Production method of high purity aluminium scandium alloy

An aluminum-scandium and alloy technology is applied in the production field of high-purity aluminum-scandium alloy, which can solve the problems of long process, difficult operation and high cost, and achieve the effects of reducing production cost, improving metal recovery rate and improving quality.

Active Publication Date: 2004-07-21
GUIZHOU BRANCH CHINA ALUMINUM IND
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The production method of aluminum-scandium alloy is now mostly used by fusion method, which is to melt high-purity metal scandium and aluminum under the protection of argon gas. This method is not easy to operate, the burning loss is serious, and the production process of pure metal scandium is complicated, and the metal yield is low. , expensive
In addition, there is a fluoride vacuum aluminothermic reduction method. The scandium fluoride used in this method is obtained by reacting scandium oxide after repeated purification with hydrofluoric acid. The process is long, the metal yield is low, and the cost is high.
Existing aluminum-scandium alloys are mostly made of industrial primary aluminum, which contains high impurities such as silicon, iron, potassium, and sodium, and it is difficult to meet the composition requirements of the aerospace industry for alloys.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The ratio of the control electrolyte is: aluminum fluoride AlF 3 25%, sodium fluoride NaF13%, barium chloride BaCl 2 57%, sodium chloride NaCl5%, add 15% scandium chloride ScCl in the electrolyte 3 . Its operating control parameters are: electrolysis temperature: 720°C, electrolytic cell working voltage: 4.5v, electrolyte thickness: 7.0cm. The chemical composition requirements of scandium chloride added to the electrolyte during electrolysis: scandium chloride ScCl 3 : >98.5%, loss on ignition <1%, sum of oxides <0.2%, sum of other impurities <0.3%. The weight percent chemical composition of the high-purity aluminum-scandium alloy produced by the method of the present invention is: scandium Sc 2.0%, the rest is aluminum Al and unavoidable impurities, wherein iron Fe<0.01%, silicon Si<0.01%, other impurities Sum < 0.02%.

Embodiment 2

[0022] The ratio of the control electrolyte is: aluminum fluoride AlF 3 22%, sodium fluoride NaF15%, barium chloride BaCl 2 55%, sodium chloride NaCl8%, add 1% scandium chloride ScCl in the electrolyte 3 . Its operating control parameters are: electrolysis temperature: 700°C, electrolytic cell working voltage: 5.0v, electrolyte thickness: 6.0cm. The chemical composition requirements of scandium chloride added to the electrolyte during electrolysis: scandium chloride ScCl 3 : >98.5%, loss on ignition <1%, sum of oxides <0.2%, sum of other impurities <0.3%. The weight percent chemical composition of the high-purity aluminum-scandium alloy produced by the method of the present invention is: scandium Sc 0.1%, the rest is aluminum Al and unavoidable impurities, wherein iron Fe<0.01%, silicon Si<0.01%, other impurities Sum < 0.02%.

Embodiment 3

[0024] The ratio of the control electrolyte is: aluminum fluoride AlF 3 27%, sodium fluoride NaF15%, barium chloride BaCl 2 50%, sodium chloride NaCl8%, add 10% scandium chloride ScCl in the electrolyte 3 . Its operating control parameters are: electrolysis temperature: 750°C, electrolytic cell working voltage: 6.0v, electrolyte thickness: 13cm. The chemical composition requirements of scandium chloride added to the electrolyte during electrolysis: scandium chloride ScCl 3 : >98.5%, loss on ignition <1%, sum of oxides <0.2%, sum of other impurities <0.3%. The weight percent chemical composition of the high-purity aluminum-scandium alloy produced by the method of the present invention is: scandium Sc 1.0%, the rest is aluminum Al and unavoidable impurities, wherein iron Fe<0.01%, silicon Si<0.01%, other impurities Sum < 0.02%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A technology for preparing high-purity Al-Sc alloy by use of three-layer molten aluminium refining electrolyzer features that the scandium chloride (or fluoride) is added to electrolyte (fluorochloride or fluoride), and then directly electrolyzed at 650-850 deg.C and under 4-7 V of working voltage. Its advantages are high quality and low cost.

Description

technical field [0001] A production method of high-purity aluminum-scandium alloy. The invention relates to a method for electrolytically producing high-purity aluminum-scandium alloy by using the existing three-layer liquid aluminum refining electrolytic cell, adding scandium chloride or scandium fluoride into the electrolyte. Background technique [0002] The production method of aluminum-scandium alloy is now mostly used by fusion method, which is to melt high-purity metal scandium and aluminum under the protection of argon gas. This method is not easy to operate, the burning loss is serious, and the production process of pure metal scandium is complicated, and the metal yield is low. , expensive. In addition, there is a fluoride vacuum aluminothermic reduction method. The scandium fluoride used in this method is obtained by reacting scandium oxide after repeated purification with hydrofluoric acid. The process is long, the metal yield is low, and the cost is high. Exis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25C3/36
Inventor 杨昇顾松青刘凤琴李强罗丽芬赵淋徐建华
Owner GUIZHOU BRANCH CHINA ALUMINUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com