A composite material and polymer technology, applied in the field of resin-based building composite materials, can solve the problems of large brittleness, cracks, knocked corners, etc.

Inactive Publication Date: 2004-11-03
东莞市东历复合材料有限公司
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The steel fiber reinforced concrete manhole cover has high bearing strength, but the material itself is brittle and the impact resistance is not ideal, especially when the joint between the manhole cover and the road surface is uneven during construction, there may be corners or cracks from time to time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0090] 10% epoxy resin glue A and 90% concrete batch B are mixed; where:

[0091] ①Epoxy resin glue A is made of 100 parts (weight) epoxy resin

[0092] 20 parts (weight) curing agent

[0093] 0.5 part (weight) antioxidant

[0094] 1 part by weight flame retardant

[0095] mixed;

[0096] ② Concrete batch B consists of 10 parts (weight) cement 525#

[0097] 400 parts (weight) of stones, with a particle size of 0.8 to 1.5 cm

[0098] 200 parts (weight) sand

[0099] 20 parts (by weight) silica powder

[0100] 15 parts (by weight) magnesium oxide

[0101] 15 parts (by weight) quartz sand

[0102] 15 parts (by weight) talc powder

[0103] 10 parts (by weight) light calcium carbonate

[0104] 15 parts (by weight) kaolin clay

Embodiment 2

[0106] 10% epoxy resin glue A and 90% concrete batch B are mixed; where:

[0107] ①Epoxy resin glue A is made of 100 parts (weight) epoxy resin

[0108] 25 parts (weight) curing agent

[0109] 1 part (by weight) antioxidant

[0110] 2 parts by weight flame retardant

[0111] 0.1 parts (weight) of inorganic pigments are mixed;

[0112] ② Concrete batch B consists of 10 parts (weight) cement 525#

[0113] 500 parts (weight) of stones, with a particle size of 0.8 to 1.5 cm

[0114] 250 parts (weight) sand

[0115] 25 parts (by weight) silica powder

[0116] 20 parts (weight) magnesium oxide

[0117] 20 parts (weight) quartz sand

[0118] 20 parts (by weight) talc powder

[0119] 15 parts (by weight) light calcium carbonate

[0120] 20 parts (by weight) kaolin clay

Embodiment 3

[0122] 20% epoxy resin glue A and 80% concrete batch B are mixed; where:

[0123] ①Epoxy resin glue A is made of 100 parts (weight) epoxy resin

[0124] 20 parts (weight) curing agent

[0125] 0.5 part (weight) antioxidant

[0126] 1 part by weight flame retardant

[0127] mixed;

[0128] ② Concrete batch B consists of 10 parts (weight) cement 525#

[0129] 400 parts (weight) of stones, with a particle size of 0.8 to 1.5 cm

[0130] 200 parts (weight) sand

[0131] 20 parts (by weight) silica powder

[0132] 15 parts (by weight) magnesium oxide

[0133] 15 parts (by weight) quartz sand

[0134] 15 parts (by weight) talc powder

[0135] 10 parts (by weight) light calcium carbonate

[0136] 15 parts (by weight) kaolin clay

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The composite polymer material for manhole cover is one kind epoxy resin cemented concrete, and consists of epoxy resin fluid an in 10-20 wt% and compounded concrete B in 80-90 wt%. Manhole cover made of the material has high toughness and high shock strength, can prevent damage during transportation, construction and use. It is also anticorrosive, has no noise produced and may be colored.

Description

technical field [0001] The invention relates to a resin-based building composite material, in particular to an epoxy resin cemented concrete. Background technique [0002] The manhole cover made of traditional materials is prone to rust under natural conditions, and it is easy to generate noise when vehicles pass by. Modern roads, especially expressways, have a large traffic flow and many heavy vehicles. Traditional manhole covers are also difficult to meet the requirements in terms of strength. The manhole covers laid on the road are often stolen, causing pedestrians and vehicles to be injured. . A few years ago, a steel fiber reinforced concrete manhole cover was developed. Its pressure bearing effect is much higher than that of the cast iron manhole cover of the same specification. It can meet the requirements of passing heavy vehicles. It does not produce noise, has no value for theft, and can prevent theft. Steel fiber reinforced concrete manhole cover has high compre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00E02D29/14
Inventor 叶炽凡
Owner 东莞市东历复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka