and monocycle oxo-compound do chemical combining reaction to generate liquid amine compound, then to be modified by acylate.

Description

technical field [0001] The present invention relates to a kind of epoxy resin mortar, also relates to the preparation method of this mortar, this kind of mortar belongs to building material, can be used in hydropower project, highway, bridge, factory, wharf and other various construction fields, especially can be used as hydropower project High-speed flow surface coating and repair and reinforcement materials. Background technique [0002] At present, hydropower projects are developing in the direction of high dams and high water heads, which puts forward higher requirements for the anti-erosion and anti-cavitation performance of the high-speed flow surface. Abrasive materials can no longer meet these requirements well. In addition, a large number of hydropower projects that have been built after long-term operation also have abrasion and erosion to varying degrees. Commonly used repair materials such as high-strength cement mortar and polymer cement mortar are affected by t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/24C04B14/06
Inventor 高富龙张涛张海泉王敬军张汉平
Owner CHINA HYDROPOWER ELEVENTH ENG BUREAU ZHENGZHOU CO LTD